Preparation method of standard spectrum sample
A spectral standard sample and standard sample technology, which is applied in the field of spectral standard sample preparation, can solve the problems of not being able to meet the requirements of fast production in front of the furnace, increasing the frequency of standard sample replacement, and unfavorable coordination, so as to achieve high practical value and reduce preparation costs. Cost, effect of increasing sample size
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0034] Example one:
[0035] This embodiment is a preparation method of stainless steel 304 standard sample, and the steps are as follows:
[0036] 1. Chemical composition selection:
[0037] The element composition range of the calibration sample should meet the requirements of the refining period sample and product sample of the AOD furnace in front of the analysis and control furnace. According to the 304 product standard, the molten steel in the furnace with the appropriate composition is selected during the smelting of the AOD furnace. The selection basis is based on the composition range requirements shown in the following table 1.
[0038] Table 1: Chemical composition range table (%)
[0039] Element
[0040] 2. Standard sample preparation:
[0041] 2.1. Baking of the model:
[0042] After cleaning the refractory bricks and porcelain pipes used, bake them at a temperature of 800-1200°C for more than 30 minutes and cool naturally;
[0043] The inner diameter of the refractory br...
Example Embodiment
[0090] Embodiment two:
[0091] This embodiment adopts the method for preparing the standard sample of heat-resistant stainless steel TP310 by continuous casting, and the steps and equipment used are the same as those in the first embodiment. The difference between the second embodiment and the first embodiment is the difference in the content of chromium and nickel. At the same time, the second embodiment adds the elements of Ti, N, Co, and Nb.
[0092] The fixed value components of the standard sample of heat-resistant stainless steel TP310 are as follows:
[0093] Table 10: Fixed value data table (%)
[0094] Element
PUM
Property | Measurement | Unit |
---|---|---|
Length | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap