Molten steel of atmospheric corrosion-resistant section steel, chromium-niobium-containing atmospheric corrosion-resistant section steel and production method thereof

Abstract

The invention relates to the field of steel making and provides atmospheric corrosion-resistant molten structural steel. The molten structural steel is composed of 0.01%-0.09% by weight of C, 0.15%-0.35% by weight of Si, 0.30%-0.60% by weight of Mn, 0.30%-0.40% by weight of Cu, 0.20%-0.30% by weight of Ni, 3.5%-5.0% by weight of Cr, 0.06%-0.12% by weight of V, 0.01%-0.015% by weight of Nb, 0.008%-0.014% by weight of N, less than or equal to 0.030% by weight of P, less than or equal to 0.020% by weight of S and the balance of unavoidable impurities and Fe. The invention provides atmospheric corrosion-resistant structural steel and a production method thereof. The molten steel continuous casting process improves the central quality of a casting blank, prevents central cracks and central shrinkage holes, improves the quality of the high strength and high atmospheric corrosion resistant structural steel blank and greatly improves a casting blank qualification rate. The atmospheric corrosion-resistant structural steel has good atmospheric corrosion resistance and high strength properties.

Description

technical field [0001] The invention relates to an atmospheric corrosion-resistant steel molten steel, an atmospheric corrosion-resistant steel obtained by continuous casting and rolling using the molten steel of the invention, a production method of the atmospheric corrosion-resistant steel and the atmospheric corrosion-resistant steel obtained by the method. Background technique [0002] Atmospheric corrosion-resistant steel is a very important class of steel. Its atmospheric corrosion resistance is 2-8 times that of ordinary steel, and its paintability is improved by 1.5-10 times. Due to the effectiveness of atmospheric corrosion resistance steel compared with ordinary steel, and its good economic efficiency compared with stainless steel, it has been developed rapidly in various countries in the world. Various steel structures used in the open air, railway vehicles and bridges are is the scope of its application. [0003] The early atmospheric corrosion-resistant steel v...

AI Technical Summary

Problems solved by technology

However, as a profile steel, the square continuous casting slab produced after increasing the chromium content has relatively obvious central defects (mainly central cracks and central shrinkage cavities), and the strength index of the final profile steel cannot reach that of plate steel Therefore, profile steels with better atmospheric corrosion resistance are still under development.

Images