Mothproof and fireproof plasterboard with glass fiber surface and manufacturing method thereof

A technology of gypsum board and glass fiber surface, which is applied in the field of architectural decorative boards, can solve the problems of the board's flexural strength drop, and achieve the effect of simple shape, light weight and good fire resistance

Active Publication Date: 2009-09-16
SHANDONG BAIER BUILDING MATERIAL CO LTD
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the flexural strength of this paper-faced gypsum board comes from the strength of the prote

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mothproof and fireproof plasterboard with glass fiber surface and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1; as figure 1 As shown, a moth-proof and fireproof glass fiber surface gypsum board includes an intermediate base 2 made of gypsum cementitious material, and a glass fiber surface formed by glass fiber mesh cloth woven with glass fibers on the outside of the intermediate base 2 2.

Embodiment 2

[0025] Embodiment 2; A kind of preparation method of mothproof, fireproof glass fiber gypsum board comprises the following steps: step 1, to a kind of mothproof, fireproof glass fiber gypsum board batching, the content of each composition is respectively weight ( number of copies):

[0026] Hemihydrate gypsum powder 1000 parts

[0027] Adhesive 30 parts

[0028] 20 parts glass fiber

[0029] Glass fiber mesh cloth 75 parts

[0030] 730 parts of water;

[0031] The above-mentioned hemihydrate gypsum powder is one or more mixtures of 80 mesh hemihydrate gypsum powder, 120 mesh hemihydrate gypsum powder or 160 mesh hemihydrate gypsum powder;

[0032] The above glass fiber length is 300mm;

[0033] Glass fiber mesh cloth with a specification of 2mm×2mm;

[0034] Above-mentioned sizing agent is cornstarch;

[0035] Step 2, batching according to the above weight percentage; add water and stir and mix according to the conventional process;

[0036] Step 3, forming;

[0037] ...

Embodiment 3

[0040] Embodiment 3; A kind of preparation method of moth-proof, fireproof glass fiber gypsum board comprises the following steps: step 1, to a kind of moth-proof, fireproof glass fiber gypsum board batching, the content of each component is respectively weight ( number of copies):

[0041] Hemihydrate gypsum powder 1000 parts

[0042] Adhesive 35 parts

[0043] 45 parts glass fiber

[0044] Fiberglass mesh 90 parts

[0045] 850 parts of water;

[0046] The above-mentioned hemihydrate gypsum powder is one or more mixtures of 100 mesh hemihydrate gypsum powder, 120 mesh hemihydrate gypsum powder or 160 mesh hemihydrate gypsum powder;

[0047] The above glass fiber length is 800mm;

[0048] Glass fiber mesh cloth with a specification of 3mm×2mm;

[0049] Above-mentioned sizing agent is cornstarch;

[0050] Step 2, batching according to the above weight percentage; add water and stir and mix according to the conventional process;

[0051] Step 3, molding;

[0052] Step 4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a mothproof and fireproof plasterboard with glass fiber surface and a manufacturing method thereof. The plasterboard comprises an intermediate basal layer composed of gypsum plaster; the outside of the intermediate basal layer is coated by glass fiber net to form a glass fiber surface; the contents of the components are respectively arranged through parts by weight in batching: 1000 parts of hemihydrate gypsum powder; 30-35 parts of adhesive; 20-45 parts of glass fiber; 75-90 parts of glass fiber mesh and 730-850 parts of water; the plasterboard of the invention features in improving strength of board material, strengthening ornament effect and easy application of basal layer paint; what is more, the plasterboard is effectively mothproof and more fireproof than the thistle board, belongs to A-level incombustible material and has better water resistance, thus being widely applied in fields such as architecture and decoration.

Description

technical field [0001] The invention relates to a building decoration board that can be used in the fields of construction and decoration, in particular to a mothproof and fireproof glass fiber-faced gypsum board and a preparation method thereof. Background technique [0002] At present, all sectors of society have higher and higher requirements for interior decoration. Users pay more and more attention to the performance of fire prevention, waterproof, and deformation resistance in terms of ceilings and partition walls. new material. A kind of decorative plate that is widely used now is plasterboard, the substrate of the plate is gypsum cementitious material, and the protective layer is paper. Most of the flexural strength of this paper-faced gypsum board comes from the strength of the protective paper. When the protective paper is damp, the flexural strength of the board will drop sharply. Moreover, the protective paper is flammable. In terms of non-combustibility, the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E04F13/075C04B28/14C04B14/42C04B24/38C04B103/44
CPCC04B2111/28C04B41/5022C04B2111/27C04B41/009C04B2111/00612C04B28/14
Inventor 孙小力
Owner SHANDONG BAIER BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap