Adhesive tape or sheet for application on skin

A skin and adhesive layer technology, applied in the direction of bandages, medical patches, adhesive types, etc., to achieve the effects of reducing skin irritation, high air permeability, and excellent fit

Inactive Publication Date: 2015-09-23
NITTO DENKO CORP
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is still difficult to say that the moisture permeability of the conventional skin-fitting tape or sheet has a sufficient level.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive tape or sheet for application on skin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Uniformly dissolve and mix a monomer mixture containing 30 parts of isononyl acrylate, 65 parts of 2-methoxyethyl acrylate, and 5 parts of acrylic acid in 100 parts of toluene, and add 0.2 parts of azobisisobutyronitrile as a polymerization initiator , and carry out the copolymerization reaction.

[0047] With respect to 100 parts of the obtained acrylic copolymer, 60 parts of glyceryl tricaprylate and 0.13 parts of a trifunctional isocyanate compound (trade name CORONATEHL, manufactured by Nippon Polyurethane Co., Ltd.) as a crosslinking agent were blended in toluene to produce a uniform bond. agent solution.

[0048] Next, this solution was applied on the release-treated surface of the release sheet after the release treatment so that the thickness after drying was 15 μm, and dried at 120° C. for 3 minutes to prepare an adhesive layer. Next, the prepared adhesive layer was transferred and bonded to one side of a polyether polyurethane film (thickness 15 μm), and aged...

Embodiment 2

[0050] The skin-attaching tape of the present invention was obtained in the same manner as in Example 1 except that tricaprylic acid glycerin in Example 1 was set to 45 parts.

Embodiment 3

[0052] The skin adhesive tape of this invention was obtained in the same manner as in Example 1 except having made tricaprylic acid glycerin into 30 parts in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A pressure-sensitive adhesive tape or sheet for application on skin includes a substrate and a pressure-sensitive adhesive layer laminated on at least one surface of the substrate. The pressure-sensitive adhesive layer contains: 100 parts by weight of an acrylic copolymer prepared by copolymerizing a monomer mixture comprising from 5 to 38% by weight of an alkyl (meth)acrylate monomer, from 61 to 90% by weight of an alkoxy group-containing ethylenic unsaturated monomer and from 1 to 10% by weight of a carboxyl group-containing ethylenic unsaturated monomer; and from 30 to 60 parts by weight of a carboxylic acid ester in a paste form or liquid form at room temperature. The acrylic copolymer has been subjected to a crosslinking treatment.

Description

technical field [0001] The present invention relates to a skin-adhering tape or sheet used in the field of medical care and hygiene. Background technique [0002] Since the adhesive used for the skin-attaching tape or sheet is usually required to adhere reliably to the skin surface, it is necessary to set the skin adhesive force to a certain level. However, when the skin adhesive force is set high, skin irritation may occur when peeling from the skin surface. In addition, when sticking to the skin surface for a long time, itching may occur on the skin surface, and various dermatitis may be caused depending on the situation. [0003] In addition, since the skin surface usually has an irregular and complicated structure, it is difficult for the adhesive to completely adhere to the applied skin surface. Therefore, it is considered to improve the adhesiveness by softening the adhesive. However, when the adhesive is softened, the cohesive force of the adhesive decreases. There...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/26A61L15/58A61L15/40
CPCB32B2250/24B32B2307/724B32B2405/00A61F13/02C09J2433/00C09J7/00B32B2556/00B32B2307/748B32B2535/00A61L24/06B32B2250/02B32B27/08B32B27/308C09J7/0207C08K5/10C09J133/00C09J133/08A61F13/0246A61F13/0253C09J7/385Y10T428/2891C09J2301/408C08F220/281C08F220/1809C08F220/06
Inventor 中川雅央菊田典之滨田昌志东尾和广
Owner NITTO DENKO CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com