A production method and technology for commercial vehicles, applied in the field of steel for vehicle beams and its manufacturing, can solve the problems that are not conducive to the forming performance of steel materials, and the hole expansion performance of materials that are not mentioned

Active Publication Date: 2021-06-15
武汉钢铁有限公司
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The addition of 0.16-0.20% carbon element is not conducive to improving the formability of steel, and the hole expansion performance of the material is not mentioned

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An easy-to-form commercial vehicle beam steel and production method
  • An easy-to-form commercial vehicle beam steel and production method
  • An easy-to-form commercial vehicle beam steel and production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0042] The present invention is described in detail below:

[0043] Table 1 is the value list of each embodiment of the present invention and comparative examples;

[0044] Table 2 is the main process parameter list of each embodiment of the present invention and comparative example;

[0045] Table 3 is a list of the performance tests of the various embodiments of the present invention and comparative examples.

[0046] Each embodiment of the present invention is produced according to the following production process:

[0047] 1) Vacuum treatment is carried out after smelting in the converter, and the treatment time is not less than 15 minutes, and then the molten steel is continuously cast into billets;

[0048] 2) Heating the slab in sections: first preheat the slab to 800-1000°C, and the preheating period is 60-80 minutes;

[0049] Heating to 1100-1200°C within 20-40 minutes;

[0050] Finally, it enters the soaking section, the soaking temperature is controlled at 1240-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

An easy-to-form commercial vehicle beam steel, the composition and weight percentage of which are: C: 0.04-0.06%, Mn: 1.81-2.10%, P≤0.008%, S≤0.002%, Als: 0.30-0.50%, Cr: 0.31~0.50%, Ti: 0.03~0.05%, N≤0.003%. Production method: 1) Vacuum treatment after smelting in converter; segmental heating of cast slab; segmental rolling; cooling by two-stage cooling method; finishing after coiling. The yield strength of the invention is ≥650 MPa, the tensile strength is 750-880 MPa, the elongation rate is ≥16%, and the hole expansion rate is ≥60%, which can meet the complex deformation requirements of commercial vehicle beams.

Description

technical field [0001] The invention relates to hot-rolled steel for automobiles and a production method thereof, in particular to steel for vehicle beams and a production method thereof. Background technique [0002] The frame is the main body of the lightweight application of commercial vehicles. The frame is composed of longitudinal beams and cross beams. Compared with the simple structural design of the longitudinal beams, the cross beams have higher requirements on the formability of materials due to their complex structure. After using high-strength steel, there is a problem of forming cracks. Currently, the main application is 500MPa-level beams. steel. There is a greater demand in the market for high-strength beam steels with higher strength grades and good formability. The hole expansion test results can better evaluate the formability of the material. [0003] After initial search: [0004] The document with the Chinese patent application number CN201310231052....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C22C38/06C22C38/04C22C38/28C21D8/02C22C33/04
CPCC21D8/0205C21D8/0226C21D8/0263C21D2211/002C21D2211/005C22C33/04C22C38/04C22C38/06C22C38/28
Inventor赵江涛李利巍陈吉清徐浩刘亮宋畅刘斌冯佳王立新
Owner武汉钢铁有限公司