Preparation method of high-strength impermeable concrete and impermeable concrete

An impermeable concrete and high-strength technology, applied in the field of impermeable concrete and high-strength impermeable concrete preparation, can solve the problems of limited waterproof and impermeability, high production process requirements, reduced water-cement ratio, etc. High efficiency of water seepage and water resistance, good anti-aging performance, and the effect of improving the compactness of concrete

Inactive Publication Date: 2020-04-21
江苏诚意智腾建材科技发展有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, reducing the water-cement ratio and selecting cement with appropriate varieties and strength grades ensures the construction quality, especially vibrating and compacting also plays an im

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A preparation method of high-strength anti-seepage concrete and the anti-seepage concrete are prepared from the following raw materials:

[0020] The raw materials include by weight: 30-50 parts of cement, 20-40 parts of water, 15-30 parts of fine sand, 30-50 parts of steel fiber, 0.3-0.6 parts of silica particles, 10-16 parts of ultra-fine slag, expansion 5-8 parts of active agent, 3-6 parts of active agent, 2-6 parts of water reducing agent, 3-6 parts of sodium alkylbenzene sulfonate, 1.1-1.6 parts of hydrophilic colloid and 10-25 parts of emulsifier.

[0021] Further, the emulsifier includes one of anionic emulsifier, cationic emulsifier and nonionic emulsifier.

[0022] A preparation method of high-strength anti-seepage concrete and anti-seepage concrete, comprising the following steps:

[0023] Step 1, dry mixing: Put 30-50 parts of cement, 15-30 parts of fine sand, 30-50 parts of steel fiber, 0.3-0.6 parts of silica particles, and 3-6 parts of sodium alkylbenzene...

Embodiment 2

[0030] A method for preparing high-strength impermeable concrete and the impermeable concrete, characterized in that: it is prepared from the following raw materials:

[0031] The raw materials include: 50 parts of cement, 40 parts of water, 30 parts of fine sand, 50 parts of steel fiber, 0.6 parts of silica particles, 16 parts of ultrafine slag, 8 parts of expansion agent, 6 parts of active agent, and water reducer 6 parts, 6 parts of sodium alkylbenzene sulfonate, 1.6 parts of hydrocolloid and 25 parts of emulsifier.

[0032] Further, the emulsifier includes one of anionic emulsifier, cationic emulsifier and nonionic emulsifier.

[0033] A preparation method of high-strength anti-seepage concrete and anti-seepage concrete, comprising the following steps:

[0034] Step 1, dry mixing: put 50 parts of cement, 30 parts of fine sand, 50 parts of steel fiber, 0.6 parts of silicon dioxide particles, and 6 parts of sodium alkylbenzene sulfonate into a mixer and dry mix until they a...

Embodiment 3

[0041] A preparation method of high-strength anti-seepage concrete and the anti-seepage concrete are prepared from the following raw materials:

[0042] The raw materials include by weight: 30 parts of cement, 20 parts of water, 15 parts of fine sand, 30 parts of steel fiber, 0.3 parts of silica particles, 10 parts of ultrafine slag, 5 parts of expansion agent, 3 parts of active agent, and water reducer 2 parts, 3 parts of sodium alkylbenzene sulfonate, 1.1 parts of hydrocolloid and 10 parts of emulsifier.

[0043] Further, the emulsifier includes one of anionic emulsifier, cationic emulsifier and nonionic emulsifier.

[0044] A preparation method of high-strength anti-seepage concrete and anti-seepage concrete, comprising the following steps:

[0045] Step 1, dry mixing: put 30 parts of cement, 15 parts of fine sand, 30 parts of steel fiber, 0.3 parts of silicon dioxide particles, and 3 parts of sodium alkylbenzene sulfonate into a mixer and dry mix until they are evenly mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of high-strength impermeable concrete and the impermeable concrete. The impermeable concrete is prepared from the following raw materials in parts by weight: 30-50 parts of cement, 20-40 parts of water, 15-30 parts of fine sand, 30-50 parts of steel fibers, 0.3-0.6 part of silicon dioxide particles, 10-16 parts of superfine slag, 5-8 parts of an expanding agent, 3-6 parts of an active agent, 2-6 parts of a water reducing agent, 3-6 parts of sodium alkyl benzene sulfonate, 1.1-1.6 parts of hydrophilic colloid and 10-25 parts of an emulsifier. The preparation method is simple, the prepared concrete is efficient and durable in impermeability and waterproofness, internal pores of the concrete can be filled, the compactness of the concrete is improved, steel bars in a concrete structure cannot be rusted, and the anti-aging performance is good.

Description

technical field [0001] The invention belongs to the technical field of concrete preparation, and in particular relates to a preparation method of high-strength impervious concrete and the impermeable concrete. Background technique [0002] Impermeability concrete is divided into P6, P8, P10, and P12 according to different impermeability pressures. Impermeable concrete improves the pore structure by increasing the compactness of the concrete, thereby reducing the permeation channels and improving the impermeability. The common way to produce impermeable concrete is to add air-entraining admixture to generate disconnected air bubbles inside the concrete, cut off the capillary channels, and change the pore structure, thereby improving the impermeability of the concrete. In addition, reducing the water-cement ratio and selecting cement with appropriate varieties and strength grades ensures the construction quality, especially vibrating and compacting also plays an important rol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00
CPCC04B28/00C04B2111/00293C04B2111/27C04B14/06C04B14/48C04B18/141C04B24/20C04B2103/302C04B2103/0068
Inventor 高旋胡兵孟文书周珂珂
Owner 江苏诚意智腾建材科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap