A kind of ceramic tile capable of generating magnetic field lines and its preparation method

Abstract

The invention discloses a ceramic tile capable of producing magnetic force lines and a preparation method thereof. The ceramic tile is prepared from the following raw materials in parts by weight: 30-40 parts of crushed gravel, 25-35 parts of iron ore tailings, 15-25 parts of brucite, 12-23 parts of obsidian, 10-15 parts of diopside, 25-35 parts of modified clay, 5-10 parts of activated carbon, 14-22 parts of flint clay, 3-7 parts of aluminum phosphate, 7-14 parts of a haematitum powder, 12-18 parts of a magnet powder, 8-12 parts of borax, 4-8 parts of a lime powder, 10-15 parts of serpeggiante, and 2-5 parts of a nano aluminum powder. The haematitum powder, the magnet powder, the serpeggiante, the iron ore tailings and other raw materials are added into the ceramic tile, so that the ceramic tile can produce the magnetic force lines beneficial to human health, and the magnetic force lines act on people body spinal cord nerves, can eliminate fatigue accumulated in human bodies, enhance the magnetic action of carbon, oxygen, nitrogen, manganese, iron and the like in human body tissues, stimulate cells in the bodies, make the cells obtain stronger regenerative capacity, can allow muscles to be stretched, and play an effective relaxation role in various pains.

Description

technical field

[0001] The invention relates to a ceramic tile capable of generating magnetic lines of force and a preparation method thereof, belonging to the field of building ceramic materials. Background technique

[0002] Ceramic bricks are plate or block ceramic products produced by clay, quartz sand and other inorganic non-metallic raw materials through batching, ball milling, powder making, molding, sintering and other processes. They are widely used in decoration and protection of walls of buildings and structures. face and ground. With the rapid development of the real estate industry, the production and consumption of ceramic tiles have been greatly developed. However, the ceramic tiles on the market are only used for decoration and have no health care function. The health care tiles in the place are used to improve people's physical fitness and purify the environment, and will have huge social and economic benefits. Contents of the invention

[0003] The obj...

Examples

Embodiment Construction

[0016] A ceramic brick capable of generating magnetic lines of force, made of the following raw materials in weight (kg): crushed gravel 35, iron ore tailings 30, brucite 20, obsidian 17, diopside 12, modified clay 30, Activated carbon 8, coke gem 18, aluminum phosphate 5, ocher powder 11, magnet powder 16, borax 10, lime powder 6, hydrostone 12, nano aluminum powder 4;

[0017] The preparation method of described modified clay is as follows: a, take attapulgite, diatomaceous earth, bentonite by mass ratio 5:3:2, mix uniformly, add appropriate amount of water to make the clay slurry that concentration is 36%, then Use sulfuric acid solution with a concentration of 25% to adjust the pH of the slurry to 3.5, heat it in a water bath to 90°C, stir for 3 hours, filter, wash with distilled water until neutral, dry, calcinate at 475°C for 2 hours, pulverize, and pass through a 300-mesh sieve; b. The weight ratio of 1:2 is to mix the above-mentioned treated clay with a concent...

technical field

[0001] The invention relates to a ceramic tile capable of generating magnetic lines of force and a preparation method thereof, belonging to the field of building ceramic materials. Background technique

[0002] Ceramic bricks are plate or block ceramic products produced by clay, quartz sand and other inorganic non-metallic raw materials through batching, ball milling, powder making, molding, sintering and other processes. They are widely used in decoration and protection of walls of buildings and structures. face and ground. With the rapid development of the real estate industry, the production and consumption of ceramic tiles have been greatly developed. However, the ceramic tiles on the market are only used for decoration and have no health care function. The health care tiles in the place are used to improve people's physical fitness and purify the environment, and will have huge social and economic benefits. Contents of the invention

[0003] The obj...

Examples

Embodiment Construction

[0016] A ceramic brick capable of generating magnetic lines of force, made of the following raw materials in weight (kg): crushed gravel 35, iron ore tailings 30, brucite 20, obsidian 17, diopside 12, modified clay 30, Activated carbon 8, coke gem 18, aluminum phosphate 5, ocher powder 11, magnet powder 16, borax 10, lime powder 6, hydrostone 12, nano aluminum powder 4;

[0017] The preparation method of described modified clay is as follows: a, take attapulgite, diatomaceous earth, bentonite by mass ratio 5:3:2, mix uniformly, add appropriate amount of water to make the clay slurry that concentration is 36%, then Use sulfuric acid solution with a concentration of 25% to adjust the pH of the slurry to 3.5, heat it in a water bath to 90°C, stir for 3 hours, filter, wash with distilled water until neutral, dry, calcinate at 475°C for 2 hours, pulverize, and pass through a 300-mesh sieve; b. The weight ratio of 1:2 is to mix the above-mentioned treated clay with a concent...