Formula and production method for composite plastic pipe

A production method and plastic pipe technology, applied in the field of plastic pipes, can solve the problems of poor use effect, lack of heat dissipation performance, and no production method, etc., and achieve the effects of improving heat dissipation performance, convenient production, and good use effect

CN109721831AActive Publication Date: 2019-05-07山东中德石油装备有限公司
8 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
Publication Date
2019-05-07

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention provides a formula and production method for a composite plastic pipe. The invention solves the technical problem that a current composite plastic pipe has too simple components, does not have better heat dissipation performance, and has a poor use effect and no corresponding production method. The composite plastic pipe is prepared from the following components, in parts by weight:100-120 parts of polypropylene, 12-16 parts of polyolefin, 2-6 parts of reinforcing fibers, 3-7 parts of acrylic resin, 1.5-4.5 parts of an antibacterial agent, 7-8 parts of a stabilizing agent, 0.6-1.2 parts of a plasticizing agent, 15-20 parts of mineral oil, 4-6 parts of stearic acid and 18-26 parts of silicon carbide. The composite plastic pipe provided by the invention has the advantages of good use effects.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the technical field of plastic pipes, and relates to a compound plastic pipe formula and a production method. Background technique

[0002] Plastic pipes have been widely used in construction projects due to their light weight, corrosion resistance, and convenient processing.

[0003] After searching, for example, Chinese patent literature discloses a composite plastic pipe [application number: 201510333839.1; publication number: CN 105037925A]. This composite plastic pipe is characterized in that it consists of the following raw material components: 50-60 parts of polypropylene, 40-45 parts of polyvinyl chloride, 30-35 parts of silica gel, 50-55 parts of polystyrene, 40 parts -50 parts of phenolic resin, 30-35 parts of epoxy resin, 8-10 parts of potassium borate, 10-12 parts of polyurethane, 6-8 parts of polycarbonate, 8-10 parts of zinc borate, 6-8 parts of propylene carbonate, 15-20 parts neoprene, 5-8 parts rosin, 5-7 par...

Examples

Embodiment Construction

[0042] The following are specific embodiments of the present invention and in conjunction with the accompanying drawings, the technical solutions of the present invention are further described, but the present invention is not limited to these embodiments.

[0043] The composite plastic pipe formula is made of the following components by weight: 100-120 parts of polypropylene, 12-16 parts of polyolefin, 2-6 parts of reinforcing fiber, 3-7 parts of acrylic resin, and 1.5-4.5 parts of antibacterial agent parts, 7-8 parts of stabilizer, 0.6-1.2 parts of plasticizer, 15-20 parts of white oil, 4-6 parts of stearic acid and 18-26 parts of silicon carbide; in the present embodiment, by the following parts by weight Made of components: 110 parts of polypropylene, 14 parts of polyolefin, 4 parts of reinforcing fiber, 5 parts of acrylic resin, 3.2 parts of antibacterial agent, 7 parts of stabilizer, 0.7 part of plasticizer, 17 parts of white oil, stearic acid 5 parts and 20 parts of sil...