A356.2 cast aluminum alloy and its pre-furnace adding titanium method

A technology of casting aluminum alloy and front furnace, which is applied in the field of aluminum alloy preparation, can solve the problems of large fluctuation of titanium element, prolonged production time, low actual yield of titanium agent, etc., so as to improve the actual yield and the actual yield , to avoid the effect of insufficient melting

Active Publication Date: 2021-03-16
YUNNAN YONGXIN ALUMINUM
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usually, after the electrolytic aluminum liquid is completely poured into the smelting furnace, it is necessary to heat up the furnace, and when the temperature reaches above 820°C, the titanium agent is then put into the furnace. This addition method has the following disadvantages: (1) Before adding the titanium agent, it needs to consume a lot of energy to heat up the molten aluminum in the furnace, which increases the cost; (2) the heating process prolongs the production time and reduces the efficiency; (3) after the titanium agent is added into the furnace, it needs to be fully stirred. Ensure uniform melting of the titanium agent and increase the labor load; (4) When the temperature is not enough and the stirring is insufficient, the unmelted titanium agent is easy to sink to the bottom. When the next batch of A356.2 cast aluminum alloy is produced, if the melting If the temperature is higher than the upper limit, the titanium agent that sinks to the bottom will melt, causing the titanium content of the furnace to increase, and resulting in large fluctuations in the titanium element in multiple batches of A356.2 cast aluminum alloy products; (5) The titanium agent is actually received The rate is low, and the cost of titanium agent is high, resulting in an increase in product cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A356.2 cast aluminum alloy and its pre-furnace adding titanium method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] Embodiments of the present invention are described in detail below, examples of which are shown in the drawings, wherein the same or similar reference numerals designate the same or similar elements or elements having the same or similar functions throughout. The embodiments described below by referring to the figures are exemplary and are intended to explain the present invention and should not be construed as limiting the present invention.

[0021] In one aspect of the present invention, the present invention proposes a method for adding titanium to an A356.2 cast aluminum alloy pre-furnace. According to an embodiment of the present invention, refer to figure 1 , the method includes:

[0022] S100: Preheating the titanium agent

[0023] In this step, the titanium agent is preheated so as to obtain the preheated titanium agent. The inventor found that by preheating the titanium agent, the influence of the titanium agent in the subsequent pre-furnace on the temperatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses A356.2 casting aluminum alloy and a method for adding titanium into a pre-furnace for the A356.2 casting aluminum alloy. The method comprises the steps of 1, preheating a titanium agent; 2, heating A356.2 electrolytic raw molten aluminum to the temperature not lower than 840 DEG C; 3, pumping the A356.2 electrolytic raw molten aluminum obtained in step 2 into the pre-furnace through a siphon, and meanwhile, supplying the titanium agent obtained after preheating of step 1 into the pre-furnace so that titanium-added molten aluminum can be obtained; and 4, smelting the titanium-added molten aluminum so that the A356.2 casting aluminum alloy can be obtained. Compared with the traditional A356.2 casting aluminum alloy smelting operation titanium agent adding process, bymeans of the method, the temperature raising process implemented before the titanium agent is added is omitted; the phenomenon that the titanium agent is not molten completely, so that the titanium agent sinks to the bottom is reduced; fluctuation of the titanium element is reduced; and the casting yield of the titanium agent is increased by 10%, and energy and time are saved.

Description

technical field [0001] The invention belongs to the field of aluminum alloy preparation, specifically, the invention relates to A356.2 cast aluminum alloy and a method for adding titanium in a pre-furnace. Background technique [0002] Titanium is a commonly used additive element in A356.2 cast aluminum alloy, and it is added in the form of Al-Ti or Al-Ti-B master alloy. Titanium and aluminum form TiAl 2 phase, which becomes the non-spontaneous core during crystallization, and plays a role in refining the cast structure and weld structure. In production practice, the titanium agent is added into the furnace in the form of titanium agent. Since the titanium agent needs to be fully melted at a relatively high temperature, it is necessary to ensure that the titanium agent is fully melted and has a high yield when the temperature in the furnace reaches above 820°C. Rate. Usually, after the electrolytic aluminum liquid is completely poured into the smelting furnace, it is nece...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/03C22C1/06C22C21/02
Inventor 杨国荣邹学通苏其军王建平臧永伟罗映东戴晓毅李顺华孙海艳季鹏辉
Owner YUNNAN YONGXIN ALUMINUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products