Double-layer knitting stitch type fleece and making method thereof

A manufacturing method and double-layer technology, which is applied in knitting, weft knitting, textiles and papermaking, etc., can solve the problems of easy pilling, poor elasticity, and single structure of the wool surface, and achieve the effect of fluffy hand feeling and excellent elasticity

CN105862238AActive Publication Date: 2016-08-17GUANGDONG ESQUEL TEXTILES CO LTD
6 Cites 14 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
Publication Date
2016-08-17

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention provides double-layer knitting stitch type fleece and a making method thereof. The double-layer knitting stitch type fleece comprises a surface layer, a middle layer and a bottom layer, wherein the surface layer is made of cotton yarn or cotton blended yarn, the middle layer is made of dacron or nylon, the bottom layer is made of dacron or blended yarn, the surface layer is connected with the bottom layer through the middle layer, and the bottom layer is subjected to fluffing finishing. The invention further provides the making method of the double-layer knitting stitch type fleece. The making method comprises the steps of forming the surface layer and the bottom layer with the knitting double-layer weaving method, connecting the surface layer and the bottom layer into a whole by means of the middle layer to form knitting double-layer gray fabric, and conducting functional after treatment on the knitting double-layer gray fabric to obtain the double-layer knitting stitch type fleece.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the field of knitted fabrics, and relates to a raised fabric with double-layer knitted fabric and a manufacturing method thereof. Background technique

[0002] Raised fabric in the field of knitting is called sweater cloth in China and FLEECE abroad. It is a single-sided structure, generally plain weave and terry weaving process. The terry surface is piled and piled. During the process, due to the limitation of the model, the fabric surface structure is single, and the front can only be made of plain weave. The product has poor elasticity and is easy to pill after washing. Due to the limitations of the above defects, only loose sweaters or loose jackets can be selected when making ready-to-wear styles, and these ready-made clothes will have pilling in the inner layer after washing, which will affect the appearance. Contents of the invention

[0003] In view of the above-mentioned shortcomings of the prior art, the object of ...

Examples

Embodiment 1

[0046] This embodiment provides a kind of double-layer knitting tissue raised fabric, the structure of this fabric is as follows: figure 1 As shown, it includes surface cloth (1), middle layer (2) and bottom layer cloth (3), wherein, surface layer cloth (1) adopts 100% ring-spun cotton yarn with 30 lbs, and its twist coefficient is 3.7; bottom layer cloth (3 ) adopts 20 English count polyester-cotton blended yarns (60% cotton / 40% polyester), and its twist coefficient is 3.5; the middle layer (2) adopts 75D / 72F polyester filaments.

[0047] The manufacture method of the present embodiment double-layer knitting organization raised fabric is:

[0048] The model used: 18G large circular knitting machine, the machine speed is 20r / min, the distance between the tube opening is 1.0cm, and the yarn feeding tension is 8cN. The large circular knitting machine is equipped with a FEED machine with a positive yarn feeding device.

[0049] Double-sided knitting with a plain weave six-patter...

Embodiment 2

[0061] This embodiment provides a kind of double-layer knitting tissue raised fabric, the structure of this fabric is as follows: figure 1 Shown, comprise surface layer cloth (1), middle layer (2) and bottom layer cloth (3), wherein, surface layer cloth (1) adopts 26 British counts 100% ring-spun cotton yarn, and its twist coefficient is 3.6; Bottom layer cloth (3 ) adopts 16 British count polyester-cotton blended yarns (60% cotton / 40% polyester), its twist coefficient is 3.5, and the middle layer (2) adopts 100D / 144F polyester filaments.

[0062] The manufacture method of the present embodiment double-layer knitting organization raised fabric is:

[0063] The model used: 18G large circular knitting machine, the machine speed is 20r / min, the distance between the tube opening is 1.0cm, and the yarn feeding tension is 8cN. The large circular knitting machine is equipped with a FEED machine with a positive yarn feeding device.

[0064] Double-sided knitting with eight-mode pique...

Embodiment 3

[0076] This embodiment provides a kind of double-layer knitting tissue raised fabric, the structure of this fabric is as follows: figure 1 Shown, comprise surface layer cloth (1), middle layer (2) and bottom layer cloth (3), wherein, surface layer cloth (1) adopts the cotton yarn of 30 pounds 100% ring spinning, twist coefficient is 3.7; Bottom layer cloth (3 ) adopts polyester-cotton blended yarn (60% cotton / 40% polyester) of 26 English count twist coefficients of 3.6, and the middle layer (2) is 75D / 72F polyester filament.

[0077] The manufacture method of the present embodiment double-layer knitting organization raised fabric is:

[0078] The model used: 18G large circular knitting machine, the machine speed is 20r / min, the distance between the tube opening is 1.0cm, and the yarn feeding tension is 8cN. The large circular knitting machine is equipped with a FEED machine with a positive yarn feeding device.

[0079] Double knitting with pique ten-mode weave, such as Figu...