Giant engineering machinery tyre repair adhesive and preparation thereof

A technology of construction machinery and repair glue, which is applied in the direction of adhesives, adhesive types, natural rubber adhesives, etc., can solve the problems of toughness, heat generation value and adhesion, and the overall effect of adhesion is not ideal, so as to improve processing safety , Improve the bonding strength, the effect of high-strength bonding ability

Inactive Publication Date: 2009-05-20
HAOHUA SOUTH CHINAGUILIN RUBBER
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But for giant OTR tires, the overall effects of toughness, calorific value and adhesion to the carcass are not ideal enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Giant construction machinery tire repair glue formula:

[0046] 2# smoked sheet glue: 100 parts;

[0047] N234 reinforcing carbon black: 30 parts;

[0048] Pine tar: 6 parts;

[0049] Adhesive RE: 2 parts;

[0050] Adhesive RH: 1 part;

[0051] Cobalt neodecanoate: 2 parts;

[0052] Zinc oxide: 3 parts;

[0053] Stearic acid: 3 parts;

[0054] Antiaging agent 4010NA: 1 part;

[0055] Antiaging agent RD: 3 parts;

[0056] Sulfur: 1 part;

[0057] Vulcanizing agent DTDM: 1 part;

[0058] Accelerator DM: 3 parts;

[0059] Anti-scorch agent CTP: 0.5 parts.

[0060] Preparation:

[0061] 1) Weigh 2# smoked sheet rubber, N234 reinforcing carbon black, pine tar, binder RE, cobalt neodecanoate, zinc oxide, stearic acid, antioxidant 4010NA and antioxidant RD according to the above ratio Put into a rubber internal mixer (volume of 140 liters, rotor speed of 20 to 40r / min), and knead for 8 minutes at a speed of 40r / min at 160°C to obtain rubber compound A;

[0062] 2...

Embodiment 2

[0065] Giant construction machinery tire repair glue formula:

[0066] 3# smoked sheet glue: 100 parts;

[0067] N115 reinforcing carbon black: 35 parts;

[0068] Pine tar: 4 parts;

[0069] Adhesive RE: 3 parts;

[0070] Adhesive RH: 2 parts;

[0071] Cobalt neodecanoate: 1.5 parts;

[0072] Zinc oxide: 5 parts;

[0073] Stearic acid: 2 parts;

[0074] Antiaging agent 4010NA: 2 parts;

[0075] Antiaging agent RD: 2 parts;

[0076] Sulfur: 1.5 parts;

[0077] Vulcanizing agent DTDM: 0.6 parts;

[0078] Accelerator DM: 2 parts;

[0079] Anti-scorch agent CTP: 0.3 parts.

[0080] Preparation:

[0081] 1) Weigh 3# smoked sheet rubber, N115 reinforcing carbon black, pine tar, adhesive RE, cobalt neodecanoate, zinc oxide, stearic acid, antioxidant 4010NA and antioxidant RD according to the above ratio Put into a rubber internal mixer (volume of 140 liters, rotor speed of 20 to 40r / min), and mix at a speed of 40r / min for 12min at 140°C to obtain rubber compound A;

[0...

Embodiment 3

[0085] Giant construction machinery tire repair glue formula:

[0086] 2# smoked sheet glue: 30 parts;

[0087] 3# smoked sheet glue: 70 parts;

[0088] N234 reinforcing carbon black: 40 parts;

[0089] Pine tar: 2 parts;

[0090] Adhesive RE: 4 parts;

[0091] Adhesive RH: 3 parts;

[0092] Cobalt neodecanoate: 1 part;

[0093] Zinc oxide: 7 parts;

[0094] Stearic acid: 1 part;

[0095] Antiaging agent 4010NA: 3 parts;

[0096] Antiaging agent RD: 1 part;

[0097] Sulfur: 2 parts;

[0098] Vulcanizing agent DTDM: 0.2 parts;

[0099] Accelerator DM: 1 part;

[0100] Anti-scorch agent CTP: 0.1 part.

[0101] Preparation:

[0102] 1) Weigh the 2# smoked sheet glue, N234 reinforcing carbon black, pine tar, binder RE, cobalt neodecanoate, zinc oxide, stearic acid, antioxidant 4010NA and antioxidant RD according to the above ratio Put into a rubber internal mixer (volume of 140 liters, rotor speed of 20 to 40r / min), and mix at a speed of 40r / min for 10min at 150°C to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a tyre-repairing adhesive for giant engineering machines and a preparation method thereof. The tyre-repairing adhesive for the giant engineering machines takes natural rubber and reinforcing carbon black as main components which are properly matched with a softener, a binding agent, an activator, an antioxidant, a vulcanizing agent, an accelerator and a scorch retarder, and is obtained by twice of mixing and milling by a rubber internal mixer. The tyre-repairing adhesive for the giant engineering machines prepared by the formula and the method is characterized by low temperature but quick vulcanizing and stable storage, can also obtain excellent balance between toughness, calorific value, thermal aging property and wearing resistance and between the tyre-repairing adhesive and the binding performance of the tyre body, and is particularly suitable for the adhesive used for repairing tyres of the giant engineering machines.

Description

(1) Technical field: [0001] The invention relates to a tire repair rubber, in particular to a giant engineering machinery tire repair rubber and a preparation method thereof. (two) background technology: [0002] Giant off-road tires are mainly used in large-scale open-pit mines. Due to poor road conditions and harsh operating conditions, the crown and sidewall of giant off-road tires are easily cut and stabbed by sharp ore. In order to prevent early scrapping of giant off-road tires, the extension For the purpose of driving life of giant off-road tires, these wounds need to be repaired. According to the special use environment of giant off-road tires, the repair rubber itself is required to have wear resistance, low heat generation, excellent anti-aging performance, and good adhesion performance with giant off-road tires, so as to ensure The repaired giant OTR tires still have good performance. At present, there are few reports on tire repair rubber, especially tire repai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More