Wood decorative mortar as well as preparation method and use method thereof

Abstract

The invention discloses wood decorative mortar as well as a preparation method and a use method thereof, and relates to the technical field of decoration. Comprising cement, a pigment, yellow sand, a wood dipping aggregate and water, and the weight ratio of the cement to the pigment to the yellow sand to the wood dipping aggregate to the water is 100: (2-5): 150: 30: 45. During preparation, the impregnated wood aggregate, the cement, the yellow sand and the pigment are put into a concrete mixer for dry mixing, and then water is added for mixing. During use, the wall surface and / or the ground are / is treated by adopting a cleaning or polishing method. The wood decorative mortar prepared by the preparation method disclosed by the invention comes from soil and then returns to the soil, so that the ecological environment is not influenced; the fine impregnated wood aggregate obtained after wood solid waste treatment is adopted to replace a large amount of non-renewable fine aggregate, so that a large amount of non-renewable resources are saved; carbon dioxide in air can be adsorbed, and carbon neutralization and carbon peak reaching are greatly facilitated; a chelation effect is achieved, bacteria can be killed, and the environment can be purified.

Description

Technical Field

[0001] The invention relates to the technical field of decoration, and in particular to a wooden decorative mortar and a preparation method and a use method thereof. Background Art

[0002] With the continuous prosperity and development of the world economy, the earth has gradually changed its original appearance. Urban construction is changing with each passing day and developing rapidly. A large amount of mortar materials are used in the construction of public buildings, houses and roads, which hardens the surface environment and almost completely changes the ecological environment of the construction site. The atmospheric evaporation cycle is affected, resulting in lower air humidity and higher temperatures in urban areas, forming a "heat island effect" and causing a huge impact on the ecological environment.

[0003] Therefore, those skilled in the art are committed to developing a wood decorative mortar that will not have an impact on the ecological environment. Summary of the invention

[0004] In view of the above-mentioned defects of the prior art, the technical problem to be solved by the present invention is to develop a wood decorative mortar which will not cause any impact on the ecological environment.

[0005] To achieve the above object, the present invention provides a wood decorative mortar, comprising cement, pigment, yellow sand, soaked wood aggregate and water.

[0006] In a preferred embodiment of the present invention, the weight ratio of cement, pigment, yellow sand, soaked wood aggregate and water is cement: pigment: yellow sand: soaked wood aggregate: water is 100:2-5:150:30:45.

[0007] In a preferred embodiment of the present invention, the density of the impregnated wood aggregate is 450 kg / m 3 , diameter ≤5mm.

[0008] In a preferred embodiment of the present invention, the soaked wood aggregate is prepared by the following method: processing wood solid waste into wood aggregate with a length of less than 5 mm, then soaking the wood aggregate to form the soaked wood aggregate, and finally drying and storing it.

[0009] Furthermore, the wooden aggregate is soaked in water and finally dried in the shade for storage.

[0010] The invention also discloses a preparation method of the wooden decorative mortar, which comprises the following steps: placing soaked wood aggregate, cement, yellow sand and pigment into a concrete mixer for dry mixing, and then adding water for stirring.

[0011] In a preferred embodiment of the present invention, the dry mixing time is 3 minutes and the stirring time is 2 minutes.

[0012] The invention also discloses a method for using the wooden decorative mortar, which uses a cleaning or polishing method to process the wall surface and / or the ground.

[0013] In a preferred embodiment of the present invention, the cleaning method includes the following steps: spraying water to moisten the required fraction of the wall and / or floor, and after drying in the shade, applying wood decorative mortar to the wall and / or floor, and after the wood decorative mortar has initially set, cleaning it with a water spray device, and applying a covering treatment to the wall or floor after it is completely dry.

[0014] In a preferred embodiment of the present invention, when a polishing method is used, the following steps are included: applying the wooden decorative mortar to the wall and / or the floor, waiting for it to be completely dry, polishing it with a polishing device until the impregnated wood aggregate is revealed, cleaning and maintaining it with clean water, and applying a topcoat after it is completely dry.

[0015] Compared with the prior art, the present invention has the following beneficial effects:

[0016] The wood decorative mortar prepared by the present invention comes from the soil and returns to the soil, and will not affect the ecological environment;

[0017] The present invention uses fine wood aggregates obtained after wood solid waste treatment to replace a large amount of non-renewable fine aggregates, thus saving a large amount of non-renewable resources.

[0018] The wood decorative mortar prepared by the present invention can absorb carbon dioxide in the air, which is of great help to carbon neutrality and carbon peak;

[0019] The wooden decorative mortar prepared by the invention has a chelating effect, can kill bacteria, and has the effect of purifying the environment.

[0020] The wooden decorative mortar prepared by the present invention also has certain superior properties, such as crack resistance, sound absorption, heat preservation, light weight, toughness, etc.

[0021] The concept, specific structure and technical effects of the present invention will be further described below in conjunction with the accompanying drawings to fully understand the purpose, characteristics and effects of the present invention. BRIEF DESCRIPTION OF THE DRAWINGS

[0022] Figure 1 This is the wood decorative mortar prepared in the embodiment of the present invention. DETAILED DESCRIPTION

[0023] The following describes several preferred embodiments of the present invention with reference to the drawings in the specification, so that the technical content is clearer and easier to understand. The present invention can be embodied in many different forms of embodiments, and the protection scope of the present invention is not limited to the embodiments mentioned in the text.

[0024] Example 1 Preparation of impregnated wood aggregate

[0025] The wood solid waste is processed into wood aggregates with a length less than 5 mm, and then the wood aggregates are soaked in water to form soaked wood aggregates, and finally dried in the shade for storage.

[0026] Example 2 Preparation of wood decorative mortar

[0027] The raw materials of wood decorative mortar are prepared according to the weight ratio of cement, pigment, yellow sand, soaked wood aggregate and water of 100:2:150:30:45, among which the density of soaked wood aggregate is 450kg / m 3 , diameter ≤5mm, then put the shade-dried soaked wood aggregate, cement, yellow sand and pigment into the concrete mixer for 3 minutes of dry mixing, then add water and stir for 2 minutes.

[0028] Example 3 Preparation of wood decorative mortar

[0029] The raw materials of wood decorative mortar are prepared according to the weight ratio of cement, pigment, yellow sand, soaked wood aggregate and water of 100:3:150:30:45, among which the density of soaked wood aggregate is 450kg / m 3 , diameter ≤5mm, then put the shade-dried soaked wood aggregate, cement, yellow sand and pigment into the concrete mixer for 3 minutes of dry mixing, then add water and stir for 2 minutes.

[0030] Example 4 Preparation of wood decorative mortar

[0031] The raw materials of wood decorative mortar are prepared according to the weight ratio of cement, pigment, yellow sand, soaked wood aggregate and water of 100:4:150:30:45, among which the density of soaked wood aggregate is 450kg / m 3 , diameter ≤5mm, then put the shade-dried soaked wood aggregate, cement, yellow sand and pigment into the concrete mixer for 3 minutes of dry mixing, then add water and stir for 2 minutes.

[0032] Example 5 Preparation of wood decorative mortar

[0033] The raw materials of wood decorative mortar are prepared according to the weight ratio of cement, pigment, yellow sand, soaked wood aggregate and water of 100:5:150:30:45, among which the density of soaked wood aggregate is 450kg / m 3 , diameter ≤5mm, then put the shade-dried soaked wood aggregate, cement, yellow sand and pigment into the concrete mixer for 3 minutes of dry mixing, then add water and stir for 2 minutes.

[0034] Example 6 Use of wood decorative mortar

[0035] This embodiment uses a cleaning method to treat the wall and / or floor, specifically: spray water to moisten the required fraction of the wall and / or floor, wait for it to dry in the shade, apply wooden decorative mortar to the wall and / or floor, and after the wooden decorative mortar has initially set, use a water spray device to clean it, and after the wall or floor is completely dry, apply a covering treatment to it.

[0036] Example 7 Use of wooden decorative mortar

[0037] This embodiment uses a polishing method to treat the wall and / or floor, specifically: apply wooden decorative mortar to the wall and / or floor, wait for it to be completely dry, use polishing equipment to polish it until the impregnated wood aggregate is exposed, wash and maintain it with clean water, and after it is completely dry, apply a topcoat treatment.

[0038] The preferred specific embodiments of the present invention are described in detail above. It should be understood that ordinary technicians in the field can make many modifications and changes based on the concept of the present invention without creative work. Therefore, all technical solutions that can be obtained by technicians in the technical field based on the concept of the present invention through logical analysis, reasoning or limited experiments on the basis of the prior art should be within the scope of protection determined by the claims.

Claims

1. A wood decorative mortar, characterized in that: Includes cement, pigment, yellow sand, soaked wood aggregate and water.

2. The wood decoration mortar according to claim 1, characterized in that: The weight ratio of cement, pigment, yellow sand, soaked wood aggregate and water is cement: pigment: yellow sand: soaked wood aggregate: water is 100:2-5:150:30:

45.

3. The wood decoration mortar according to claim 1, characterized in that: The density of the impregnated wood aggregate is 450kg / m 3 , diameter ≤5mm.

4. The wood decoration mortar according to claim 1, characterized in that: The soaked wood aggregate is prepared by the following method: processing wood solid waste into wood aggregate with a length less than 5 mm, then soaking the wood aggregate to form the soaked wood aggregate, and finally drying and storing it.

5. The wood decoration mortar according to claim 4, characterized in that: The wooden aggregate is soaked in water and finally dried in the shade for storage.

6. The method for preparing the wood decorative mortar according to any one of claims 1 to 5, characterized in that: The method comprises the following steps: putting soaked wood aggregate, cement, yellow sand and pigment into a concrete mixer for dry mixing, and then adding water for stirring.

7. The method for preparing wood decorative mortar according to claim 6, characterized in that: The dry mixing time is 3 minutes and the stirring time is 2 minutes.

8. The method for using the wood decoration mortar according to any one of claims 1 to 5, characterized in that: Prepare walls and / or floors by cleaning or polishing.

9. The method of use according to claim 8, characterized in that: When the cleaning method is adopted, the following steps are included: spraying water to moisten the required fraction of the wall and / or floor, and after drying in the shade, applying the wood decorative mortar to the wall and / or floor, and after the wood decorative mortar has initially set, cleaning it with a water spray device, and applying a covering treatment to the wall or floor after it is completely dry.

10. The method of use according to claim 8, characterized in that: When the polishing method is adopted, the following steps are included: applying the wooden decorative mortar to the wall and / or the floor, waiting for it to be completely dry, polishing it with polishing equipment until the impregnated wood aggregate is exposed, cleaning and maintaining it with clean water, and applying a topcoat after it is completely dry.