Retardation pumping type three-expansion source cement expansive material

A technology of expansion agent and retarding pump, applied in the field of concrete expansion agent, can solve the problems of insufficient synchronization of compensation and shrinkage, single expansion source, and many exposure problems, and achieves strong adaptability, low chloride ion content, and comprehensive physical performance improvement. Effect

Inactive Publication Date: 2012-07-11
广西云燕特种水泥建材有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still deficiencies in the composite expansion agents currently on the market: ①The expansion rate is low; ②The alkali content is high; ③The expansion source is single, and the compensation for shrinkage is not synchronized; The compatibility of the product is not good, and many problems are exposed when used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Retardation pumping type three-expansion source cement expansive material
  • Retardation pumping type three-expansion source cement expansive material
  • Retardation pumping type three-expansion source cement expansive material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] (1), the preparation process formula is shown in Table 1:

[0064] Table 1 (unit: kg)

[0065] Anhydrite

50

High alumina clinker

10

High Calcium Sulfur Aluminum Clinker

25

Calcined magnesite

3

water slag

12

Polycarboxylate superplasticizer (external mixing)

3.0

Sodium Gluconate (External Mix)

0.6

HPMC cellulose (external blend)

0.02

K12 air-entraining agent (external mixing)

0.04

[0066] (2) Preparation process:

[0067]

[0068] (3) The inspection data is shown in Table 2:

[0069] Table 2

[0070]

[0071]

Embodiment 2

[0073] (1), the preparation process formula is shown in Table 3

[0074] Table 3 (unit: kg)

[0075] Anhydrite (%)

55

High alumina clinker (%)

10

High calcium sulfur aluminum clinker (%)

30

Calcined magnesite (%)

2

Slag (%)

3

Polycarboxylate superplasticizer (external mixing) (%)

3.0

Sodium gluconate (additional) (%)

0.6

HPMC cellulose (external doping) (%)

0.02

K12 air-entraining agent (external mixing) (%)

0.04

[0076] (2), preparation process:

[0077]

[0078] (3) The inspection data is shown in Table 4:

[0079] Table 4

[0080]

[0081] Only two examples have been cited above, and the products prepared within the range of raw material ratio in actual production can meet the quality requirements.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a slow hardening pump deliver type three expansion source concrete expansion agent, which is characterized by comprising preparation of raw materials such as anhydrite, high alumina chamotte, high-calcium sulphoaluminate chamotte, calcined magnesite and so on by weight portion and externally doped slushing agent, water retention agent, air entraining agent and retardant. The preparation method of the expansion agent comprises steps of crushing, common mixture, mixing and grinding and external doping mixture and finish product forming. The product has low alkali content, excellent expansion performance, strong suitability with concrete, balanced mechanical property after hardening, and small gradual slump loss of concrete shrinkage compensation, contributes to improving safety and durability of reinforced concrete, obviously improves the cracking resistance, volume stability, impermeability and frost resistance, and is simple and convenient to use and easy to control quality in construction. The slow hardening pump deliver type three expansion source concrete expansion agent can meet construction use requirements of commercial concrete, long distance pump-delivering concrete and mass concrete.

Description

technical field [0001] The present invention relates to concrete, especially concrete expansive agent. technical background [0002] With the large-scale application of commercial and high-performance concrete in my country, the prominent contradiction is that the probability of cracks in concrete engineering increases, and harmful cracks are directly related to the durability of structures. Commercial housing has involved people's livelihood issues, and users have strongly responded to this. In recent years, the Ministry of Construction and engineering circles have attached great importance to the control of concrete cracks. From the material point of view, concrete expansion agent, shrinkage reducer, steel fiber and synthetic organic fiber are all effective measures to reduce or disperse cracks, but in terms of material price and construction convenience, expansion agent has more advantages. Academician Wu Zhongwei of my country pointed out that "micro-cracks to visible c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/38C04B24/10C04B22/14
CPCC04B2111/29C04B2111/00146C04B2111/34C04B2111/00293C04B2111/343C04B40/0039Y02W30/91C04B7/32C04B7/323C04B11/06C04B22/066C04B24/10C04B24/16C04B24/26C04B24/383C04B28/02C04B18/141
Inventor 李光达黄芳许建兴
Owner 广西云燕特种水泥建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More