Colored coating
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A color coating, weight percentage technology, applied in multi-color effect coatings, anti-corrosion coatings, coatings, etc., can solve problems such as excessive heating
Inactive Publication Date: 2014-04-02
TIANCHANG CITY TONGTIAN CHEM
View PDF3 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] Another object of the present invention is to provide a kind of thermal insulation coating, which can effectively solve the problem that the factory heats up too fast in summer and cools down too fast in winter, saves energy, improves the comfort of the factory, and is beneficial to production;
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] Polymer emulsion of styrene-acrylic acid-maleic anhydride copolymer 50%,
[0020] Flake aluminum powder 10%,
[0021] Nano calcium carbonate 5%,
[0022] Phase Change Paraffin Microcapsules 15%
[0023] Nano Iron Oxide 6%,
[0024] Dispersant 2%,
[0025] The balance is water.
Embodiment 2
[0027] Polymer emulsion of styrene-acrylic acid-maleic anhydride copolymer 45%,
[0028] Flake aluminum powder 15%,
[0029] Nano Calcium Carbonate 7%,
[0030] Phase change paraffin microcapsules 13%
[0031] Nano Iron Oxide 8%,
[0032] Dispersant 1%,
[0033] The balance is water.
[0034] When the above-mentioned paint is applied to the factory building, compared with the general factory paint, the temperature in the factory is reduced by 3-5 degrees Celsius, no corrosion is found on the steel components of the factory building, and the coating integrity is good.
[0035] The coating of the present invention has outstanding anti-corrosion performance, and also has temperature control performance, especially the combination of nano-iron oxide and emulsion improves the above performance, which is higher than any single function, and has a wide application prospect.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a colored coating, which consists of the following components in percentage by weight: 40-50 percent of polymer emulsion of a styrene-acrylic acid-maleic anhydride copolymer, 5-8 percent of calcium carbonate, 10-15 percent of phase change paraffin microcapsules, 6-8 percent of nanometer ferric oxide, 1-2 percent of dispersing agent, 10-20 percent of flake aluminum powder and the balance of water. The colored coating has low cost, and can be applied to different places.
Description
technical field [0001] The present invention relates to a kind of color paint, especially relates to the paint of anti-corrosion, corrosion resistance and certain temperature resistance, more especially the application in the plant structure of iron parts. Background technique [0002] With the development of the national economy and high technology, the demand for special coatings is increasingly urgent in addition to general-purpose coatings. Among anti-corrosion coatings, peroxide ethylene coatings, epoxy resin coatings, and oxysulfonated polyethylene coatings all exist concurrently, but each has its own shortcomings. Ethylene peroxide paint came out in the early 1970s. This kind of paint has a certain anti-corrosion effect, but due to the large molecular weight, the leveling property is not ideal, the solid content is low, generally only 14-18%, the paint film density is poor, and the viscosity is also very high. Low, only 20-50 seconds, its adhesion is not good, and th...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More