Manufacture methods of contact wire and rod blank

A technology for contacting wires and wire rods, which is used in metal rolling, manufacturing of extensible conductors/cables, rods/rods/wires/strip conductors, etc. and other problems to achieve the effect of simplifying smelting and heat treatment problems, maintaining electrical conductivity and good physical properties

Active Publication Date: 2011-04-13
CHINA RAILWAY CONSTR ELECTRIFICATION BUREAU GRP CO LTD +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, although precipitation-strengthened copper alloy materials have been widely used in metallurgy and other industrial fields, they have not yet been practically applied to railway contact wires. The reason is that the contact wires are longer, so that the volume and weight of the whole rod blank are larger; The requirements for smelting equipment are very high, and it is necessary to prevent the oxidation of alloy elements; the large-volume billet is not easy to be heated evenly during solid melting, and the solid-melting effect becomes poor; the large-volume copper alloy solid-melting furnace is expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacture methods of contact wire and rod blank
  • Manufacture methods of contact wire and rod blank

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] Such as figure 1 as shown, figure 1 It is a schematic flow chart of the preparation method of the contact wire according to the present invention, which may specifically include the following steps:

[0031] Step 101: Melting the copper alloy; various appropriate smelting methods can be used, and it is necessary to ensure that chromium accounts for 0.4% to 1.0% of the total weight of the copper alloy, zirconium accounts for 0.05% to 0.2%, and the balance is composed of copper and other elements and unavoidable impurities; other elements can be metals such as rare earths or magnesium, accounting for 0.05% of the total weight of the copper alloy, and the content of impurities such as oxides is as low as possible.

[0032] Step 102: preparing an oxygen-free casting rod; pouring is performed under a protective atmosphere (for example, argon protection), or an oxygen-free casting rod is prepared by means of upward (horizontal) continuous casting, and the size of the obtaine...

Embodiment 1

[0042] 1) Non-vacuum melting copper alloy. Copper-chromium alloy and copper-zirconium alloy are added in the form of master alloy. In the furnace, chromium element accounts for 0.6% of the total weight, zirconium accounts for 0.1%, magnesium accounts for 0.05%, and the rest is copper. Argon protection.

[0043] 2) Prepare an oxygen-free casting rod.

[0044] 3) Put the casting rod into the solid melting furnace, the solid melting temperature is 950°C, keep it warm for 2 hours and then carry out water quenching.

[0045] 4) Clean the surface of the billet rod after solidification and connect it to ensure that the connection is free of oxides and other impurities and repair the connection.

[0046] 5) Send the connected billet rods into the Kangfu extrusion machine for continuous extrusion and cooling to obtain the contact wire rod billet.

[0047] 6) The billet is cold-rolled with a deformation of 45%.

[0048] 7) Carry out aging treatment, the temperature is 550 ℃, keep wa...

Embodiment 2

[0051] 1) Add electrolytic copper, rare earth, magnesium, chromium and zirconium into the vacuum induction furnace, wherein chromium accounts for 0.6% of the total weight, zirconium accounts for 0.1%, rare earth accounts for 0.05%, magnesium accounts for 0.05%, and the rest is copper. The melting temperature is 1300°C, and the temperature is lowered to 1250°C for casting after melting.

[0052] 2) Process the alloy billet into an oxygen-free cast rod.

[0053]3) Put the cast rod coil into the solid melting furnace, the solid melting temperature is 950°C, heat it for 2 hours and then water quench.

[0054] 4) Clean the surface of the billet rod after solidification, and make a seamless connection to ensure that the connection is free of oxides and other impurities and repair the connection.

[0055] 5) Send the connected billet rods into the Kangfu extrusion machine for continuous extrusion and cooling to obtain the contact wire rod billet.

[0056] 6) The billet is cold-roll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses the manufacture methods of a contact wire and a rod blank. The manufacture method of the contact wire comprises the following steps: manufacturing a plurality of precipitation-strengthened copper alloy oxygen-free cast rods by smelting; preprocessing the oxygen-free cast rods to obtain a plurality of blank rods; connecting the plurality of blank rods seamlessly; feeding the connected blank rods to an extruder for continuous extrusion, and cooling the extruded contact wire rod blanks; cold-rolling the contact wire rod blanks, and subjecting to aging treatment; and cold-drawing the contact wire rod blanks for multiple times according to the predetermined section size of the contact wire to obtain the contact wire. The method can simplify the smelting and thermal treatment of the precipitation-strengthened copper alloy contact wire material. The manufactured contact wire has the advantages of fine and dense grains, higher mechanical strength, good conductivity, and better physical performance, and can meet the length requirement for railway construction.

Description

technical field [0001] The invention relates to the technical field of power supply wires, in particular to a method for preparing a contact wire and a rod blank. Background technique [0002] Electrified railway contact wire is one of the power supply wires used in the worst working environment, and its performance directly affects the safe operation of high-speed trains. The high-speed railway contact wire has a large rated working tension, and is constantly impacted and rubbed by the pantograph during long-term operation, and needs to endure arc ablation, temperature changes and the influence of the environment. In this case, the contact wire is required to have high tensile strength, wear resistance, corrosion resistance, good high temperature softening resistance, and good electrical conductivity for energy saving requirements. These are only the required material properties of the wire itself. In practical application, issues such as wire production cost, large-lengt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B13/008H01B5/02B21C23/02B21B1/16B21C1/02
Inventor 郑斌寇宗乾李学斌万传军孟宪浩侯晓俊张强刘建涛
Owner CHINA RAILWAY CONSTR ELECTRIFICATION BUREAU GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com