Welding method of titanium alloy bar

A welding method and titanium alloy technology, applied in welding equipment, welding accessories, welding/welding/cutting items, etc., can solve problems such as inability to meet the quality requirements of radiographic flaw detection, difficulty in guaranteeing welding quality, and incomplete penetration and fusion

Active Publication Date: 2021-11-16
WUHAN MARINE MACHINERY PLANT
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, according to the root cleaning treatment specifications for titanium alloy rods, when grinding with grinding wheels, the particles of the grinding wheel will adhere to the groove surface, which needs to be treated separately, which will affect the production efficiency and make it difficult to guarantee the welding quality
Moreover, when welding titanium alloy rods, if the straightness of the two rods after butt joint does not meet the requirements, it will also lead to defects such as cracks, incomplete penetration and insufficient fusion after welding, resulting in failure to meet the quality requirements of radiographic flaw detection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding method of titanium alloy bar
  • Welding method of titanium alloy bar
  • Welding method of titanium alloy bar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] In order to make the purpose, technical solution and advantages of the present disclosure clearer, the implementation manners of the present disclosure will be further described in detail below in conjunction with the accompanying drawings.

[0026] In the related art, when titanium alloy rods are welded, the end faces of two titanium alloy rods to be welded (that is, welded joints) are triangular, so that after the two titanium alloy rods are relatively butted, a double-sided groove can be formed. to be welded.

[0027] According to the technical requirements, the titanium alloy bar needs to be inspected by radiograph after welding, which requires NB / T47013-2015 Class I qualification, and the straightness of the welded titanium alloy bar is ≤1.5mm.

[0028] In the related art, usually after rooting welding is performed on one side of the double-sided groove of the titanium alloy rod, root cleaning is performed on the other side of the double-sided groove to ensure the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The disclosure provides a welding method for titanium alloy rods, belonging to the field of welding technology, comprising: installing two titanium alloy rods to be welded on two positioning devices respectively; installing the two positioning devices on the adjusting device ;Adjust the distance between the two positioning frames, and control the opposite butt joint of the end faces to be welded on the two titanium alloy bars to be welded to form a double-sided groove; at the same time, weld on both sides of the double-sided groove to form a bottom weld bead , so that the molten pools on both sides of the double-sided groove are fused into a molten pool; welding is formed on the bottom weld bead on both sides of the double-sided groove to form a multi-layer weld bead, and the welding of the titanium alloy bar is completed. The disclosure can ensure that the straightness of the bars after butt jointing meets the requirements, and avoid root cleaning after bottom welding, so as to ensure the welding quality.

Description

technical field [0001] The present disclosure relates to the field of welding technology, in particular to a welding method for titanium alloy rods. Background technique [0002] Titanium alloy bars are usually welded by butt welding. Butt welding means that two bars are respectively placed between two clamping devices, and the end faces to be welded on the two bars are controlled to be relatively butted together, and the two bars are connected together. The method of welding by electric heating at the butt contact of the material. Usually the welding groove of titanium alloy rod adopts the form of double-sided groove. In the related art, it is required to carry out radiographic flaw detection after the welding of the titanium alloy bar, so as to ensure that the quality of the welded titanium alloy bar meets the requirements. [0003] In order to improve the welding quality of titanium alloy rods, usually after backing welding is performed on one side of the double-sided g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/00B23K9/32B23K103/14
CPCB23K9/00B23K9/0026B23K9/32B23K2103/14
Inventor 蒋文学赵金明代俊杨新明张汉斌李阳
Owner WUHAN MARINE MACHINERY PLANT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products