Red plastic color master batch

Abstract

The invention discloses a red plastic color master batch, which is prepared from the following ingredients in parts by weight: 880 to 960 parts of polypropylene, 20 to 40 parts of polyethylene wax, 5 to 15 parts of fast scarlet, 5 to 15 parts of zinc stearate, 10 to 30 parts of calcium carbonate, 0.1 to 0.25 part of stearate, 0.3 to 0.8 part of iron oxide red and 1 to 5 parts of phthalocyanine red. The red plastic color master batch provided by the invention solves the technical problems of poor color concentration and insufficient hardness of the traditional red plastic master batch.

Description

Technical Field

[0001] The invention relates to the technical field of plastic masterbatches, in particular to a red plastic masterbatch. Background Art

[0002] The existing red plastic masterbatch has poor color concentration and insufficient hardness, which cannot meet market requirements. It is urgent to develop a plastic masterbatch with high red color concentration and high hardness to meet market demand and improve product adaptability. Summary of the invention

[0003] The purpose of the invention is to provide a red plastic masterbatch to solve the technical problems of poor color concentration and insufficient hardness of traditional red plastic masterbatch.

[0004] To achieve the above purpose, the present invention provides the following technical scheme: comprising the following components by weight: 880-960 parts of polypropylene, 20-40 parts of polyethylene wax, 5-15 parts of fast red, 5-15 parts of zinc stearate, 10-30 parts of calcium carbonate, 0.1-0.25 parts of stearate, 0.3-0.8 parts of red iron oxide, and 1-5 parts of phthalocyanine red.

[0005] 900-940 parts of polypropylene, 25-35 parts of polyethylene wax, 7-13 parts of fast red, 7-13 parts of zinc stearate, 15-25 parts of calcium carbonate, 0.1-0.2 parts of stearate, 0.4-0.7 parts of red iron oxide, and 2-4 parts of phthalocyanine red.

[0006] 910-930 parts of polypropylene, 28-32 parts of polyethylene wax, 8-12 parts of fast red, 8-12 parts of zinc stearate, 18-22 parts of calcium carbonate, 0.12-0.18 parts of stearate, 0.5-0.6 parts of red iron oxide, and 2.5-3.5 parts of phthalocyanine red.

[0007] Compared with the prior art, the beneficial effect of the present invention is that the color concentration and hardness of the plastic are improved by configuring multiple components. DETAILED DESCRIPTION

[0008] The technical solutions in the embodiments of the present invention are described clearly and completely below. Obviously, the described embodiments are only part of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by ordinary technicians in this field without creative work are within the scope of protection of the present invention.

[0009] Example 1

[0010] The invention provides a technical solution for a red plastic masterbatch, which comprises the following components by weight: 880-960 parts of polypropylene, 20-40 parts of polyethylene wax, 5-15 parts of fast red, 5-15 parts of zinc stearate, 10-30 parts of calcium carbonate, 0.1-0.25 parts of stearate, 0.3-0.8 parts of red iron oxide and 1-5 parts of phthalocyanine red.

[0011] Example 2

[0012] The invention comprises the following components by weight: 900-940 parts of polypropylene, 25-35 parts of polyethylene wax, 7-13 parts of fast red, 7-13 parts of zinc stearate, 15-25 parts of calcium carbonate, 0.1-0.2 parts of stearate, 0.4-0.7 parts of red iron oxide and 2-4 parts of phthalocyanine red.

[0013] Example 3

[0014] The invention comprises the following components by weight: 910-930 parts of polypropylene, 28-32 parts of polyethylene wax, 8-12 parts of fast red, 8-12 parts of zinc stearate, 18-22 parts of calcium carbonate, 0.12-0.18 parts of stearate, 0.5-0.6 parts of red iron oxide and 2.5-3.5 parts of phthalocyanine red.

[0015] Although the present invention has been described in detail with reference to the aforementioned embodiments, it is still possible for those skilled in the art to modify the technical solutions described in the aforementioned embodiments, or to make equivalent substitutions for some of the technical features therein. Any modifications, equivalent substitutions, improvements, etc. made within the spirit and principles of the present invention should be included in the protection scope of the present invention.

Claims

1. A red plastic masterbatch, characterized in that: The invention comprises the following components by weight: 880-960 parts of polypropylene, 20-40 parts of polyethylene wax, 5-15 parts of fast red, 5-15 parts of zinc stearate, 10-30 parts of calcium carbonate, 0.1-0.25 parts of stearate, 0.3-0.8 parts of red iron oxide and 1-5 parts of phthalocyanine red.

2. The red plastic masterbatch according to claim 1, characterized in that: 900-940 parts of polypropylene, 25-35 parts of polyethylene wax, 7-13 parts of fast red, 7-13 parts of zinc stearate, 15-25 parts of calcium carbonate, 0.1-0.2 parts of stearate, 0.4-0.7 parts of red iron oxide, and 2-4 parts of phthalocyanine red.

3. The red plastic masterbatch according to claim 2, characterized in that: 910-930 parts of polypropylene, 28-32 parts of polyethylene wax, 8-12 parts of fast red, 8-12 parts of zinc stearate, 18-22 parts of calcium carbonate, 0.12-0.18 parts of stearate, 0.5-0.6 parts of red iron oxide, and 2.5-3.5 parts of phthalocyanine red.