Method for continuously preparing mesophase carbon microspheres for co-production of impregnating agent asphalt and coated asphalt

A technology of mesophase carbon microspheres and mesophase carbon microspheres, which is applied to the processing of tar pitch/petroleum pitch/natural pitch by chemical methods, the processing of tar pitch/petroleum pitch/natural pitch by selective extraction, the preparation/purification of carbon, etc. It can solve the problems of heavy environmental pollution and large energy consumption, and achieve the effect of avoiding material hanging on the wall, avoiding asphalt coking, and promoting uniform and rapid growth

Active Publication Date: 2017-03-15
ANSHAN XINGDE MATERIAL SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the above-mentioned problems existing in the preparation technology of existing mesocarbon microspheres, the present invention provides a method for continuously preparing mesocarbon microspheres for co-production of impregnating agent pitch and coated pitch, which is carried out by continuous preparation equipment and thermal polymerization method Continuous production, solving problems such as large energy consumption and heavy environmental pollution, and obtaining a variety of products with stable quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for continuously preparing mesophase carbon microspheres for co-production of impregnating agent asphalt and coated asphalt
  • Method for continuously preparing mesophase carbon microspheres for co-production of impregnating agent asphalt and coated asphalt
  • Method for continuously preparing mesophase carbon microspheres for co-production of impregnating agent asphalt and coated asphalt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] Under the condition of nitrogen atmosphere, the temperature is 180 ℃ medium temperature coal tar pitch and the temperature is 180 ℃ stabilizer mixed, mixing ratio is medium temperature coal tar pitch by mass ratio: stabilizer=1:0.1, obtains the mixed material; described stable The agent is anthracene oil;

[0059] The mixed material is heated to 350°C and sent to the rapid temperature riser. In the rapid temperature riser, the temperature of the material is raised to 410°C within 1 second, and then enters the continuous polymerization reactor for polymerization at 410°C. The medium temperature coal tar pitch is controlled to continuously The reaction time in the polymerization reactor is 6h, and after the reaction is completed, the material discharged from the continuous polymerization reactor contains polymerized pitch of mesophase carbon microspheres;

[0060] Cool the polymerized pitch containing mesocarbon microspheres to 290°C, then mix it with the extractant and s...

Embodiment 2

[0066] Method is with embodiment 1, and difference is:

[0067] (1) Under the condition of nitrogen atmosphere, mix the medium-temperature coal tar pitch with a temperature of 210°C and the stabilizer with a temperature of 210°C, and the mixing ratio is medium-temperature coal tar pitch:stabilizer=1:0.5 according to the mass ratio, and the mixture is obtained; The stabilizer mentioned above is washing oil;

[0068] (2) Heat the mixed material to 360°C and send it to the rapid temperature increaser. In the rapid temperature increaser, the material is heated to 430°C within 3 seconds, and then enters the continuous polymerization reactor to carry out polymerization reaction at 430°C to control the medium-temperature coal The reaction time of asphalt in the continuous polymerization reactor is 5h;

[0069] (3) Cool down the polymerized pitch containing mesocarbon microspheres to 310°C, then mix it with the extractant and send it to the extraction tank for extraction. The mixing ...

Embodiment 3

[0072] Method is with embodiment 1, and difference is:

[0073] (1) Under the condition of nitrogen atmosphere, mix the medium-temperature coal tar pitch with a temperature of 200°C and the stabilizer with a temperature of 20°C, and the mixing ratio is medium-temperature coal tar pitch:stabilizer=1:1 by mass ratio to obtain a mixture; The stabilizer mentioned above is steam;

[0074] (2) Heat the mixed material to 380°C and send it to the rapid temperature riser. In the rapid temperature riser, the material is heated to 450°C within 5 seconds, and then enters the continuous polymerization reactor to carry out polymerization reaction at 450°C to control the medium-temperature coal The reaction time of asphalt in the continuous polymerization reactor is 4h;

[0075] (3) Cool the polymerized pitch containing mesocarbon microspheres to 340°C, mix it with the extractant and send it to the extraction tank for extraction. The mixing ratio is the polymerized pitch containing mesocarb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for continuously preparing mesophase carbon microspheres for co-production of impregnating agent asphalt and coated asphalt, which is carried out as follows: (1) under nitrogen atmosphere, medium temperature coal tar pitch and stabilizer are mixed; (2) heating to 350 After ~380°C, it is sent to the rapid warmer, and the temperature is raised to 410~450°C in 1~5s for polymerization; (3) Cool down to 290~340°C and extract with the extractant; (4) Centrifugal separation, solid phase Dry to obtain mesophase carbon microsphere products; (5) The mother liquor is evaporated in a distillation tower to recover the extractant, and the remaining material at the bottom of the tower is used as an impregnating agent pitch or a reforming reactor is used for reforming reaction. The method of the invention fundamentally solves the problems of large energy consumption, heavy environmental pollution, low product yield, high cost, unstable quality and single variety in the traditional production process.

Description

technical field [0001] The invention relates to the technical field of mesocarbon microsphere materials, in particular to a method for continuously preparing mesocarbon microspheres for co-production of impregnating agent pitch and coating pitch. Background technique [0002] The negative electrode material is one of the important factors affecting the performance of lithium-ion batteries. Graphite or modified graphite is generally used in the prior art. However, its theoretical lithium intercalation capacity of 372mAh / g can no longer meet the demand, and its unique layered structure leads to limited times. cycle stability, and is also highly sensitive to the electrolyte, so it is urgent to find a new type of anode material to replace graphite. [0003] Mesophase carbon microspheres are ideal raw materials for negative electrode materials of lithium-ion batteries. At present, the processes for producing mesocarbon microspheres from coal tar pitch mainly include thermal cond...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/05C10C3/02C10C3/08
Inventor 朱兴建张力王永志王莹
Owner ANSHAN XINGDE MATERIAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com