Centrifugal cast high-speed steel roll manufacture

A technology of centrifugal casting and manufacturing method, which is applied in the fields of centrifugal casting high-speed steel roll manufacturing and metallurgical roll manufacturing. It can solve the problems that segregation is difficult to completely eliminate, and achieve the effects of inhibiting gravity segregation, convenient operation, good red hardness and high temperature wear resistance. Effect

Inactive Publication Date: 2005-01-26
XI AN JIAOTONG UNIV
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The W content in high-speed steel rolls is also controlled at a low level, and Nb is not added to high-speed steel, so segregation is difficult to completely eliminate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] The high-speed steel roll of this embodiment is cast by a vertical centrifuge, the roll body is made of high-C high-W high-speed steel, the roll core is made of ductile iron, the roll body is melted in a 500kg intermediate frequency induction furnace, the roll core is melted in a 3t cupola furnace, and the roll core is melted in a 1t intermediate frequency induction furnace. The furnace adjusts the composition and temperature, and the roller core is spheroidized with rare earth magnesium alloy. The chemical composition of the roll is shown in Table 2.

[0066] Table 2 Chemical composition of high-speed steel rolls

[0067] C

W

V

Mo

Cr

Ni

Si

mn

Y

K

S

P

Roll body

2.46

16.68

4.31

3.64

11.2

0.65

1.32

0.87

0.07

0.11

0.026

0.034

Roll core

3.53

-

-

-

0.28

0.37

2.17

0.52

0.03RE

0.05Mg...

Embodiment 2

[0075] In this embodiment, the high-speed steel roll is cast by a horizontal centrifuge. The roll body is made of high-C and high-W high-speed steel, and the roll core is made of high-strength gray cast iron. The chemical composition of the roll is shown in Table 3.

[0076] Table 3 Chemical composition of high-speed steel rolls

[0077] C

W

V

Mo

Cr

Ni

Si

mn

Y

K

S

P

Roll body

2.54

20.27

4.90

2.26

9.68

0.73

1.21

0.75

0.08

0.13

0.017

0.037

Roll core

2.93

-

0.12

0.26

0.44

0.87

2.06

0.48

-

-

0.038

0.043

[0078] During the pouring and solidification process of the high-speed steel roll body, an electromagnetic field is added to the mold, and the magnetic induction intensity of the electromagnetic field is 0.10T. Adding an electromagnetic field to the centrifugal cas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A centrifugal casting technology for manufacturing roller of high-speed steel, which is composed of the roller body made of high-C high-W high-speed steel and the core made of cast iron, includes such steps as pouring the molten high-speed steel in the rotating mould of centrifugal machine, applying an electromagnetic field in the pouring and solidifying procedure, adding protecting agnet to the inner surface of roller body, pouring molten iron, cooling to lower than 100 deg.C, demoulding, coarse machining, quenching, tempering, and fine machining. Its advantages are high uniformity without segregation, and compact structure.

Description

1. Technical field [0001] The invention belongs to the technical field of steel rolling, and relates to a method for manufacturing metallurgical rolls, in particular to a method for manufacturing centrifugally cast high-speed steel rolls. 2. Background technology [0002] In recent years, hot rolling technology has made great progress, and in terms of hot rolling rolls, high-performance high-speed steel rolls are also being developed. The outer layer of the high-speed steel roll is based on the addition of C content to ordinary high-speed steel, and a large amount of V and W are added at the same time to generate more high-hardness V carbides and W carbides, thereby obtaining high wear resistance. Centrifugal casting roll production method and continuous casting composite method (Chinese invention patent CN1280042), electroslag remelting method (US patent US5081760, Chinese invention patent CN1157192), spray deposition forming method and hot isostatic pressing method (Japane...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D13/02B22D19/16
Inventor 符寒光邢建东
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com