A method for removing carbon from gasification slag

A gasification slag and slurry technology, applied in chemical instruments and methods, solid separation, electrostatic effect separation, etc., can solve the problems of increased cost, secondary pollution, etc., and achieve low cost, rapid carbon removal, and good carbon removal effect Effect

Active Publication Date: 2022-04-26
HUBEI UNIV OF TECH
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process of the invention is simple, and can better realize the secondary recycling of coal gasification slag solid waste, but the use of activators, collectors, and foaming agents will increase costs and cause secondary pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for removing carbon from gasification slag
  • A method for removing carbon from gasification slag

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Example 1 is used to illustrate the method for removing carbon from gasification slag according to the present invention.

[0045] The method for removing carbon by wet grinding and gasification slag in this embodiment comprises the following steps in sequence:

[0046] (1) Take 70 parts of gasification slag and add 30 parts of water, mix and stir to prepare slurry A with a solid content of 70%;

[0047] (2) Take 100 parts by mass of slurry A, add grinding media, place it in a stirring wet mill and wet grind until the particle size is 5 μm, sieve and take out the grinding medium to obtain slurry B;

[0048] In step (2), the following wet grinding process parameters are adopted:

[0049] The grinding medium is zirconia grinding balls with a particle size of 0.5-3.0mm. The filling rate of the grinding medium is 70%, the weight ratio of the ball to material is 1:4, and the stirring shaft speed of the wet mill is 400r / min. The grinding time is 60min.

[0050] (3) Put the...

Embodiment 2

[0055] Example 2 is used to illustrate the method for removing carbon from gasification slag according to the present invention.

[0056] The method for removing carbon by wet grinding and gasification slag in this embodiment comprises the following steps in sequence:

[0057] (1) Take 50 parts of gasification slag and add 50 parts of water, mix and stir to prepare slurry A with a solid content of 50%;

[0058] (2) Take 100 parts by mass of slurry A, add grinding media, place it in a stirring wet mill and wet grind it to a particle size of 10 μm, sieve and take out the grinding medium to obtain slurry B;

[0059] In step (2), the following wet grinding process parameters are adopted:

[0060] The grinding medium is zirconia grinding balls with a particle size of 0.5-3.0mm. The filling rate of the grinding medium is 70%, the weight ratio of the ball to material is 1:4, and the stirring shaft speed of the wet mill is 400r / min. The grinding time is 40min.

[0061] (3) Put the ...

Embodiment 3

[0066] Example 3 is used to illustrate the method for removing carbon from gasification slag according to the present invention.

[0067] The method for removing carbon by wet grinding and gasification slag in this embodiment comprises the following steps in sequence:

[0068] (1) Take 30 parts of gasification slag and add 70 parts of water, mix and stir to prepare slurry A with a solid content of 30%;

[0069] (2) Take 100 parts by mass of slurry A, add grinding media, place it in a stirring wet mill for wet grinding to a particle size of 15 μm, sieve and take out the grinding media to obtain slurry B;

[0070] In step (2), the following wet grinding process parameters are adopted:

[0071] The grinding medium is zirconia grinding balls with a particle size of 0.5-3.0mm. The filling rate of the grinding medium is 65%, the weight ratio of the ball to material is 1:3, and the stirring shaft speed of the wet mill is 350r / min. The grinding time is 30min.

[0072] (3) Put the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a method for removing carbon from gasification slag, wherein the method comprises the following steps: Step 1: uniformly mixing gasification slag and water to obtain slurry A with a solid content of 10-70% by weight; step 2: Add grinding media to the slurry A, place in a stirring wet mill, wet grind until the particle size of the gasification slag is ≦20 μm, sieve and take out the grinding media, and obtain slurry B; step 3: Place the metal container containing the slurry B in an electric field to rapidly stratify the components in the slurry B; step 4: recover the upper layer of floating carbon particles from the metal container, recover the middle layer of water, and obtain the lower layer Gasification slag after wet grinding to remove carbon. The method of the invention has good carbon removal effect, the treated gasification slag has high purity and no other harmful chemicals are attached, and the carbon content is lower than 1%, which is beneficial to the subsequent wide application of the gasification slag.

Description

technical field [0001] The invention belongs to the technical field of solid waste resource treatment in coal chemical industry, and in particular relates to a method for removing carbon from gasification slag. Background technique [0002] In recent years, the national coal chemical industry has continued to develop, and our country emits 360 million tons of gasification slag every year due to coal combustion. The construction of a large number of gasification slag yards occupies a large amount of land, causes environmental pollution, wastes resources, and brings greater economic pressure and environmental risks to the normal operation of enterprises. Gasification slag is highly corrosive and releases pungent gas, which will occupy a large amount of land when piled up or landfilled, and its leachate will also pollute soil and water. [0003] By studying the composition and chemical properties of the coal gasification slag, it is found that the gasification slag not only ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B03C7/00
CPCB03C7/003B03C7/00
Inventor 贺行洋马庆红苏英赵浩祥杨明鉴付健健王传辉陈顺郑正旗
Owner HUBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap