A Method for Reinforcing Wood Flour/Polyolefin Composites Using Surface-Treated Continuous Aramid Fibers

A technology of aramid fibers and composite materials, which is applied in the field of reinforced wood powder/polyolefin composite materials, can solve the problems of high cost, poor bonding strength of fibers and wood-plastic matrix interfaces, and affecting the strength of the surface structure of aramid fibers, and achieves Improve the interface bonding strength and improve the effect of surface polarity

Active Publication Date: 2021-09-28
NORTHEAST FORESTRY UNIVERSITY
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problem that the existing fiber-reinforced wood-plastic composite material has a poor bonding strength between the fiber and the wood-plastic matrix interface, but the existing fiber modification method is expensive, or may affect the surface structure of the aramid fiber and thus The problem of reducing its own strength provides a method for reinforcing wood flour / polyolefin composites with surface-treated continuous aramid fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Method for Reinforcing Wood Flour/Polyolefin Composites Using Surface-Treated Continuous Aramid Fibers
  • A Method for Reinforcing Wood Flour/Polyolefin Composites Using Surface-Treated Continuous Aramid Fibers
  • A Method for Reinforcing Wood Flour/Polyolefin Composites Using Surface-Treated Continuous Aramid Fibers

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0033] Specific embodiment one: a kind of method utilizing the continuous aramid fiber of surface treatment in this embodiment to strengthen wood powder / polyolefin composite material, it carries out according to the following steps:

[0034] 1. Pretreatment:

[0035] washing the continuous aramid fiber bundle with a solvent to remove surface impurities, and then drying to constant weight to obtain the pretreated continuous aramid fiber bundle;

[0036] 2. Continuous aramid fiber bundles coated with dopamine:

[0037] Adjust the pH of the Tris-HCl buffer solution to 8-9 to obtain a Tris-HCl buffer solution after adjusting the pH, then add dopamine hydrochloride to the Tris-HCl buffer solution after adjusting the pH to obtain a dopamine hydrochloride solution. The continuous aramid fiber bundle is immersed in the dopamine hydrochloride solution, soaked at room temperature for 2 hours to 48 hours, taken out after dipping, washed and dried, and the continuous aramid fiber bundle ...

specific Embodiment approach 2

[0049] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is that the continuous aramid fiber bundle described in step 1 is 1000D continuous aramid fiber bundle, wherein D is the linear density unit, referring to the length of the 9000m long fiber bundle Mass, in g. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0050] Embodiment 3: This embodiment is different from Embodiment 1 or Embodiment 2 in that: a continuous aramid fiber bundle consists of 666 single fibers. Others are the same as those in the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for reinforcing wood powder / polyolefin composite material with surface-treated continuous aramid fibers, which relates to a method for reinforcing wood powder / polyolefin composite material. The purpose of the present invention is to solve the problem that the existing fiber-reinforced wood-plastic composite materials have poor bonding strength between the fiber and the wood-plastic matrix interface, but the existing fiber modification method is expensive and may affect the surface structure of the aramid fiber to reduce its A question of self-strength. Preparation method: 1. pretreatment; 2. dopamine-coated continuous aramid fiber bundle; 3. dopamine-VTES synergistic treatment of continuous aramid fiber bundle; 4. preparation of continuous aramid fiber reinforced wood flour / polyolefin composite material. The invention relates to a continuous aramid fiber reinforced wood powder / polyolefin composite material for surface treatment.

Description

technical field [0001] The invention relates to a method for strengthening wood flour / polyolefin composite materials. Background technique [0002] Wood-plastic composites (WPCs) are high-value-added composite materials composed of thermoplastics as the matrix and wood fibers as the reinforcing phase. Due to its environmental friendliness, adjustability, and easy processing, it is widely used in interior decoration, infrastructure, building materials and other fields. In the actual production of WPCs, coupling agents / compatibilizers (maleic anhydride grafted polyolefins, silane coupling agents, etc.) are often added to improve the interfacial bonding between non-polar plastic matrix and polar wood fibers. The prepared WPCs have effectively improved mechanical properties due to the enhanced stress transfer efficiency. Nevertheless, due to the limited strength of the plastic matrix itself and the high addition of wood fiber, traditional WPCs are still difficult to apply to s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L97/02C08L23/06C08L51/06C08L77/10C08K5/098C08J5/06
CPCC08J5/06C08J2397/02C08J2423/06C08J2451/06C08J2477/10C08K5/098
Inventor 王海刚栗越谢延军刘婉玉王伟宏肖泽芳王永贵
Owner NORTHEAST FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap