High-mutual viscosity lustered yellowing-resistance bleached sole rubber and preparation method thereof

A mutual-adhesion and yellowing-resistant technology, applied in shoe soles, footwear, applications, etc., can solve the problem of difficult to meet the needs of use, and achieve the effect of simple method, good use effect and crisp product appearance

Active Publication Date: 2012-11-21
JIHUA 3537 SHOE MAKING
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above properties lead to vulcanized rubber having many deficiencies when used as sole rubber, and it is difficult to meet the needs of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-mutual viscosity lustered yellowing-resistance bleached sole rubber and preparation method thereof
  • High-mutual viscosity lustered yellowing-resistance bleached sole rubber and preparation method thereof
  • High-mutual viscosity lustered yellowing-resistance bleached sole rubber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Embodiment 1 of the present invention: high mutual stickiness luster type anti-yellowing bleaching white shoe sole rubber, calculates by weight, it comprises 65 parts of 1# standard glues, 15 parts of 2000R solution polymerized styrene-butadiene rubbers, 20 parts of butadiene rubbers, 2 parts of sulfur, 2.6 parts of microcrystalline wax, 0.5 parts of accelerator M, 1.9 parts of accelerator DM, 5.6 parts of tertiary stearic acid, 2.5 parts of nano-zinc oxide; 4.3 parts of polyethylene glycol 4000, 1.7 parts of anti-aging agent KY- 405L, 1.9 parts of ultramarine blue, 50 parts of titanium dioxide (R930), 45 parts of white carbon black, 25 parts of nano-calcium carbonate, 0.50 parts of 1% permanent purple mother gum, 8.6 parts of 5# white machine oil and 2.5 parts of RX-80 xylene resin.

[0044] The preparation method of the high mutual-adhesive gloss type anti-yellowing bleaching white shoe sole rubber is characterized in that: plasticizing first, pressing the 1# standard...

Embodiment 2

[0045] Embodiment 2 of the present invention: high mutual stickiness luster type anti-yellowing bleaching white shoe sole rubber, calculates by weight, it comprises 60 parts of 1# standard glues, 20 parts of 2000R solution polymerized styrene-butadiene rubbers, 15 parts of butadiene rubbers, 1 part of sulfur, 2.4 parts of microcrystalline wax, 0.4 parts of accelerator M, 2.0 parts of accelerator DM, 5 parts of tertiary stearic acid, 2 parts of nano-zinc oxide; 4 parts of polyethylene glycol 4000#, 12 parts of anti-aging agent KY -405L, 1.7 parts of ultramarine blue, 55 parts of titanium dioxide (R930), 40 parts of white carbon black, 30 parts of nano calcium carbonate, 0.1 part of 1% permanent purple mother gum, 8 parts of 5# white machine oil and 2 parts of RX-80 toluene resin.

[0046] The preparation method of the high mutual-adhesive gloss type anti-yellowing bleaching white shoe sole rubber is characterized in that: plasticizing first, pressing the 1# standard rubber in t...

Embodiment 3

[0047] Embodiment 3 of the present invention: high mutual tack gloss type anti-yellowing bleaching white shoe sole rubber, is characterized in that: by weight, it comprises 70 parts of 1# standard glue, 10 parts of 2000R solution polystyrene butadiene rubber, 25 parts Butadiene gum, 3 parts of sulfur, 2.8 parts of microcrystalline wax, 0.6 parts of accelerator M, 1.8 parts of accelerator DM, 6 parts of tertiary stearic acid, 3 parts of nano-zinc oxide; 5 parts of polyethylene glycol 4000#, 2 parts 1 part of anti-aging agent KY-405L, 2.1 parts of ultramarine blue, 45 parts of titanium dioxide (R930), 50 parts of white carbon black, 20 parts of nano-calcium carbonate, 0.15 parts of 1% permanent purple mother gum, 9 parts of 5# white machine oil and 2~ 3 parts RX-80 xylene resin.

[0048] The preparation method of the high mutual-adhesive gloss type anti-yellowing bleaching white shoe sole rubber is characterized in that: plasticating first, pressing the 1# standard rubber in the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to high-mutual viscosity lustered yellowing-resistance bleached sole rubber and a preparation method thereof. The high-mutual viscosity lustered yellowing-resistance bleached sole rubber comprises 60 to 70 weight parts of No.1 standard rubber, 10 to 20 weight parts of 2000R solution polymerized butadiene-styrene rubber, 15 to 25 weight parts of cis-1,4-butadiene rubber, 1 to3 weight parts of sulfur, 2.2 to 2.6 weight parts of promoter, 5 to 6 weight parts of stearic acid, 2 to 3 weight parts of nano zinc oxide, 4 to 5 weight parts of polyethylene glycol No.4000, 1 to 2 weight parts of anti-aging agent, 1.7 to 2.1 weight parts of ultramarine, 45 to 55 weight parts of titanium white, 40 to 50 weight parts of white carbon black, 20 to 30 weight parts of nano calcium carbonate, 0.4 to 0.6 weight part of 1-percent pigment permanent violet and 7 to 9 weight parts of white engine oil. In the invention, the formula and preparation method of the product are improved, andsole rubber, which has high rubber viscosity and luster and is yellowing-resistance and as white as snow, is obtained by screening.

Description

technical field [0001] The invention relates to a rubber and a preparation method thereof, in particular to a bleached sole rubber and a preparation method thereof. Background technique [0002] There are many different proportioning schemes for shoe sole rubber according to the needs of the application. Vulcanized rubber is one of them. The current vulcanized rubber has the characteristics of low whiteness, low gloss, matte type, low viscosity of semi-finished rubber materials, and pattern retention. Poor resistance, easy to cause compression deformation, and the appearance of the product is not clear; and the yellowing resistance of the sun lamp B method reaches 3 to 5 grades, and the yellowing resistance of the sun lamp B method is lower than 3 grades, and the anti-yellowing accelerator must be used High-priced functional materials such as ultraviolet light absorbers; the surface of the film has poor adhesion and is easy to fall off, and the mutual adhesion of unvulcanize...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/06C08L9/00C08K13/02C08K3/06C08K3/22C08K3/36C08K5/09A43B13/04B29B7/02
Inventor 杜江陈松雄晋齐怀周川泉田杰王春桥
Owner JIHUA 3537 SHOE MAKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com