Tyre having improved wear properties

A technology for tires and treads, which is applied to heavy tires, tire parts, reinforcement layers of pneumatic tires, etc., and can solve problems such as wear and performance degradation

Active Publication Date: 2018-08-03
MICHELIN & CO CIE GEN DES ESTAB MICHELIN
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0024] The inventors have demonstrated during experiments that the size of the concealed voids including the longitudinal and transverse cuts (both types of cuts) can be relatively small for the same application compared to a similar tire not comprising such concealed voids. ) in combination may result in reduced performance in terms of wear and irregular wear shapes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tyre having improved wear properties
  • Tyre having improved wear properties
  • Tyre having improved wear properties

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0094] exist figure 1 In , a tire 1 of size 315 / 70 R 22.5 has an aspect ratio H / S equal to 0.70, where H is the height of the tire 1 on its mounted rim and S is its maximum axial width. Said tire 1 comprises a radial carcass reinforcement 2 anchored in two beads (not shown in the figures). The carcass reinforcement is formed from a single layer of metal cords. The carcass reinforcement 2 is wrapped by a crown reinforcement 4 formed radially from the inside to the outside by:

[0095] - a first working layer 41 formed of unwrapped 9.28 non-extensible metal cords continuous over the entire width of the ply and oriented at an angle of 24°,

[0096] - a layer 42 of circumferential reinforcing elements formed of 21x23 steel metal cords of the "dual modulus" type,

[0097] - a second working layer 43 formed of unwrapped 9.28 non-extensible metal cords continuous over the entire width of the ply and oriented at an angle equal to 24° and crossing the metal cords of layer 41,

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a tyre comprising a crown reinforcement formed by at least two working crown layers (41, 43) of reinforcing elements and at least one layer (42) of circumferential reinforcingelements. According to the invention, the tread includes at least one longitudinal notch (8) and at least one transverse notch (10), the depth of said at least one longitudinal notch and said at least one transverse notch, measured on a new tyre, being greater than or equal to 40% of the thickness of the tread. The ratio of the width of said longitudinal notches measured at the base thereof to the width of same measured at the surface of the tread is strictly greater than 1.2, while the ratio of the width of said at least one transverse notch measured at the base thereof to the width of samemeasured at the surface of the tread on a new tyre is strictly greater than 1.

Description

technical field [0001] The present invention relates to tires with radial carcass reinforcement, and more particularly to tires, for example intended to equip vehicles carrying heavy loads traveling at sustained speeds, such as trucks, tractors, trailers or coaches. Background technique [0002] In heavy tyres, the carcass reinforcement is usually anchored on either side in the bead area and is radially covered by a crown reinforcement consisting of at least two superimposed layers of The layers are formed by threads or cords parallel in each layer and crossing from one layer to the next so as to form an angle with the circumferential direction of between 10° and 45°. Said working layer forming the working reinforcement may further be covered by at least one layer called protective layer formed by reinforcing elements, advantageously metallic and stretchable and called elastic Reinforcement elements. It may also comprise layers of wires or cords of low elongation at an ang...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B60C9/20B60C11/12B60C11/03B60C9/22
CPCB60C9/2006B60C2200/06B60C11/1281B60C11/0323B60C9/22
Inventor P·热尔韦斯G·戈多B·匡蒂尼特T·日夫科维奇
Owner MICHELIN & CO CIE GEN DES ESTAB MICHELIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap