Low temperature co-fired PTC ceramic material composition

A ceramic material and low-temperature co-firing technology, which is applied in the field of new PTC ceramic material composition, can solve the problems of PbO-BN glass phase to reduce the sintering temperature of PTC ceramic material, and achieve the effect of wide application range

Inactive Publication Date: 2017-06-16
QINGDAO XIANGZHI ELECTRONICS TECH CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Judging from the recently announced technology, there has been no report on the use of PbO-BN glass phases to reduce the sintering temperature of PTC ceramic materials and at the same time have high-performance PTC ceramic materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A low-temperature co-fired PTC ceramic material composition is composed of a ceramic phase and a glass phase. The ceramic phase is a common PTC ceramic material, and the glass phase is a PbO-BN series material. The molar ratio of PbO-BN material is 1.5. Now the weight percentage of PbO and BN is: PbO: BN=93: 7 (wt %)

[0015] PTC ceramic materials need to be synthesized in advance, and the synthesis process is as follows:

[0016] BaCO 3 、TiO 2 , Y 2 o 3 , SrCO 3 , CaCO 3 , SiO 2 and Mn(NO 3 ) 2 , according to the chemical equation (1) of the following common PTC ceramic materials:

[0017] Ba 0.85 Ca 0.15 Ti 1.01 o 3 +0.25mol% Y 2 o 3 +2.4mol% SiO 2 +0.08mol%Mn(NO 3 ) 2 (1)

[0018] Mixing ingredients-ball milling-drying-pre-calcination synthesis, the temperature of pre-calcination synthesis is preferably 1100°C to 1200°C.

[0019] PbO-BN materials need to be mixed in advance, and the mixing process is as follows:

[0020] The molar ratio of PbO ...

Embodiment 2

[0024] A low-temperature co-fired PTC ceramic material composition is composed of a ceramic phase and a glass phase. The ceramic phase is common PTC ceramic material, and the glass phase is PbO-BN material. The molar ratio of PbO-BN material is 2. Now the weight percentage of PbO and BN is: PbO: BN=95: 5 (wt %)

[0025] PTC ceramic materials need to be synthesized in advance, and the synthesis process is as follows:

[0026] BaCO3, TiO2, Y203, SrCO3, CaCO3, SiO2 and Mn(NO3)2, according to the chemical equation (1) of the following common PTC ceramic materials:

[0027] Ba0.85Ca0.15Ti1.01O3+0.25mol%Y2O3+2.4mol%SiO2+0.08mol%Mn(NO3)2(1)

[0028] Mixing ingredients-ball milling-drying-pre-calcination synthesis, the temperature of pre-calcination synthesis is preferably 1100°C to 1200°C.

[0029] PbO-BN materials need to be mixed in advance, and the mixing process is as follows:

[0030] The molar ratio of PbO and BN is 2. The weight percentage of PbO and BN is: PbO:BN=95:5 (wt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a novel PTC ceramic material composition, specifically, a low-temperature co-fired PTC ceramic material composition. The composition includes a ceramic phase and a glass phase, and is characterized in that: the ceramic phase is a conventional PTC ceramic material, the glass phase is a PbO-BN material, and the content of the PbO-BN material is 1-10 wt%. The content of ceramic material is 90-99wt%. This product uses PbO-BN glass phase to reduce the sintering temperature of PTC ceramic materials, and has high-performance PTC characteristics, and has a wide range of applications.

Description

technical field [0001] The invention relates to a novel PTC ceramic material composition, specifically, a low-temperature co-fired PTC ceramic material composition. Background technique [0002] In recent years, driven by the rapid development of semiconductor technology, electronic components continue to develop in the direction of miniaturization, integration and high frequency. With the rapid development of SMT technology, it has greatly promoted the miniaturization, miniaturization, integration and chipping of electronic equipment and electronic components, and the development and preparation of chip and miniaturized PTC components with multi-layer structure It has become a research hotspot and focus at home and abroad. In order to achieve chipping and miniaturization of multilayer PTC components, the PTC material used must have a good PTC effect, high withstand voltage, and low resistivity under low-temperature sintering conditions; Microcircuits and other wider appli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/468C04B35/626
CPCC04B35/468C04B35/626C04B2235/3208C04B2235/3213C04B2235/3225C04B2235/3262C04B2235/3296C04B2235/3418C04B2235/386C04B2235/5436
Inventor 李春花
Owner QINGDAO XIANGZHI ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap