A kind of chlorine-free reinforced slump-preserving cement grinding aid and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cement grinding aid and slump-preserving technology, applied in the field of cement additives, can solve problems such as poor slump-preserving performance of cement, unsustainable cement strength, and impact on building durability.
Active Publication Date: 2021-04-16
UNIV OF JINAN
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, cement grinding aids used in China are divided into two types: liquid and powder, and the effect on cement is single. The strength cannot last; the common problem at present is that in order to reduce the cost of cement production, the cement plant will give full play to the characteristics of cement clinker, the cement is ground very finely or the mixed materials of poor quality are used, resulting in poor adaptability of cement. The time loss is large, and the slump performance of cement is poor, which seriously affects its use in concrete, and most of the existing products contain chloride ions that corrode building steel bars, and have an impact on building volume stability Sulfates seriously affect the durability of buildings
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0041] The present invention also provides a preparation method of the chlorine-free enhanced cement grinding aid described in the above technical solution, comprising the following steps:
[0042] 1) Weigh raw materials: diethanol monoisopropanolamine, triethanolamine, sodium formate, organic phosphonate retarder, polymer dispersant, molasses, and the remaining water;
[0043] 2) Add the water in step 1) into the mixing tank, stir, slowly add sodium formate to dissolve it completely, and continue stirring to obtain a sodium formate solution;
[0044] 3) Add diethanol monoisopropanolamine, triethanolamine, organic phosphonate retarder, and polymer dispersant in sequence to the sodium formate solution in step 2), and stir to obtain a mixed solution;
[0045] 4) Add molasses to the mixed solution in step 3), and stir to obtain cement grinding aid.
[0046] Preferably, the stirring time of step 3) is 2 min.
[0047] Preferably, the stirring time of step 4) is 5 minutes.
Embodiment 1
[0050] Prepare cement grinding aid, its composition raw material is by weight: 5 parts of diethanol monoisopropanolamine, 8 parts of triethanolamine, 15 parts of sodium formate, 1 part of disodium hydroxyethylidene diphosphonate, 1 part of polyepoxysuccinic acid parts, molasses 2 parts, water 68 parts;.
Embodiment 2
[0052] Prepare cement grinding aid, its composition raw material is by weight: 5 parts of diethanol monoisopropanolamine, 8 parts of triethanolamine, 15 parts of sodium formate, 1 part of potassium hydroxyethylidene diphosphonate, 1 part of sodium polyepoxysuccinate 1 part, 2 parts molasses, 68 parts water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a chlorine-free reinforced slump-preserving cement grinding aid. The components include the following parts by weight: 2-8 parts of diethanol monoisopropanolamine, 6-20 parts of triethanolamine, 10-25 parts of sodium formate, 0.5-2 parts of organic phosphonate retarder, polymer dispersant 0.5 to 2 parts, 2 to 4 parts of molasses, and the rest of water. The advantages of the present invention are: diethanol monoisopropanolamine is used in conjunction with triethanolamine and sodium formate to significantly improve the early and late strength properties of cement; organic phosphonate retarders are used in combination with polymer dispersants to make Cement has excellent slump retention performance and good adaptability to concrete admixtures; in actual use, the early and late strength of cement are increased by 3-5 MPa, and the adaptability to three types of water reducers of naphthalene, aliphatic and polycarboxylic acid All are good, and the fluidity of the cement slurry will not be lost for 2 hours; and it does not contain any chloride ions and sulfate ions, non-toxic, environmentally friendly, non-corrosive, and has no damage to human bodies and buildings.
Description
technical field [0001] The invention relates to the technical field of cement additives, in particular to a chlorine-free reinforced slump-preserving cement grinding aid and a preparation method thereof. Background technique [0002] Cement production is a typical high-pollution and high-energy-consuming industry. Under the general trend of pursuing green GDP, energy conservation and emission reduction are required. As an innovative application technology product, cement grinding aid can improve cement production efficiency, reduce energy consumption, and improve Cement quality, reduce the mixing ratio of conveying materials. At present, cement grinding aids used in China are divided into two types: liquid and powder, and the effect on cement is single. The strength cannot last; the common problem at present is that in order to reduce the cost of cement production, the cement plant will give full play to the characteristics of cement clinker, the cement is ground very finel...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).