Medium plate made of duplex stainless steel with excellent low-temperature toughness and manufacturing method for medium plate

A technology of duplex stainless steel and low-temperature toughness, which is applied in the field of duplex stainless steel and its manufacturing, can solve the problems of toughness (impact value drop, etc.), achieve the effect of increasing N solubility, reducing adverse effects, and improving corrosion resistance

Inactive Publication Date: 2012-08-29
BAOSHAN IRON & STEEL CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the Ni content in the alloy is below 1.7%, its toughness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medium plate made of duplex stainless steel with excellent low-temperature toughness and manufacturing method for medium plate
  • Medium plate made of duplex stainless steel with excellent low-temperature toughness and manufacturing method for medium plate
  • Medium plate made of duplex stainless steel with excellent low-temperature toughness and manufacturing method for medium plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The metallographic diagram of the alloy of embodiment 1 along the rolling direction (also known as the longitudinal direction) is as follows figure 1 As shown (the austenite phase accounts for about 58%), the alloy metallographic diagram of the alloy in Example 1 perpendicular to the rolling direction (also known as the transverse direction) is as follows figure 2 As shown, the metallographic diagram of the alloy of Comparative Example 2 along the rolling direction is as follows image 3 shown. Table 1 also shows the mechanical properties and corrosion resistance of the steel of the present invention and the comparative steel types, especially the impact toughness at -40°C and -80°C. Among them, the metallographic sample of duplex stainless steel is electrolytically corroded, and the etchant is 40gKOH+100mlH 2 O, corrosion current 0.3~0.8A / cm 2 The mechanical properties are all taken from the hot-rolled annealed sheet, and the impact properties are in accordance wit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a medium plate made of duplex stainless steel with excellent low-temperature toughness and a manufacturing method for the medium plate. The duplex stainless steel comprises the following chemical components in weight percentage: 0.01-0.10 percent of C, 0.2-1.0 percent of Si, 2.0-3.5 percent of Mn, 20.0-21.5 percent of Cr, 3.0-3.5 percent of Ni, 0.08-0.15 percent of N, 0.5-1.0 percent of W, 0.01-0.5 percent of Cu, 0.001-0.005 percent of B, 0.05-0.25 percent of V and the balance Fe and unavoidable impurities. The stainless steel is proper in phase proportion and excellent in low-temperature toughness through controlling component proportion. Meanwhile, the length-width ratio of the austenite phase of the stainless steel along the rolling direction is enabled to be less than 3 through a special rolling process, and thus, the stainless steel is prevented from being excessively lengthened along the rolling direction. The duplex stainless steel is excellent in low-temperature toughness along the longitudinal direction and the lateral direction. The longitudinal impact value and the lateral impact value are greater than 220J at the temperature of -40 DEG C, and the longitudinal impact value and the lateral impact value are greater than 200J at the temperature of -80 DEG C. The duplex stainless steel can be widely applied to the field of coasting buildings and petrochemical engineering under the cold condition.

Description

technical field [0001] The invention relates to a duplex stainless steel and a manufacturing method thereof, in particular to a duplex stainless steel with excellent low-temperature toughness and a manufacturing method thereof. Background technique [0002] Duplex stainless steel is composed of ferrite and austenite, and the proportion of each phase is not less than 30%. Due to the characteristics of the two-phase structure, duplex stainless steel has the advantages of both ferritic stainless steel and austenitic stainless steel. Compared with ferritic stainless steel, it has high toughness, low brittle transition temperature, intergranular corrosion resistance and good welding performance. At the same time, the advantages of high thermal conductivity and small expansion coefficient of ferritic steel are retained. Compared with austenitic stainless steel, its yield strength is significantly improved, and its resistance to chloride stress corrosion cracking is significantly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/58C21D8/02
Inventor 江来珠张伟宋红梅王治宇胡锦程
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap