A brick adobe fired into a glass-ceramic composite board at one time

A technology of glass-ceramic and glass-ceramic frit, which is applied in the field of architectural ceramics, can solve the problems of pinholes or dissolved holes, low yield, low flatness, etc., and achieves no influence on color effects and high yield. Effect

Active Publication Date: 2015-11-18
江苏鑫宝门窗制造有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The adobe of the glass-ceramic composite board fired at one time includes a green body layer, a bottom glaze layer and a glass-ceramic layer from bottom to top. The glass-ceramic layer is generally composed of glass-ceramic frit particles. The adobe is pressed, glazed and printed. Finally, a layer of glass-ceramic frit particles will be placed on the surface of the bottom glaze layer, and then sent to the kiln for firing. When transported into the kiln, it will pass through a low negative pressure pre-tropical zone. The glass-ceramic frit particles are easy to be sucked away because of their light weight, resulting in the lack of many glass-ceramic frit particles on the surface layer. It greatly affects the quality and aesthetics of the glass-ceramic composite board, and the qualified yield is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A brick adobe fired into a glass-ceramic composite board at one time
  • A brick adobe fired into a glass-ceramic composite board at one time
  • A brick adobe fired into a glass-ceramic composite board at one time

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-1

[0025] The high-temperature transparent glass-ceramic frit particles (purchased from Quincy Carloby Glaze Company, 90 mesh) are clothed on the body surface through the printing process, and then the glass-ceramic frit made in one layer of embodiment 1 is sprayed Particle fixative, you can get the required adobe. This kind of adobe can be sent into a kiln for firing at 1200°C, and the edges are ground and chamfered to obtain a finished glass-ceramic composite board with uniform distribution and complete ice crystal texture. The brick adobe provided by the invention can avoid adverse effects (such as pinholes, lack of decorative effects, etc.) caused by the negative pressure of the preheating zone on the adsorption of frit particles during firing. It should be noted that the high-temperature transparent glass-ceramics frit particles selected in Example 1-1 spread stably during the sintering process, forming a silver-white ice crystal texture on the green body layer, and the glas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a green brick of a monofired glass ceramic composite plate. The green brick comprises a green body layer and a glass ceramic frit layer from bottom to top, and further comprises a fixed layer arranged on the surface of the glass ceramic frit layer; the fixed layer is formed by spraying of a glass ceramic frit particle fixative; the glass ceramic frit particle fixative comprises the following components by mass percent: 6.5-7.5 percent of a nonionic polyurethane associative thickener, 3.2-4.4 percent of silica, 1-1.5 percent of a defoamer, 0.3-1.3 percent of a dispersant and the balance of a solvent. The glass ceramic frit particles of the surface of the green brick structure are not taken away by a blower at a preheating zone during firing, so that waste is avoided and the defect rate of the glass ceramic composite plate product is reduced.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a brick adobe made of a glass-ceramic composite plate fired once. Background technique [0002] Since the technology of glass-ceramic composite panel has been maturely applied, its technology has been continuously developed and innovated, and the product has become a high-grade decorative material in the market because of its transparent micro-crystalline frit particles and personalized decorative effect, and is well received by consumers. favorite. [0003] The adobe of the glass-ceramic composite board fired at one time includes a green body layer, a bottom glaze layer and a glass-ceramic layer from bottom to top. The glass-ceramic layer is generally composed of glass-ceramic frit particles. The adobe is pressed, glazed and printed. Finally, a layer of glass-ceramic frit particles will be placed on the surface of the bottom glaze layer, and then sent to the kiln...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86
Inventor 朱培祺朱丽萍刘向阳王燕玲刘仁昌
Owner 江苏鑫宝门窗制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More