High service strength enameled steel plate and preparation method thereof

A manufacturing method and technology for steel plates, applied to the steel plate for enamel and its manufacturing field, can solve the problems of lack of steel plates for enamel, low yield strength, etc., and achieve the effects of high strength level, reduced wear, and good anti-scalding performance.

Active Publication Date: 2019-01-15
SHOUGANG CORPORATION +1
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the yield strength of the thick hot-rolled steel plate used for the lower layer of the domestic assembled tank is not high, generally lower than 300MPa, which is only sui

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High service strength enameled steel plate and preparation method thereof
  • High service strength enameled steel plate and preparation method thereof
  • High service strength enameled steel plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0041] Example 1

[0042] A steel plate for enamel with high strength after enamelling, its chemical composition is shown in Table 1 by weight percentage, and its thickness is 11mm.

[0043] The preparation method of above-mentioned steel plate for enamel, comprises the steps:

[0044] Step 1, the molten iron is subjected to pretreatment, converter steelmaking and refining to obtain molten iron with the composition ratio of the steel plate for enamel, wherein the chemical composition of the steel plate for enamel is shown in Table 1 by weight percentage;

[0045] Step 2, continuous casting: the refined molten iron is continuously casted to obtain a billet;

[0046]Step 3, heating the billet: the temperature of the billet is controlled to be 1220°C by heating;

[0047] Step 4, two-stage hot rolling: 6 passes of rough rolling are performed first, followed by 7 passes of finishing rolling, and the final rolling temperature is 860°C;

[0048] Step 5, coiling: the finish-rolled ...

Example Embodiment

[0056] Example 2

[0057] A steel plate for enamel with high strength after enamelling, its chemical composition is shown in Table 1 by weight percentage, and its thickness is 13mm.

[0058] The preparation method of above-mentioned steel plate for enamel, comprises the steps:

[0059] Step 1, the molten iron is subjected to pretreatment, converter steelmaking and refining to obtain molten iron with the composition ratio of the steel plate for enamel, wherein the chemical composition of the steel plate for enamel is shown in Table 1 by weight percentage;

[0060] Step 2, continuous casting: the refined molten iron is continuously casted to obtain a billet;

[0061] Step 3, heating the billet: the temperature of the billet is controlled to be 1230°C by heating;

[0062] Step 4, two-stage hot rolling: 6 passes of rough rolling are performed first, followed by 7 passes of finishing rolling, and the final rolling temperature is 840°C;

[0063] Step 5, coiling: the finish-rolled...

Example Embodiment

[0071] Example 3

[0072] A steel plate for enamel with high strength after enamelling, its chemical composition is shown in Table 1 by weight percentage, and its thickness is 14mm.

[0073] The preparation method of above-mentioned steel plate for enamel, comprises the steps:

[0074] Step 1, the molten iron is subjected to pretreatment, converter steelmaking and refining to obtain molten iron with the composition ratio of the steel plate for enamel, wherein the chemical composition of the steel plate for enamel is shown in Table 1 by weight percentage;

[0075] Step 2, continuous casting: the refined molten iron is continuously casted to obtain a billet;

[0076] Step 3, heating the billet: the temperature of the billet is controlled to be 1210°C by heating;

[0077] Step 4, two-stage hot rolling: 6 passes of rough rolling are performed first, followed by 7 passes of finishing rolling, and the final rolling temperature is 840°C;

[0078] Step 5, coiling: the finish-rolled...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Average grain sizeaaaaaaaaaa
Sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high service strength enameled steel plate and a preparation method thereof. The steel plate is prepared from the following chemical components in percent by weight: 0.1-0.15% of C, 0.3-0.5% of Si, 1-1.8% of Mn, less than 0.013% of P, less than 0.005% of S, 0.020-0.050% of Alt, 0.04-0.07% of V, 0.011-0.015% of N and the balance ferrum and impurities. The preparation method comprises the following steps: 1) carrying out pre-treatment, converter steelmaking and refining on molten iron to obtain casting blank molten iron; 2) continuously casting the molten iron to prepare a casting blank; 3) heating the casting blank; 4) carrying out multi-pass rough rolling and finish rolling to obtain a finish rolled plate; and 5) carrying out laminar cooling to coil to obtain a finished product. The yield strength of the steel plate is 460-550 MPa, the yield strength of the enameled steel plate is 400-460 MPa, and the enameled steel plate can be used for manufacturing a lowertank wall of an enameled spliced tank, the moisture storage capacity of which is greater than 9000 m<3>.

Description

technical field [0001] The invention relates to a steel plate for enamelling and a manufacturing method thereof, in particular to a steel plate for enameling with high service strength and a manufacturing method thereof. Background technique [0002] Nowadays, some large-scale water treatment facilities, such as water storage tanks and sewage treatment tanks, all use enamel assembled tanks. The main components of enamel assembled tanks are enamel steel plates, which are made of enamel-coated and enamelled hot-rolled steel plates for enamel. Because the water pressure on the lower layer of the tank body is greater than that of the upper layer, the lower layer of the tank body is generally made of thick-gauge steel plates, while the upper layer is made of thin-gauge steel plates. The yield strength of the steel plate after enamelling is the service strength of the steel plate. The larger the water storage capacity of the tank body and the lower the position of the tank body, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/12C21D8/02
CPCC21D8/0226C21D2211/002C21D2211/004C21D2211/005C21D2211/009C22C38/02C22C38/04C22C38/06C22C38/12
Inventor 张志敏潘辉李晓林黄学启肖宝亮崔阳陈斌李飞程政张鹤松邱婉凌张镇高智慧安瑞东徐永先金钊
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap