Vacuum reverse sucking technology for shaping refractory fibre products

A technology of refractory fiber and molding process, used in manufacturing tools, ceramic molding machines, etc., can solve the problems of affecting the construction and application effect of products, large fluctuation range of bulk density, poor structure of fiber interweaving, etc. Simplified, low thermal conductivity effect

CN1124192CInactive Publication Date: 2003-10-15LUYANG ENERGY SAVING MATERIALS CO LTD
0 Cites 3 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
Publication Date
2003-10-15
Estimated Expiration
Not applicable · inactive patent
Patent Text Reader

Abstract

A vacuum reverse-sucking technology for manufacturing refractory fibrous product features that the mould for manufacturing the said refractory fibrous product is turned over by 180 deg.C to make its sucking mouth deconward, the vacuum sucking region has multiple cavities and multiple segments, and the sucking net is composed of overlapped multiple layers. Its advantages include precise control of volume density, uniform fibre interleaving, high antiflex cracking strength and low thermal conductivity.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to a refractory fiber product forming process, and relates to a refractory fiber product vacuum suction forming process. It is suitable for the molding process of refractory fiber products. Background technique

[0002] When manufacturing refractory fiber products in the prior art, the vacuum forming process is usually adopted. In the negative pressure source for suction filtration-mold combination, the negative pressure source is at the bottom, with a layer of suction filter mesh in the middle, and finally a mold is used; The process is: use aluminum silicate refractory fiber as the main raw material, add a certain amount of binder to make a suspension slurry, pour it into the mold from top to bottom, and separate the solvent water through vacuum suction filtration, and the aluminum silicate refractory The fiber mixture is adsorbed in a mold of a certain shape, and after drying, felts, boards and special-shaped products of diffe...

Examples

Embodiment Construction

[0011] A vacuum reverse suction molding process for refractory fiber products, including a suction filtration process, in the negative pressure source for suction filtration - mold combination, the negative pressure source is at the bottom, a layer of suction filter mesh is lined in the middle, and a mold is used on it. The suspension slurry is poured into the mold from top to bottom, the solvent water is separated by vacuum suction filtration, the aluminum silicate refractory fiber mixture is absorbed in a mold of a certain shape, and special-shaped products of different shapes can be produced after drying. Features:

[0012] (1) The negative pressure source for suction filtration—in the mold combination, the negative pressure source for vacuum suction filtration is on the liquid surface, and the suction port of the mold is immersed in the feed liquid downward;

[0013] (2) The vacuum suction filter area is a multi-cavity multi-stage distributed arrangement, and the negative ...