Abstract

The invention relates to an environmental health-care functional material and a preparation method thereof. The preparation method comprises the following steps: placing loess into an oven for dry sterilizing, drying, then grinding and screening to prepare loess powder; performing microwave heating pretreatment on tourmaline powder, then pouring into a stirring machine to stir, simultaneously adding catalyst powder, uniformly stirring, then further adding permanent magnet material powder, further stirring, further adding graphene powder, further stirring, finally adding activated carbon powder and the well prepared loess powder, and stirring at uniform speed for 1h to prepare environmental health-care functional composite powder; and sintering at low temperature, taking out, cooling to room temperature and magnetizing by using a magnetizing machine to prepare the environmental health-care functional material. The environmental health-care functional material provided by the invention can effectively improve and perfect theory of a multi-material micro-particle system, realize a synergistic aggregation effect of ecological environmental factors with relatively high efficiency, greatly improve the comprehensive control effect of a current living environment of people and meet the demands of environmental health care of the people.

Description

technical field

[0001] The invention belongs to the field of materials, and in particular relates to an environmental health-preserving functional material and a preparation method thereof. Background technique

[0002] With the acceleration of industrialization and urbanization in our country, while enjoying modern material civilization, we must also face environmental problems such as land pollution, air pollution, and water pollution. This is also the main reason for the increasing number of sub-healthy populations. Therefore, developing new materials with environmental health-preserving factors and restoring the living environment of human beings has become an urgent problem to be solved in the research of new materials.

[0003] The theory of "Dongtian Fudi" in ancient China believes that the world has its own unique space-time structure and is relatively isolated, with its own natural components such as heaven and earth, sun and moon, mountains, rivers, and vegetation....

Examples

Embodiment 1

[0028] Take 10% of graphene powder of 10 microns, 30% of loess, 20% of titanium dioxide powder of 10 microns, 20% of ferrite powder of 10 microns, 10% of ferrite permanent magnetic material powder of 10 microns, 100 Micron coconut shell activated carbon powder 10%.

[0029] The specific preparation method is to prepare the raw materials in the above weight percentage according to the following steps:

[0030] a) Put the loess in an oven for drying and sterilization, continue drying at 300°C for 6 hours, then grind it with a ball mill for 3 hours, pass through a 100 micron sieve, and prepare loess powder;

[0031] b) Pretreat the 10 micron ferrite powder with microwave heating for 1 hour, then pour it into the blender and stir while adding 10 micron titanium dioxide powder, stir evenly for 30 minutes, then add 10 micron ferrite permanent magnet material Powder, continue stirring for 30 minutes, then add 10 micron graphene powder, continue stirring for 30 minutes, finally add 1...

Embodiment 2

[0034] Take 5% of graphene powder of 5 microns, 20% of loess, 20% of tungsten trioxide powder of 5 microns, 20% of magnesium tourmaline powder of 5 microns, 20% of NdFeB material powder of 5 microns, 50 Micron bamboo activated carbon powder 15%.

[0035] The specific preparation method is to prepare the raw materials in the above weight percentage according to the following steps:

[0036] a) Put the loess in an oven for drying and sterilization, continue drying at 300°C for 6 hours, then grind it with a ball mill for 3 hours, pass through a 100 micron sieve, and prepare loess powder;

[0037] b) Pretreat 5-micron magnesium tourmaline powder with microwave heating for 1 hour, then pour it into a blender and stir while adding 5-micron tungsten trioxide powder, stir evenly for 30 minutes, then add 5-micron NdFeB Material powder, continue stirring for 30 minutes, then add 5 micron graphene powder, continue stirring for 30 minutes, finally add 50 micron bamboo activated carbon po...

Embodiment 3

[0040] Take 5 micron graphene powder 10%, 100 micron loess powder 20%, 10 micron tungsten trioxide powder 10%, 3 micron lithium tourmaline powder 30%, 10 micron samarium cobalt material powder 15%, 100 micron coal-based activated carbon powder 15%.

[0041] The specific preparation method is to prepare the raw materials in the above weight percentage according to the following steps:

[0042] a) Put the loess in an oven for drying and sterilization, continue drying at 300°C for 6 hours, then grind it with a ball mill for 3 hours, pass through a 100 micron sieve, and prepare loess powder;

[0043] b) Pretreat 3 micron lithium tourmaline powder with microwave heating for 1 hour, take the pretreated 3 micron lithium tourmaline powder and pour it into a blender, add 10 micron samarium cobalt material powder, and stir evenly for 30 Minutes later, add 10 microns of ferrite powder and continue stirring for 30 minutes, then add 5 microns of graphene powder, continue stirring for 30 m...

technical field

[0001] The invention belongs to the field of materials, and in particular relates to an environmental health-preserving functional material and a preparation method thereof. Background technique

[0002] With the acceleration of industrialization and urbanization in our country, while enjoying modern material civilization, we must also face environmental problems such as land pollution, air pollution, and water pollution. This is also the main reason for the increasing number of sub-healthy populations. Therefore, developing new materials with environmental health-preserving factors and restoring the living environment of human beings has become an urgent problem to be solved in the research of new materials.

[0003] The theory of "Dongtian Fudi" in ancient China believes that the world has its own unique space-time structure and is relatively isolated, with its own natural components such as heaven and earth, sun and moon, mountains, rivers, and vegetation....

Examples

Embodiment 1

[0028] Take 10% of graphene powder of 10 microns, 30% of loess, 20% of titanium dioxide powder of 10 microns, 20% of ferrite powder of 10 microns, 10% of ferrite permanent magnetic material powder of 10 microns, 100 Micron coconut shell activated carbon powder 10%.

[0029] The specific preparation method is to prepare the raw materials in the above weight percentage according to the following steps:

[0030] a) Put the loess in an oven for drying and sterilization, continue drying at 300°C for 6 hours, then grind it with a ball mill for 3 hours, pass through a 100 micron sieve, and prepare loess powder;

[0031] b) Pretreat the 10 micron ferrite powder with microwave heating for 1 hour, then pour it into the blender and stir while adding 10 micron titanium dioxide powder, stir evenly for 30 minutes, then add 10 micron ferrite permanent magnet material Powder, continue stirring for 30 minutes, then add 10 micron graphene powder, continue stirring for 30 minutes, finally add 1...

Embodiment 2

[0034] Take 5% of graphene powder of 5 microns, 20% of loess, 20% of tungsten trioxide powder of 5 microns, 20% of magnesium tourmaline powder of 5 microns, 20% of NdFeB material powder of 5 microns, 50 Micron bamboo activated carbon powder 15%.

[0035] The specific preparation method is to prepare the raw materials in the above weight percentage according to the following steps:

[0036] a) Put the loess in an oven for drying and sterilization, continue drying at 300°C for 6 hours, then grind it with a ball mill for 3 hours, pass through a 100 micron sieve, and prepare loess powder;

[0037] b) Pretreat 5-micron magnesium tourmaline powder with microwave heating for 1 hour, then pour it into a blender and stir while adding 5-micron tungsten trioxide powder, stir evenly for 30 minutes, then add 5-micron NdFeB Material powder, continue stirring for 30 minutes, then add 5 micron graphene powder, continue stirring for 30 minutes, finally add 50 micron bamboo activated carbon po...

Embodiment 3

[0040] Take 5 micron graphene powder 10%, 100 micron loess powder 20%, 10 micron tungsten trioxide powder 10%, 3 micron lithium tourmaline powder 30%, 10 micron samarium cobalt material powder 15%, 100 micron coal-based activated carbon powder 15%.

[0041] The specific preparation method is to prepare the raw materials in the above weight percentage according to the following steps:

[0042] a) Put the loess in an oven for drying and sterilization, continue drying at 300°C for 6 hours, then grind it with a ball mill for 3 hours, pass through a 100 micron sieve, and prepare loess powder;

[0043] b) Pretreat 3 micron lithium tourmaline powder with microwave heating for 1 hour, take the pretreated 3 micron lithium tourmaline powder and pour it into a blender, add 10 micron samarium cobalt material powder, and stir evenly for 30 Minutes later, add 10 microns of ferrite powder and continue stirring for 30 minutes, then add 5 microns of graphene powder, continue stirring for 30 m...