Surface treatment agent for anodic oxidation coating of dyed aluminum or aluminum alloy, surface treatment method using same, sealing treatment method, and article
A surface treatment agent and surface treatment technology, applied in the direction of surface reaction electrolytic coatings, coatings, electrolytic coatings, etc., can solve the problems of no research, no research, color fading, etc., to achieve fading inhibition, excellent dyeing fixity, The effect of excellent light fastness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1~5
[0124] Each of the anodized-dyed test pieces made using the dyes shown in Tables 1 and 2 was mixed with 0.4 g of metal oxide salt containing 1.2 g / L of ammonium fluorozirconate, 1 g / L of glycine, and 0.4 g of fluorine-free metal oxide salt. / L and adjusted to pH 2.5 with nitric acid in a surface treatment agent (bath temperature: 45° C.) for 3 minutes, followed by water washing to perform surface treatment. Next, it was immersed in a sealing treatment agent (bath temperature: 92° C.) consisting of an aqueous solution of pH 5.7 containing 40 ml / L of Okuno Pharmaceutical Co., Ltd. Top Seal H-298 for 15 minutes, washed with water, and dried.
Embodiment 6
[0126] Except that no fluorine-free metal oxide salt was added, in the same manner as in Examples 1 to 5, the anodized-dyed test piece was subjected to surface treatment, dipped in a sealing treatment agent, and washed with water. and dry.
Embodiment 7
[0128] The pH of the surface treatment solution was adjusted to 3.0, except that, in the same manner as in Examples 1 to 5, the anodized-dyed test piece was surface-treated, immersed in a sealing treatment agent, washed with water and dry.
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com