Production method of ultrahigh magnetic permeability of iron-based nanocrystalline magnetic powder core

A technology of iron-based nanocrystalline and magnetic powder cores, which is applied in the direction of magnetic materials, magnetic objects, and inorganic materials, can solve the problems of large gaps, difficulty in pressing and molding, and low magnetic permeability of nanocrystalline magnetic powder cores to achieve uniform composition , Accelerated passivation, beneficial to the effect of compression molding

Inactive Publication Date: 2014-04-23
QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
View PDF10 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, this method has the following defects: 1. The magnetic permeability of the obtained nanocrystalline magnetic powder core is still low, which cannot meet the requirements of the motor; The gap is large, it is difficult to press and form
[0008] In summary, there are no reports on nanocrystalline magnetic powder cores with a magnetic permeability of more than 200 and their preparation methods in the prior art; there are no reports in the prior art that can effectively solve the problem of large-particle nanocrystalline powder compression molding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The preparation method of the iron-based nanocrystalline magnetic powder core with ultrahigh magnetic permeability provided in this embodiment comprises the following steps:

[0029] In step 1, the iron-based nanocrystalline ribbon is mechanically pulverized to obtain iron-based nanocrystalline powder; the composition of the iron-based nanocrystalline ribbon is Fe 73.5 Cu 1 Nb 3 Si 13.5 B 9 ;

[0030] Step 2, the iron-based nanocrystalline powder is screened and proportioned, and then mixed into a coarse powder with a weight content of 40 to 80% passing through -40 to +100 mesh and a weight content of 20 to 60%. - Mixed powders consisting of fine powders of 325 mesh;

[0031] Step 3: passivate, couple, insulate and coat the mixed powder sequentially using a passivating agent, coupling agent, insulating agent and binder respectively, and then press molding; the coupling agent uses titanate ; The passivator uses water; the insulating agent uses low-melting glass pow...

Embodiment 2

[0042] The preparation method of the iron-based nanocrystalline magnetic powder core with ultrahigh magnetic permeability provided in this embodiment comprises the following steps:

[0043] In step 1, the iron-based nanocrystalline ribbon is mechanically pulverized to obtain iron-based nanocrystalline powder; the composition of the iron-based nanocrystalline ribbon is Fe 73.5 Cu 1 Nb 3 Si 13.5 B 9 ;

[0044] Step 2, the iron-based nanocrystalline powder is screened and proportioned, and then mixed into coarse powder with a weight content of 60% passing through -40~+100 mesh and a weight content of 40% passing through -325 mesh Mixed powder composed of fine powder;

[0045] Step 3: passivate, couple, insulate and coat the mixed powder sequentially using a passivating agent, coupling agent, insulating agent and binder respectively, and then press molding; the coupling agent uses titanate ; The passivator uses water; the insulating agent uses low-melting glass powder; the b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of alloy soft magnetic powder cores and particularly relates to a production method of an ultrahigh magnetic permeability of iron-based nanocrystalline magnetic powder core. The production method comprises step 1, performing mechanical crushing treatment on an iron-based nanocrystalline thin belt so as to obtain iron-based nanocrystalline powder; step 2, screening and matching the iron-based nanocrystalline powder and mixing into mixed powder which is formed by coarse powder and fine powder; step 3, performing passivation, coupling and insulation coating treatment on the mixed powder in turn through a passivation agent, a coupling agent, an insulating agent and a binding agent and performing compression forming; step 4, performing annealing treatment and spraying insulation treatment on the formed magnetic powder core in turn. According to the production method of the ultrahigh magnetic permeability of iron-based nanocrystalline magnetic powder core, the coarse powder and fine powder mixing and coupling treatment is adopted and accordingly the problem of the compression forming of large particle nanocrystalline powder can be effectively solved and the ultrahigh magnetic permeability of iron-based nanocrystalline magnetic powder core can be produced, wherein the magnetic permeability can reach more than 200.

Description

technical field [0001] The invention belongs to the technical field of alloy soft magnetic powder cores, and in particular relates to a preparation method of an iron-based nanocrystalline magnetic powder core with ultrahigh magnetic permeability. Background technique [0002] With the development of the electronics industry, a large number of applications of various switching power supplies require a magnetic powder core with high magnetic permeability, low loss, and good AC-DC superposition performance at a frequency of 10kHz-200kHz to make an inductor core, which is generally made of sendust aluminum alloy. The iron core is also called alloy magnetic powder core, and its relative magnetic permeability does not exceed 200 at the highest. For example, the Chinese invention patent application CN 101090019 A "Manufacturing method of high magnetic permeability FeSiAl magnetic powder core" discloses a magnetic permeability of 150 The manufacturing method of FeSiAl magnetic powde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/147H01F1/22B22F1/00B22F1/02
Inventor 王亚娜江志滨纪杰李维强
Owner QINGDAO YUNLU ADVANCED MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap