Atmospheric corrosion-resistant molten structural steel and nitrogen-containing atmospheric corrosion-resistant structural steel and production method thereof
An atmospheric corrosion-resistant and profiled steel technology, applied in the field of atmospheric corrosion-resistant profiled steel, can solve problems such as failure to meet the strength index of profiled steel, and achieve the effects of improving quality, improving center quality, and avoiding center cracks
Active Publication Date: 2018-01-16
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF3 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, as a profile steel, the square continuous casting slab produced after increasing the chromium content has relatively obvious central defects (mainly central cracks and central shrinkage cavities), and the strength index of the final profile steel cannot reach that of plate steel Therefore, profile steels with better atmospheric corrosion resistance are still under development.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0025] Specific embodiments of the present invention will be described in detail below. It should be understood that the specific embodiments described here are only used to illustrate and explain the present invention, and are not intended to limit the present invention.
[0026] Neither the endpoints nor any values of the ranges disclosed herein are limited to such precise ranges or values, and these ranges or values are understood to include values approaching these ranges or values. For numerical ranges, between the endpoints of each range, between the endpoints of each range and individual point values, and between individual point values can be combined with each other to obtain one or more new numerical ranges, these values Ranges should be considered as specifically disclosed herein.
[0027] As mentioned above, the present invention provides a kind of atmospheric corrosion-resistant molten steel, based on the total weight of molten steel, molten steel is comp...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| yield strength | aaaaa | aaaaa |
| yield strength | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to the field of steel making and provides atmospheric corrosion-resistant molten structural steel. The molten structural steel is composed of 0.01%-0.09% by weight of C, 0.15%-0.35% by weight of Si, 0.30%-0.60% by weight of Mn, 0.30%-0.40% by weight of Cu, 0.20%-0.30% by weight of Ni, 3.5%-5.0% by weight of Cr, 0.13%-0.15% by weight of V, 0.015%-0.020% by weight of N, less than or equal to 0.030% of P, less than or equal to 0.020% of S and the balance of inescapable impurities and Fe. The invention provides atmospheric corrosion-resistant structural steel and a productionmethod thereof. Through continuous casting of molten steel, the central quality of a casting blank is improved, central cracks and central shrinkage cavity are avoided, the quality of the high strength and high atmospheric corrosion resistant structural steel blank is improved, a casting blank qualification rate is greatly improved and good atmospheric corrosion resistance and high strength of the atmospheric corrosion-resistant structural steel are obtained.
Description
technical field [0001] The invention relates to an atmospheric corrosion-resistant steel molten steel, an atmospheric corrosion-resistant steel obtained by continuous casting and rolling using the molten steel of the invention, a production method of the atmospheric corrosion-resistant steel and the atmospheric corrosion-resistant steel obtained by the method. Background technique [0002] Atmospheric corrosion-resistant steel is a very important class of steel. Its atmospheric corrosion resistance is 2-8 times that of ordinary steel, and its paintability is improved by 1.5-10 times. Due to the effectiveness of atmospheric corrosion resistance steel compared with ordinary steel, and its good economic efficiency compared with stainless steel, it has been developed rapidly in various countries in the world. Various steel structures used in the open air, railway vehicles and bridges are is the scope of its application. [0003] The early atmospheric corrosion-resistant steel v...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/18C22C38/02C22C38/04C22C38/16C22C38/08C22C38/12C22C33/04B22D11/124C21D8/00
Inventor 刘明邓通武郭跃华何为
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP