Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A sole material and anti-aging technology, which is applied in the field of anti-aging and antibacterial sole materials, can solve the problems of insufficient durability of antibacterial, sole elasticity, and uncomfortable hardness, etc., and achieve the effect of moderate hardness
Inactive Publication Date: 2015-01-07
常熟市任阳工艺鞋厂(普通合伙)
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The elasticity and hardness of the soles made of existing sole materials are not very comfortable, and the antibacterial is not durable enough, which needs to be improved
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0052] The anti-aging and antibacterial shoe sole material consists of the following components by weight:
[0053] 7 parts fatty acid methyl ester sulfonate,
[0054] 7 parts dicumyl peroxide,
[0055] 3 parts diethylene glycol,
[0056] 5 parts white carbon black,
[0057] 7 parts isoprene rubber,
[0058] 9 parts SBR,
[0059] 2 parts thiosulfate,
[0060] 2 parts aniline,
[0061] 3 parts aluminate,
[0062] 6 parts of vinyltrimethoxysilane.
Embodiment 2
[0064] The anti-aging and antibacterial shoe sole material consists of the following components by weight:
[0065] 6 parts fatty acid methyl ester sulfonate,
[0066] 6 parts dicumyl peroxide,
[0067] 2 parts diethylene glycol,
[0068] 4 parts white carbon black,
[0069] 6 parts isoprene rubber,
[0070] 8 parts SBR,
[0071] 1 part thiosulfate,
[0072] 1 part aniline,
[0073] 2 parts aluminate,
[0074] 5 parts vinyltrimethoxysilane.
Embodiment 3
[0076] The anti-aging and antibacterial shoe sole material consists of the following components by weight:
[0077] 6.7 parts fatty acid methyl ester sulfonate,
[0078] 6.7 parts dicumyl peroxide,
[0079] 2.3 parts diethylene glycol,
[0080] 4.5 parts white carbon black,
[0081] 6.7 parts isoprene rubber,
[0082] 8.9 parts of styrene-butadiene rubber,
[0083] 1.2 parts of thiosulfate,
[0084] 1.2 parts of aniline,
[0085] 2.3 parts aluminate,
[0086] 5.6 parts of vinyltrimethoxysilane.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an aging-resistant antibacterial shoe sole material which comprises the following components in parts by weight: 6-7 parts of fatty acid methyl ester sulfonate, 6-7 parts of dicumyl peroxide, 2-3 parts of diethylene glycol, 4-5 parts of white carbon black, 6-7 parts of isoprene rubber, 8-9 parts of butadiene-styrene rubber, 1-2 parts of thiosulfate, 1-2 parts of phenylamine, 2-3 parts of aluminic acid ester, 5-6 parts of vinyl trimethoxy silane. The shoe sole material prepared from the components is relatively moderate in elasticity and hardness and is effective and lasting in bacterial resistance and aging resistance.
Description
technical field [0001] The invention relates to an aging-resistant and antibacterial shoe sole material. Background technique [0002] The elasticity and hardness of the soles made of existing sole materials are not very comfortable, and the antibacterial is not durable enough, which needs to be improved. Contents of the invention [0003] The object of the present invention is to provide an aging-resistant and antibacterial shoe sole material. The shoe sole prepared by using the material has relatively moderate elasticity and hardness, and has effective and durable antibacterial and antiaging properties. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of anti-aging antibacterial shoe sole material, which consists of the following components in parts by weight: [0005] 6-7 parts of fatty acid methyl ester sulfonate, [0006] 6-7 parts of dicumyl peroxide, [0007] 2 to 3 parts of diethylene glycol, [...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more