Negative ion water-based coating and preparation method thereof

A water-based paint and negative ion technology, applied in the field of paint, can solve the problems of destroying charge balance, agglomeration, affecting the uniformity of the dispersion of negative ion components, and achieve the effect of good negative ion release effect.

Inactive Publication Date: 2020-08-14
吴佰川 +1
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, the negative ion component itself has electric polarity, and it is easy to interact with other materials, thereby destroying the charge balance, causing agglomeration, and affecting the dispersion uniformity of the negative ion component.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Negative ion water-based coating and preparation method thereof
  • Negative ion water-based coating and preparation method thereof
  • Negative ion water-based coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0076] Embodiment 2 and comparative example 2 raw material ratio as shown in table 2, prepared is negative ion water-based wood finish.

[0077] Table 2

[0078]

[0079]

[0080] The present embodiment and comparative example comprise the following steps:

[0081] The first step is to accurately weigh component 1, and add the premixed components 2-7 groups under the 300-rpm stirrer to stir, and maintain the stirring speed at 300 rpm;

[0082] In the second step, adjust the rotation speed to 400 rpm, add the diluted components of components 8 and 9, and defoam at a slow speed for 10 minutes.

[0083] In this embodiment and comparative example, the pH value of coating remains between 7-8, and aqueous polyurethane dispersion is detected by molecular detector, and molecular particle size is at 6-8 micron, and Guanyin bamboo is through 2000 revolutions in embodiment 2 High-speed friction, detected by a molecular detector, the molecular particle size is in the range of 6-8 ...

Embodiment 3

[0084] Embodiment 3 Raw material ratio is as shown in table 3, prepared is negative ion water-based sealing primer.

[0085] table 3

[0086]

[0087]

[0088] This embodiment includes the following steps:

[0089] The first step is to accurately weigh 1 component, add 2-8 components under the condition of 400 rpm stirring, adjust to 1000 rpm and stir for 5 minutes;

[0090] In the second step, add components 9-11 and stir for 10 minutes under the stirring condition of 400 rpm;

[0091] In the third step, 12 components are added to adjust the viscosity.

[0092] In this embodiment, the pH value of the coating remains between 7-8, and the acrylic polyester emulsion is detected by a molecular detector, and the molecular particle size is within the range of 6-8 microns. Speed ​​friction, detected by molecular detector, the molecular particle size is in the range of 6-8 microns, the main performance indicators of embodiment 3: solid content 35%, viscosity 65MPa.s, negativ...

Embodiment 4

[0093] Example 4 Raw material ratio as shown in Table 4, prepared is negative ion water-based matt finish for woodware.

[0094] Table 4

[0095]

[0096]

[0097] The preparation method is as follows:

[0098] The first step is to accurately weigh 1 component and add 2-8 under the condition of stirring at 400 rpm to stir evenly for 10-20 minutes;

[0099] In the second step, under the stirring condition of 800 rpm, add 9-12 components and stir evenly for 15 minutes;

[0100] In the third step, add 13 to adjust the viscosity (MPa.s) under the stirring condition of 300 rpm.

[0101] In this embodiment, the pH value of the coating remains at 7-8, and the acrylic polyester emulsion is detected by a molecular detector. Detected by a molecular detector, the molecular particle size is in the range of 6-8 microns, the main performance indicators of embodiment 4: solid content 40%, viscosity 70MPa.s, gloss (60 °) is 20, negative ion release (1 cubic m square warehouse) 14000...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

Negative ion water-based coating is provided. The coating well achieves dissolution and dispersion of a negative ion additive in the water-based coating and a better negative ion release effect is achieved.

Description

technical field [0001] The invention belongs to the technical field of coatings, and relates to a negative ion water-based coating and a preparation method thereof. Background technique [0002] Water-based paint uses water instead of traditional organic solvents as the main solvent or dispersion medium, and its water content is about 20% to 50%. Water is used as the diluent, that is, water is used as the medium, and it does not contain toxic heavy metals such as benzene, formaldehyde, and free TDI. [0003] In recent years, water-based paint, as an energy-saving, environmentally friendly, green and safe clean paint, has received more and more attention and attention in various industries in our country. [0004] Water-based coatings are widely favored mainly because of their following advantages: [0005] (1) The main raw material used to produce water-based coatings is renewable energy. Water-based paint contains more than half of water. Water is a clean and renewable e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D133/04C09D7/40
CPCC09D7/40C09D7/69C09D133/04C09D175/04
Inventor 吴佰川李伟
Owner 吴佰川
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products