A polyvinyl chloride rubber and composition technology, applied in the rubber field, can solve the problems of collapsed rubber hose, reduced rubber strength and other mechanical properties, blocked pipelines, etc., and achieves stable volume change, improved safety and service life, and oil resistance. good effect

Active Publication Date: 2016-06-08
TIANJIN PENGYI GRP CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the automobile industry, machinery manufacturing, oil exploration, oil refining and other industrial production, it is necessary to use rubber hoses in the transmission process of gasoline, fuel oil, lubricating oil, hydraulic oil, etc. However, rubber hoses produced according to standard processes exist Lack of oil resistance
If the rubber hose is soaked in oil medium for a long time during use, the oil can penetrate into the inside of the hose to cause swelling, resulting in a decrease in the strength and other mechanical properties of the rubber, causing the hose to collapse and block the pipeline

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A 120 ℃ aging butady/polyvinyl chloride rubber composition
  • A 120 ℃ aging butady/polyvinyl chloride rubber composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0013] In parts by mass

[0014] components

Example 1

Example 2

Example 3

Example 4

Example 5

Nitrile / PVC Rubber

100

100

100

100

100

quick press carbon black

50

55

56

60

58

Ether ester ADB-30

8

10

10

14

8

Polyadipate

8

8

10

6

10

Zinc oxide

5

5

5

5

5

Antiager B

1.0

1.0

1.0

1.0

1.0

Antiager D

0.7

0.7

0.7

0.7

0.7

Antiager E

2.0

2.0

2.0

2.0

2.0

Antiager H

2.0

2.0

2.0

2.0

2.0

Dimorpholine disulfide

2.5

3.0

3.5

3.0

3.0

dibenzothiazole disulfide

1.5

2.0

1.5

2.0

2.0

total

180.7

188.7

191.7

195.7

191.7

[0015] The nitrile / polyvinyl chloride rubber is domestically produced 41% to 43% nitrile / polyvinyl chloride rubber with medium and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention develops a 120-DEG C aging-resistant nitrile / polyvinyl chloride rubber composition which mainly comprises nitrile / polyvinyl chloride rubber, ester ether ADB-30, polyester adipate and fast extruding carbon black; through the development of a formula and the preparation of a rubber tube, the fuel B and 93# gasoline resistance, the excellent elongation at break resisting a high temperature of 120 DEG C for above 500 hours and heat aging performance of a surplus and the performance of no crack at a low temperature of below 30 DEG C below zero required in product standards are better solved; the 120-DEG C aging-resistant nitrile / polyvinyl chloride rubber composition has greater advantages in aspects of cost and performance in comparison with imported sizing material; meanwhile, the high-temperature long-time aging resistance, the low-temperature performance and the user value of the rubber are also improved; the 120-DEG C aging-resistant nitrile / polyvinyl chloride rubber composition has important significance in better playing roles of a nitrile / polyvinyl chloride rubber material and a product thereof in the auto industry and other fields, the safety guarantee of the product is improved, and the service life of the product is prolonged.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to an oil-resistant rubber hose, a nitrile / polyvinyl chloride rubber composition resistant to 120°C aging and long life cycle. Background technique [0002] In the automobile industry, machinery manufacturing, oil exploration, oil refining and other industrial production, it is necessary to use rubber hoses in the process of oil transmission such as gasoline, fuel oil, lubricating oil, hydraulic oil, etc. However, rubber hoses produced according to standard processes exist Insufficient oil resistance. If the rubber hose is soaked in oil medium for a long time during use, the oil can penetrate into the inside of the hose to cause swelling, resulting in a decrease in the strength and other mechanical properties of the rubber, causing the hose to collapse and block the pipeline. [0003] Nitrile / polyvinyl chloride rubber is a high molecular elastomer obtained by mechanically blending n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L9/02C08L27/06C08K13/02C08K3/04C08K3/22C08K5/10
CPCC08L9/02C08L27/06C08L2201/08C08L2203/18C08L2205/03C08L67/02C08K13/02C08K3/04C08K5/10C08K2003/2296C08K5/378C08K5/47
Inventor 张洪起侯波薛俊芳
Owner TIANJIN PENGYI GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap