Titanium alloy bar welding method

A welding method and titanium alloy technology, applied in welding equipment, welding accessories, welding/welding/cutting items, etc., can solve the problems of incomplete penetration fusion, inability to meet the quality requirements of radiographic flaw detection, and deficiencies

Active Publication Date: 2020-10-27
WUHAN MARINE MACHINERY PLANT
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, according to the root cleaning treatment specifications for titanium alloy rods, when grinding with grinding wheels, the particles of the grinding wheel will adhere to the groove surface, which needs to be treated separately, which will affect the production efficiency and make it difficult to guarantee the welding quality
Moreover, when welding titanium alloy rods, if the straightness of the two rods after butt joint does not meet the requirements, it will also lead to defects such as cracks, incomplete penetration and insufficient fusion after welding, resulting in failure to meet the quality requirements of radiographic flaw detection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Titanium alloy bar welding method
  • Titanium alloy bar welding method
  • Titanium alloy bar welding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] In order to make the purpose, technical solution and advantages of the present disclosure clearer, the implementation manners of the present disclosure will be further described in detail below in conjunction with the accompanying drawings.

[0026] In the related art, when titanium alloy rods are welded, the end faces of two titanium alloy rods to be welded (that is, welded joints) are triangular, so that after the two titanium alloy rods are relatively butted, a double-sided groove can be formed. to be welded.

[0027] According to the technical requirements, the titanium alloy bar needs to be inspected by radiograph after welding, which requires NB / T47013-2015 Class I qualification, and the straightness of the welded titanium alloy bar is ≤1.5mm.

[0028] In the related art, usually after rooting welding is performed on one side of the double-sided groove of the titanium alloy rod, root cleaning is performed on the other side of the double-sided groove to ensure the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a titanium alloy bar welding method, and belongs to the technical field of welding. The titanium alloy bar welding method comprises the following steps that two to-be-welded titanium alloy bars are correspondingly arranged on positioning devices; the two positioning devices are mounted on the two positioning devices; the distance between two positioning frames is adjusted, the to-be-welded end faces of the two to-be-welded titanium alloy bars are controlled to be in butt joint oppositely, and a double groove is formed; meanwhile, backing runs are formed on the two sidesof the double groove through welding, so that molten pools located on the two sides of the double groove are molten into one molten pool; and multiple layers of welding runs are formed on the backingruns on the two sides of the double groove in a welding mode, and welding of the titanium alloy bars are completed. According to the titanium alloy bar welding method, the straightness of the butted bars can meet the requirement, and back chipping treatment is avoided after backing weld, so that the welding quality is ensured.

Description

technical field [0001] The present disclosure relates to the field of welding technology, in particular to a welding method for titanium alloy rods. Background technique [0002] Titanium alloy bars are usually welded by butt welding. Butt welding means that two bars are respectively placed between two clamping devices, and the end faces to be welded on the two bars are controlled to be relatively butted together, and the two bars are connected together. The method of welding by electric heating at the butt contact of the material. Usually the welding groove of titanium alloy rod adopts the form of double-sided groove. In the related art, it is required to carry out radiographic flaw detection after the welding of the titanium alloy bar, so as to ensure that the quality of the welded titanium alloy bar meets the requirements. [0003] In order to improve the welding quality of titanium alloy rods, usually after backing welding is performed on one side of the double-sided g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K9/00B23K9/32B23K103/14
CPCB23K9/00B23K9/0026B23K9/32B23K2103/14
Inventor 蒋文学赵金明代俊杨新明张汉斌李阳
Owner WUHAN MARINE MACHINERY PLANT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products