Aluminum alloy wires, wires, cables and harnesses

An aluminum alloy wire and wire technology, applied in the field of wire harnesses, can solve problems such as insufficient single wire strength of alloy wires

Inactive Publication Date: 2017-05-10
YAZAKI CORP
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when this alloy wire is used as a conductor for an aluminum electric wire thinner than the above-mentioned size of 0.75sq, there is a concern that the single wire strength of this alloy wire is insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy wires, wires, cables and harnesses
  • Aluminum alloy wires, wires, cables and harnesses
  • Aluminum alloy wires, wires, cables and harnesses

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0058] Hereinafter, the aluminum metal wire of the present invention will be described more specifically by showing operational examples.

[0059]

[0060] Magnesium and silicon were blended with aluminum to have a blending ratio of each of Examples 1 to 9 and Comparative Examples 1 to 4 in Table 1, and the blend was melted in a crucible and then poured into a mold. In this way, each ingot is formed.

[0061]

[0062] Each ingot was machined to predetermined dimensions using a roller press and a wire drawing machine to form two rolled material samples, one of which had a wire diameter of 18 mm (for rolling to a 99.9% reduction in cross-sectional area, which will be later described), and the other has a wire diameter of 3.2 mm (for rolling to 99% reduction in cross-sectional area, which will be described later). This step and the steps preceding it can be performed using continuous casting and rolling machines and wire drawing machines.

[0063]

[0064] Each rolled and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
sizeaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

As a small-diameter conductor for electric wires for automobiles, provided is an aluminum alloy wire satisfying all requests of sufficient strength, elongation and electroconductivity. The wire is an aluminum alloy wire including: magnesium; silicon; and aluminum and inevitable impurities as the balance, the content (M) by atomic percentage (at%) of the magnesium in the wire and the content (S) by atomic percentage (at%) of the silicon satisfying the following expressions (1) and (2), a metallic microstructure of a cross section of the wire having an average crystal grain size of 3 to 20 µm or less, a precipitation size of the metallic microstructure in the cross section being 100 nm or less, and the number density of the precipitations in the cross section being one or more per square micrometer. [Mathematical Formula 1] 0.2 ‰¤ M ‰¤ 1.19 and - 0.81 �¢ M + 1.44 ‰¤ S ‰¤ - 1.54 �¢ M + 2.31

Description

technical field [0001] The present invention relates to an aluminum alloy wire, an electric wire and a cable respectively using the aluminum alloy wire as a conductor, and a wire harness. Background technique [0002] Regarding an aluminum alloy wire used as a conductor, Patent Document 1 discloses an aluminum alloy wire whose composition includes 0.2% to 1.0% of Mg, 0.1% to 1.0% of Si, and 0.1% or more to less than 0.5% Cu, and including Al and other impurities, wherein the mass ratio of Mg / Si satisfies the following formula: 0.8≤Mg / Si≤2.7. [0003] When this alloy wire is produced through the process of "casting (continuous casting or billet casting), rolling, melt treatment, aging treatment, wire drawing and final heat treatment", the alloy wire can be produced to have a tensile strength of 120 to 200MPa Aluminum alloy wire with strength, elongation above 10%, conductivity above 58% IACS, and diameter from 0.2 to 1.5mm. [0004] Among such technologies, due to recent de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22F1/04H01B1/02H01B5/02H01B7/00C22F1/00
CPCH01B1/023C22C21/02C22C21/08C22F1/04C22F1/043C22F1/047H01B7/0045
Inventor 后藤润大
Owner YAZAKI CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap