Nano-modified water-based weather-resistant sound isolation adhesive and preparation method thereof

A nano-modification and manufacturing method technology, applied in the direction of adhesive types, ester copolymer adhesives, etc., can solve the problems of uneven actual performance, limited sound insulation effect, complex process, etc., achieve high use value, improve Sound insulation effect, the effect of broad application prospects

Inactive Publication Date: 2015-04-01
南京创宁空间新材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Soft elastic materials such as rubber, sound insulation felt, etc. need to bond the structural layer multiple times, and the process is slightly complicated. The damping value provided by this type of material is tanδ<0.3, and the sound insulation effect is limited and decreases with the aging of the material; high viscoelasticity The effect of molecular polymer as a damping layer is outstanding, but due to technical and process reasons, many such products on the market have different performances in sound insulation, humidity, temperature, aging and other factors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano-modified water-based weather-resistant sound isolation adhesive and preparation method thereof
  • Nano-modified water-based weather-resistant sound isolation adhesive and preparation method thereof
  • Nano-modified water-based weather-resistant sound isolation adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Ingredients as follows:

[0048]

[0049] The formulation amounts of the above formulation components are calculated in parts by mass, and the parts by mass specifically refer to the reference quantities calculated by weight of each component under the same unit of measurement, the same below.

[0050] The preparation process is as follows:

[0051] 1) Mix and stir the acrylate polymer emulsion and the silicone-modified acrylate copolymer emulsion according to the specified number of parts, and add all the tackifier emulsion, 50% dispersant, 50% wetting agent, and all bactericides at the beginning of stirring, 50% defoamer. Stir and blend for 20-40 minutes to prepare blended emulsion C.

[0052] 2) Put all the water into an empty mixing container, add the remaining dispersant, wetting agent and defoamer at the beginning of stirring at 100-300r / min, stir for about 10 minutes and start to sift in the formula filler at a uniform speed, Disperse at high speed for 40-6...

Embodiment 2

[0057] Ingredients as follows:

[0058]

[0059]

[0060] The preparation process is the same as in Example 1.

[0061] According to the GB / T 18258-2000 standard test, the nano-modified water-based weather-resistant sound-insulating adhesive obtained in this example has a damping platform with a damping value greater than 0.9 in the temperature range of -5°C to 115°C.

[0062] According to the standard test of GB / T 2791-1995, the arithmetic mean value of the peel strength of the nano-modified water-based weather-resistant sound-insulating adhesive obtained in this example is σT=4.7KN / m.

Embodiment 3

[0064] Ingredients as follows:

[0065]

[0066] The preparation process is the same as in Example 1.

[0067] According to the GB / T 18258-2000 standard test, the nano-modified water-based weather-resistant sound-insulating adhesive obtained in this example has a damping platform with a damping value greater than 0.9 in the temperature range of 5°C to 135°C.

[0068] According to the standard test of GB / T 2791-1995, the arithmetic mean value of the peel strength of the nano-modified water-based weather-resistant sound-insulating adhesive obtained in this example is σT=3.6KN / m.

[0069] The acrylate polymer emulsion and silicone-modified acrylate copolymer emulsion in the formula components are characterized in that at least one of the emulsions is an acrylate emulsion with a LIPN interpenetrating network type core-shell structure, and at least one of them is an acrylic emulsion that has undergone Silicone modified acrylic polymer emulsion. Among them, preferably, the acry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano-modified water-based weather-resistant sound isolation adhesive. The nano-modified water-based weather-resistant sound isolation adhesive consists of an acrylate polymer emulsion, an organic silicone modified acrylate copolymer emulsion, a tackifier emulsion, a filler, water, a dispersing agent, a wetting agent, nano-powder aqueous dispersion, a sterilizing agent, a PH value regulating agent, a de-foaming agent and a thickening agent. A preparation method of the nano-modified water-based weather-resistant sound isolation adhesive comprises the steps of emulsion polymerization, emulsion blending, filler slurry preparation, mixture nano-modification and finished product synthesis. The nano-modified water-based weather-resistant sound isolation adhesive has the advantages of wide temperature range, wide frequency, high damping platform, high peeling strength, energy conservation, environment friendliness and light weight; the cost is saved, the construction difficulty is lowered, and the effective space utilization rate is greatly improved. Due to modification of a nano material, the nano-modified water-based weather-resistant sound isolation adhesive is wide in temperature range, good in moisture protection, resistant to heat, light, salt spray and the like, good in ageing resistance, wide in using environment range, high in sound isolation efficiency and high in using value. The sound isolation adhesive is aqueous, has environment-friendly and pollution-free effects, and belongs to novel energy-saving and environment-friendly high molecular materials.

Description

technical field [0001] The invention belongs to the field of sound-insulating glue, in particular to a water-based weather-resistant sound-insulating glue and a manufacturing method thereof. Background technique [0002] Noise pollution has become one of the world's three major pollutions alongside air pollution and water pollution. Especially in some construction fields, traffic fields, industrial production fields, entertainment places and other noise pollution is particularly serious. The sound insulation problem seriously affects people's health, study, work and life, and is generally valued by people. Sound insulation and noise reduction often have to solve two types of problems, one is to prevent noise sources from interfering with the external environment; the other is to prevent external noise from interfering with the internal space. The traditional sound insulation and noise reduction methods are divided into three types in terms of treatment methods: noise source...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/04C09J133/08C09J133/14C09J133/10C08F220/18C08F220/28C08F2/30C08F2/26
Inventor 王盛常春红
Owner 南京创宁空间新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com