A kind of chilled iron coating for wet mold casting ductile iron castings and its application method

A technology for casting ductile iron and chilled iron coating, which is applied in the field of chilled iron coating for wet mold casting ductile iron castings. It can solve the problems of a large amount of harmful gas and dust, easy to produce pore defects, etc., and achieve fine internal structure and simple preparation method. Fast, low production cost effect

Active Publication Date: 2015-10-28
SHANDONG YUANTONG MASCH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the materials commonly used in the industry to prepare coatings, such as graphitic alcohol-based coatings, are organic substances like alcohol, which are easy to burn and generate gas. Therefore, these materials will inevitably produce a large amount of harmful gas and smoke when pouring, and at the same time make the product very easy. porosity defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of chilled iron coating for wet mold casting ductile iron castings and its application method
  • A kind of chilled iron coating for wet mold casting ductile iron castings and its application method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～7

[0013] The mass percentage components of the cold iron coating for the molding of the green cast ductile iron casting are shown in Table 1, and Example 3 is the best implementation mode.

[0014] Table 1 Examples 1-5 Cold iron coatings for wet casting ductile iron castings (by mass percentage)

[0015]

[0016] Graphite alcohol-based paint, alcohol and iron oxide powder are put into a mixer in proportion, and stirred evenly at room temperature, that is, the chilled iron paint for wet casting ductile iron castings in Examples 1-5. When pouring, evenly brush a layer of uniformly mixed chilled iron paint on the surface of the chilled iron in the molding sand. The thickness of the chilled iron paint is 1-2mm. It is heated and dried before pouring.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a chiller coating for the molding of green-sand-casting ductile iron castings and an application method thereof, which belong to the technical field of coatings for casting molding. The coating is prepared from the following components in percentage by mass: 55-60% of a graphite alcohol based coating, 30-35% of alcohol and 5-10% of ferric oxide powder. When in use, the coating is uniformly coated on the surface of chiller, and the coating thickness is 1-2 mm. By using the coating for the molding of green-sand-casting ductile iron castings disclosed by the invention, no harm is caused to castings, no influence is caused on the environment, and the quenching of ductile iron castings is reduced; meanwhile, because gas in a cavity is reduced, and the cooling speed is high, a casting has no pore defect, and the finished product ratio of the casting can reach 100%, therefore, the coating has a broad market prospect.

Description

technical field [0001] The invention belongs to the technical field of coatings for casting molding, and in particular relates to a cold iron coating for molding of wet-type casting ductile iron castings and a use method thereof. Background technique [0002] In my country's foundry industry, ductile iron products generally require low-temperature pouring, which produces a large amount of gas during pouring, resulting in castings that are prone to fire and porosity defects; and ductile iron castings have subcutaneous porosity on the processed surface after processing, resulting in a large number of waste products . Due to the large amount of gas generated in the wet casting cavity after drying, there is currently no suitable molding coating product for wet casting ductile iron castings. [0003] In recent years, with the continuous improvement of product requirements, how to use a ductile iron chilled iron coating material to reduce the occurrence of pores has become an impo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22C3/00B22D15/00
Inventor 周仕勇李兴华魏汝斌
Owner SHANDONG YUANTONG MASCH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com