A kind of inner layer iron printing paint and iron printing method

A technology of iron printing paint and inner layer, which is applied in the field of inner layer iron printing paint and iron printing paint, and can solve the problems of poor adhesion of UV iron printing paint and inconvenient painting

Active Publication Date: 2015-09-16
无锡品源科技咨询有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adhesion of UV iron printing paint is poor, it is not convenient to paint on it, and it is not as good as heat curing iron printing paint in terms of alkali resistance, post-processing resistance, flexibility, wear resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of inner layer iron printing paint and iron printing method
  • A kind of inner layer iron printing paint and iron printing method
  • A kind of inner layer iron printing paint and iron printing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] A kind of inner layer iron printing coating comprises following components by mass percentage:

[0080]

[0081]

[0082] Preparation method: Mix the raw materials of the inner iron printing coating according to the formula ratio, then stir, and at the same time raise the temperature to react until the solution is uniform.

Embodiment 2

[0084] A kind of inner layer iron printing coating comprises following components by mass percentage:

[0085]

[0086] The preparation method is the same as that of Example 1.

Embodiment 3

[0088] A kind of inner layer iron printing coating comprises following components by mass percentage:

[0089]

[0090] The preparation method is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to inner layer metal decorating paint. The inner layer metal decorating paint comprises the following components: (a) bisphenol A, epoxy chloropropane and a catalyst; (b) an amino resin crosslinking agent; (c) a solvent; and (d) wax powder, wherein the catalyst is used for preparing bisphenol A epoxy resin by the bisphenol A and the epoxy chloropropane; and the mass ratio of the bisphenol to the epoxy chloropropane is (1.17-3.5): 1, and addition amount is 1-8wt%. The inner layer metal decorating paint provided by the invention can be cured in only 25-120 seconds, and continuous printing and coating can be carried out; and the inner layer metal decorating paint provided by the invention has high corrosion resistance.

Description

technical field [0001] The invention relates to an iron printing paint, in particular to an inner layer iron printing paint, which belongs to the technical field of can making. Background technique [0002] Tinplate, also known as tin-plated iron, is a common name for electroplated tin-plated steel sheet, and its English abbreviation is SPTE. It refers to cold-rolled low-carbon thin steel sheet or steel strip coated with commercial pure tin on both sides. Tin mainly plays the role of preventing corrosion and rust. It combines the strength and formability of steel with the corrosion resistance, solderability and beautiful appearance of tin in one material, which is corrosion-resistant, non-toxic and high-strength. , good ductility characteristics. Therefore, it is widely used in various fields such as packaging containers (canning, barrel making and food and beverage packaging), electronic products, household appliances, automobiles, motorcycles, etc. Of course, when the pac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/02C09D7/12C09D5/08C09D11/102C09D11/03B05D7/24B05D3/02
Inventor 孙才清吴爱明
Owner 无锡品源科技咨询有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com