Decorative rock plate with naturally pushed-aside textures and production method of decorative rock plate
A production method and decorative rock technology, applied in the production of ceramic materials, manufacturing tools, ceramic molding machines, etc., can solve the problems of not clear and realistic texture, difficult pattern control of glaze process, and not natural and rich patterns, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0079] like Figure 1-11 As shown, the present invention adopts the following steps to realize:
[0080] A, prepare the green body powder according to the conventional method, standby;
[0081] B. Preparation of slurry for digital pulping system: Weigh mineral raw materials according to the designed pulp chemical composition of digital pulping system, add a certain proportion of debonding agent, suspending agent and water for ball milling to prepare digital pulping system. Slurry, the specific gravity of the slurry for digital pulping system is 1.20g / cm 3 , the flow rate of the 50mL flow rate cup is 10s, the viscosity is 40mPa·s, the surface tension is 50mN / m, the Reynolds number is 48, the Weber number is 76.9, and the Bond number is 0.15; the chemical composition of the slurry used in the digital pulping system is Weight percent: SiO 2 47%, Al 2 O 3 14%, CaO 13%, MgO 7%, K 2 O 2%, Na 2 O 2%, BaO 5%, ZnO 2%, B 2 O 3 2%, Fe 2 O 3 ≤0.5%, TiO 2 ≤0.3%, loss on ignit...
Embodiment 2
[0095] like Figure 1-11 As shown, the present invention adopts the following steps to realize:
[0096] A, prepare the green body powder according to the conventional method, standby;
[0097] B. Preparation of slurry for digital pulping system: Weigh mineral raw materials according to the designed pulp chemical composition of digital pulping system, add a certain proportion of debonding agent, suspending agent and water for ball milling to prepare digital pulping system. Slurry, the specific gravity of the slurry used in the digital pulping system is 1.85g / cm 3 , the flow rate of the 50mL flow rate cup is 25s, the viscosity is 500mPa·s, the surface tension is 60mN / m, the Reynolds number is 5.9, the Weber number is 98.9, and the Bond number is 0.19; the chemical composition of the slurry used in the digital pulping system is Weight percent: SiO 2 46%, Al 2 O 3 23%, CaO 7%, MgO 3%, K 2 O 1%, Na 2 O 2%, BaO 6%, ZnO 2%, B 2 O 3 2%, Fe 2 O 3 ≤0.5%, TiO 2 ≤0.3%, loss...
Embodiment 3
[0112] like Figure 1-11 As shown, the present invention adopts the following steps to realize:
[0113] A, prepare the green body powder according to the conventional method, standby;
[0114] B. Preparation of slurry for digital pulping system: Weigh mineral raw materials according to the designed pulp chemical composition of digital pulping system, add a certain proportion of debonding agent, suspending agent and water for ball milling to prepare digital pulping system. Slurry, the specific gravity of the pulp used in the digital pulping system is 1.55g / cm 3 , the flow rate of the 50mL flow rate cup is 20s, the viscosity is 135mPa·s, the surface tension is 70mN / m, the Reynolds number is 18.4, the Weber number is 71, and the Bond number is 0.14; the chemical composition of the slurry used in the digital pulping system is Weight percent: SiO 2 66%, Al 2 O 3 21%, CaO 0.5%, MgO 0.1%, K 2 O 4%, Na 2 O 3%, ZrO 2 2%, Fe 2 O 3 ≤0.5%, TiO 2 ≤0.5%, loss on ignition ≤8%;...
PUM
Property | Measurement | Unit |
---|---|---|
surface tension | aaaaa | aaaaa |
Reynolds number | aaaaa | aaaaa |
Weber number | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com