A kind of modified bamboo charcoal fiber-rubber composite shoe sole material and its preparation method and application

A technology of bamboo charcoal fiber and composite shoe sole, which is applied in the field of materials, can solve the problems of high density and serious dust pollution in the processing process, and achieve the effects of increasing tensile strength, improving compatibility, and improving interface adhesion

Active Publication Date: 2019-07-19
贝克兰(厦门)新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the technical problems in the prior art that the sole material is filled with inorganic reinforced composite materials, resulting in high density and serious dust pollution during processing, and to provide a lightweight and environmentally friendly The shoe sole material, through the modification of bamboo charcoal fiber, solves the technical bottleneck problem of interfacial compatibility between bamboo charcoal fiber and shoe sole matrix material and the dispersibility of bamboo charcoal fiber in shoe sole material, provides a kind of modified bamboo charcoal fiber-rubber The composite shoe sole material and its preparation method make the bamboo charcoal fiber easily disperse in the processing process and form a stable, firm and uniform interface layer. The composite shoe sole material and its products obtained in the present invention can be used as the shoe sole material, and have lighter weight, and The characteristics of excellent mechanical properties can meet the needs of lightweight and low cost required by new shoe soles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified bamboo charcoal fiber-rubber composite shoe sole material and its preparation method and application
  • A kind of modified bamboo charcoal fiber-rubber composite shoe sole material and its preparation method and application
  • A kind of modified bamboo charcoal fiber-rubber composite shoe sole material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Present embodiment adopts maleic anhydride to carry out modification to bamboo charcoal fiber according to the following steps, makes maleic anhydride modified bamboo charcoal fiber, and step comprises:

[0035] S1. Weighing: Weigh the bamboo charcoal fiber and maleic anhydride according to the ratio of parts by weight of 1:1-1:2.

[0036] S2, the preparation of modifying agent: the maleic anhydride taken in the step (S1) is completely dissolved in the DMF solvent; Simultaneously take xylene according to 6-8 times of maleic anhydride weight, and add to maleic anhydride - In the DMF solution, all the components are dissolved under stirring conditions to obtain a modifier solution.

[0037] S3, bamboo charcoal fiber modification: adding the bamboo charcoal fiber weighed in step (S1) to the modifier solution obtained in step (S2), this step is stirred and modified at 30°C, and the reaction time is 4h; Suction filtration is carried out after the reaction is finished, and t...

Embodiment 2

[0040] The present embodiment adopts silane coupling agent to modify bamboo charcoal fiber according to the following steps to obtain silane coupling agent modified bamboo charcoal fiber. The steps include:

[0041] S1. Surface passivation treatment of bamboo charcoal fibers: soak the dried bamboo charcoal fibers in a sufficient amount of NaOH solution with a mass concentration of 10% for 48 hours, take out the soaked bamboo charcoal fibers and dry them at 105°C to obtain bamboo charcoal fibers Pre-processing material.

[0042] S2, the preparation of coupling modification liquid: according to the weight ratio of silane coupling agent and bamboo charcoal fiber is 1: 30-1: 40, take silane coupling agent KH570 and dissolve in absolute ethanol, the obtained silane coupling agent is in The concentration in absolute ethanol is 2.5%-3.5% to obtain a coupling modification solution.

[0043] S3. Coupling modification of bamboo charcoal fiber: soak the bamboo charcoal fiber pretreatmen...

Embodiment 3

[0045] The sole material of the present embodiment is mainly formulated by the raw material of following weight portion: 30 parts of the maleic anhydride modified bamboo charcoal fiber that make with embodiment 1, other components are as follows: 50 parts of butadiene rubber, 50 parts of styrene-butadiene rubber , 30 parts of maleic anhydride modified bamboo charcoal fiber, 1.5 parts of sulfur, 3 parts of zinc oxide, 1 part of stearic acid, and 1.5 parts of accelerator TMTD.

[0046] In the preparation of the above-mentioned maleic anhydride modified bamboo charcoal fiber, the weight ratio of bamboo charcoal fiber, maleic anhydride and xylene is 1:2:14.

[0047] The preparation method of present embodiment raw material, realizes by following steps:

[0048] (1) Weighing: Weigh the above raw materials in parts by weight.

[0049] (2) Mixing: Mix the above-mentioned combined rubber weighed in the step (1) in an open mill to mix evenly. In this step, the operating parameters of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified bamboo charcoal fiber and rubber composite material, a preparation method therefor and an application of the modified bamboo charcoal fiber and rubber composite material. The composite material is prepared from the following ingredients in parts by weight: 100 parts of natural rubber, cis-butadiene rubber and styrene-butadiene rubber blended rubber, 15-35 parts of modified bamboo charcoal fibers, 1.2-3.3 parts of sulfur, 2.5-4 parts of zinc oxide, 0.9-1.3 parts of stearic acid and 1.2-2 parts of accelerant TMTD. The preparation method comprises the steps of using the natural rubber, cis-butadiene rubber and styrene-butadiene rubber blended rubber as a raw material, carrying out milling and plastifying on the modified bamboo charcoal fibers, processing aids and the blended rubber in mixing and milling procedures of the raw material, and carrying out procedures such as vulcanization, thereby preparing a modified bamboo charcoal fiber containing rubber composite material and products. The composite material and the products thereof, prepared by the method, can serve as a shoe sole material and can meet the requirements of novel shoe soles on light weight and low cost.

Description

[0001] Technical field: [0002] The invention relates to the field of materials, in particular to a bamboo charcoal fiber-rubber composite sole material and a manufacturing method thereof. [0003] Background technique: [0004] With the rapid development of the footwear industry, sole materials are mainly developed in terms of light weight and environmental protection. Most of the traditional shoe sole materials are prepared by adding inorganic substances to strengthen composite materials. However, the shoe sole materials prepared by this method have disadvantages such as high density and heavy dust pollution during processing, while plant fibers have low density compared to inorganic fillers. The advantages of being biodegradable and easy to recycle can solve the shortcomings in the application process of inorganic fillers. The interface compatibility between plant fiber and sole matrix material and the dispersion of plant fiber in sole material are the bottlenecks that res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L9/00C08L9/06C08L7/00C08L67/00C08K13/02C08K3/04D06M13/203D06M13/513A43B13/02D06M101/32
CPCA43B13/026C08L9/00C08L9/06C08L2205/03C08L2205/035C08L2205/16D06M13/203D06M13/5135D06M2101/32C08L67/00C08K13/02C08K3/04C08L7/00
Inventor 曾安蓉张青海李云龙汪扬涛余梓铭
Owner 贝克兰(厦门)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com