The invention provides a shoe sole suitable for running and a preparation method thereof, and relates to the technical field of shoe soles. The shoe sole suitable for running includes the following raw materials by weight: nitrile rubber, brominated butyl rubber, nano silicon dioxide, chlorinated polyethylene , polyethylene wax, magnesium oxide, nano zinc oxide, sulfur, quartz glass fiber, polyvinyl formal fiber, boron fiber, polyamide fiber, vulcanization accelerator, plasticizer, antioxidant, white smoke activator, coupling agent, softener, light stabilizer and heat stabilizer. The preparation method comprises the following steps: (1) weighing raw materials, (2) adding into an internal mixer, (3) adding into a double-roller open mill, and (4) vulcanizing and forming. The invention solves the problem that the existing soles do not have the properties of anti-skid, high compressive strength, flexural strength, good toughness and light weight.

Description

technical field

[0001] The invention belongs to the technical field of shoe soles, and in particular relates to a shoe sole suitable for running and a preparation method thereof. Background technique

[0002] With the development of the economy and the improvement of people's living standards, more and more attention is paid to health, among which exercise is an important way to obtain health. Sports shoes are used as a protection tool for people when they exercise, and the soles of shoes often break after wearing them for a short period of time. The phenomenon. As an important part of the shoe, the sole is the most direct part of the shoe in contact with the ground, and its toughness is related to the quality of the entire shoe.

[0003] In addition, the sole must also have other properties besides the basic performance of good skid resistance, such as high compressive strength and light weight.

[0004] However, the existing soles do not have the properties of anti-slip,...

Examples

Embodiment 1

[0037] A sole suitable for running, comprising the following raw materials in parts by weight: 17 parts of nitrile rubber, 55 parts of brominated butyl rubber, 15 parts of nano silicon dioxide, 3 parts of chlorinated polyethylene, 2 parts of polyethylene wax, oxidized 0.5 parts of magnesium, 2.5 parts of nano zinc oxide, 1 part of sulfur, 12 parts of quartz glass fiber, 8 parts of polyvinyl formal fiber, 12 parts of boron fiber, 10 parts of polyamide fiber, 1.1 parts of vulcanization accelerator, 6 parts of plasticizer 1.2 parts of antioxidant, 3 parts of white smoke active agent, 1.5 parts of coupling agent, 0.7 part of softener, 0.3 part of light stabilizer and 0.5 part of heat stabilizer.

[0038] Quartz glass fiber is added to the raw material, and the quartz glass fiber has high strength, high temperature resistance, corrosion resistance, heat insulation and good chemical stability.

[0039] Polyvinyl formal fibers are added to the raw materials, which have the characteri...

Embodiment 2

[0054] A shoe sole suitable for running, comprising the following raw materials in parts by weight: 15 parts of nitrile rubber, 50 parts of brominated butyl rubber, 10 parts of nano silicon dioxide, 1 part of chlorinated polyethylene, 1 part of polyethylene wax, oxidized 0.2 parts of magnesium, 1 part of nano zinc oxide, 0.6 parts of sulfur, 6 parts of quartz glass fiber, 6 parts of polyvinyl formal fiber, 9 parts of boron fiber, 7 parts of polyamide fiber, 0.6 part of vulcanization accelerator, 4 parts of plasticizer 0.6 parts of antioxidant, 2 parts of white smoke active agent, 1 part of coupling agent, 0.5 part of softener, 0.2 part of light stabilizer and 0.2 part of heat stabilizer.

[0055] Quartz glass fiber is added to the raw material, and the quartz glass fiber has high strength, high temperature resistance, corrosion resistance, heat insulation and good chemical stability.

[0056] Polyvinyl formal fibers are added to the raw materials, which have the characteristic...

Embodiment 3

[0071] A shoe sole suitable for running, comprising the following raw materials in parts by weight: 19 parts of nitrile rubber, 60 parts of brominated butyl rubber, 20 parts of nano silicon dioxide, 5 parts of chlorinated polyethylene, 3 parts of polyethylene wax, oxidized 0.8 parts of magnesium, 4 parts of nano zinc oxide, 1.4 parts of sulfur, 18 parts of quartz glass fiber, 10 parts of polyvinyl formal fiber, 15 parts of boron fiber, 13 parts of polyamide fiber, 1.6 parts of vulcanization accelerator, 8 parts of plasticizer 1.8 parts of antioxidant, 4 parts of white smoke active agent, 2 parts of coupling agent, 0.9 part of softener, 0.4 part of light stabilizer and 0.8 part of heat stabilizer.

[0072] Quartz glass fiber is added to the raw material, and the quartz glass fiber has high strength, high temperature resistance, corrosion resistance, heat insulation and good chemical stability.

[0073] Polyvinyl formal fibers are added to the raw materials, which have the chara...

technical field

[0001] The invention belongs to the technical field of shoe soles, and in particular relates to a shoe sole suitable for running and a preparation method thereof. Background technique

[0002] With the development of the economy and the improvement of people's living standards, more and more attention is paid to health, among which exercise is an important way to obtain health. Sports shoes are used as a protection tool for people when they exercise, and the soles of shoes often break after wearing them for a short period of time. The phenomenon. As an important part of the shoe, the sole is the most direct part of the shoe in contact with the ground, and its toughness is related to the quality of the entire shoe.

[0003] In addition, the sole must also have other properties besides the basic performance of good skid resistance, such as high compressive strength and light weight.

[0004] However, the existing soles do not have the properties of anti-slip,...

Examples

Embodiment 1

[0037] A sole suitable for running, comprising the following raw materials in parts by weight: 17 parts of nitrile rubber, 55 parts of brominated butyl rubber, 15 parts of nano silicon dioxide, 3 parts of chlorinated polyethylene, 2 parts of polyethylene wax, oxidized 0.5 parts of magnesium, 2.5 parts of nano zinc oxide, 1 part of sulfur, 12 parts of quartz glass fiber, 8 parts of polyvinyl formal fiber, 12 parts of boron fiber, 10 parts of polyamide fiber, 1.1 parts of vulcanization accelerator, 6 parts of plasticizer 1.2 parts of antioxidant, 3 parts of white smoke active agent, 1.5 parts of coupling agent, 0.7 part of softener, 0.3 part of light stabilizer and 0.5 part of heat stabilizer.

[0038] Quartz glass fiber is added to the raw material, and the quartz glass fiber has high strength, high temperature resistance, corrosion resistance, heat insulation and good chemical stability.

[0039] Polyvinyl formal fibers are added to the raw materials, which have the characteri...

Embodiment 2

[0054] A shoe sole suitable for running, comprising the following raw materials in parts by weight: 15 parts of nitrile rubber, 50 parts of brominated butyl rubber, 10 parts of nano silicon dioxide, 1 part of chlorinated polyethylene, 1 part of polyethylene wax, oxidized 0.2 parts of magnesium, 1 part of nano zinc oxide, 0.6 parts of sulfur, 6 parts of quartz glass fiber, 6 parts of polyvinyl formal fiber, 9 parts of boron fiber, 7 parts of polyamide fiber, 0.6 part of vulcanization accelerator, 4 parts of plasticizer 0.6 parts of antioxidant, 2 parts of white smoke active agent, 1 part of coupling agent, 0.5 part of softener, 0.2 part of light stabilizer and 0.2 part of heat stabilizer.

[0055] Quartz glass fiber is added to the raw material, and the quartz glass fiber has high strength, high temperature resistance, corrosion resistance, heat insulation and good chemical stability.

[0056] Polyvinyl formal fibers are added to the raw materials, which have the characteristic...

Embodiment 3

[0071] A shoe sole suitable for running, comprising the following raw materials in parts by weight: 19 parts of nitrile rubber, 60 parts of brominated butyl rubber, 20 parts of nano silicon dioxide, 5 parts of chlorinated polyethylene, 3 parts of polyethylene wax, oxidized 0.8 parts of magnesium, 4 parts of nano zinc oxide, 1.4 parts of sulfur, 18 parts of quartz glass fiber, 10 parts of polyvinyl formal fiber, 15 parts of boron fiber, 13 parts of polyamide fiber, 1.6 parts of vulcanization accelerator, 8 parts of plasticizer 1.8 parts of antioxidant, 4 parts of white smoke active agent, 2 parts of coupling agent, 0.9 part of softener, 0.4 part of light stabilizer and 0.8 part of heat stabilizer.

[0072] Quartz glass fiber is added to the raw material, and the quartz glass fiber has high strength, high temperature resistance, corrosion resistance, heat insulation and good chemical stability.

[0073] Polyvinyl formal fibers are added to the raw materials, which have the chara...