A kind of heat-sensitive type film-forming resin for exempting CTP plate and preparation method thereof

A film-forming resin and treatment-free technology, applied in the field of materials, can solve the problems of poor heat resistance, affecting the quality of offset printing CTP plates, limiting the development of offset printing CTP plates, etc., to achieve the effect of increasing melting point, weakening thermal motion, and small weight loss

Active Publication Date: 2022-02-18
安徽强邦新材料股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the above-mentioned technical problems, the object of the present invention is to provide a kind of heat-sensitive type film-forming resin and preparation method thereof for exempting from processing CTP plate: by adding epoxy resin to a constant pressure dropping funnel, magnetic stirrer , a thermometer, an air guide tube and a four-necked flask with a condenser tube, then add a mixed solvent, pass through nitrogen protection, heat up and stir until the epoxy resin is completely dissolved, and obtain a reaction solution a, add the initiator to the mixed solvent, and ultrasonically stir to make It is completely dissolved to obtain the reaction solution b, which is added to the constant pressure dropping funnel, and added dropwise to the reaction solution a to obtain the intermediate product A, and then the modifier is added to the four-necked flask, and the temperature is raised Heating and constant temperature reaction, the reaction product is subjected to a rotary evaporation operation to remove the solvent, and a heat-sensitive film-forming resin for a treatment-free CTP plate is obtained, which solves the problem of poor heat resistance of the existing heat-sensitive film-forming resin for a treatment-free CTP plate. The quality of offset printing CTP plates limits the development of offset printing CTP plates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of heat-sensitive type film-forming resin for exempting CTP plate and preparation method thereof
  • A kind of heat-sensitive type film-forming resin for exempting CTP plate and preparation method thereof
  • A kind of heat-sensitive type film-forming resin for exempting CTP plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Present embodiment is a kind of modifying agent, and the preparation method of described modifying agent comprises the following steps:

[0044]S1: Add the mixed acid into a three-necked flask equipped with a stirrer, a thermometer and a constant pressure dropping funnel, add 1,3,5-trifluorobenzene into the constant pressure dropping funnel, and stir at a temperature of 60°C Add 1,3,5-trifluorobenzene dropwise into the three-necked flask at a speed of 100r / min, and control the dropping rate at 1 drop / s. After the dropwise addition, raise the temperature to 68°C and continue stirring at a constant temperature for 2h After the reaction, the reaction product was washed 3 times successively with deionized water, sodium hydroxide solution and deionized water, and suction filtered to obtain intermediate 1; the mixed acid was controlled to be 65% concentrated nitric acid and mass fraction The concentrated sulfuric acid that fraction is 98% is according to the mixture that volu...

Embodiment 2

[0050] Present embodiment is a kind of modifying agent, and the preparation method of described modifying agent comprises the following steps:

[0051] S1: Add the mixed acid into a three-necked flask equipped with a stirrer, a thermometer and a constant pressure dropping funnel, add 1,3,5-trifluorobenzene into the constant pressure dropping funnel, and stir at a temperature of 62°C. Add 1,3,5-trifluorobenzene dropwise into the three-necked flask at a speed of 150r / min, and control the dropping rate at 1 drop / s. After the dropwise addition, raise the temperature to 70°C and continue the constant temperature stirring reaction for 2.5 h, after the reaction finishes, the reaction product is washed 4 times successively with deionized water, sodium hydroxide solution, and deionized water, and suction filtered to obtain intermediate 1; the mixed acid is controlled to be concentrated nitric acid with a mass fraction of 65% and The concentrated sulfuric acid that mass fraction is 98% ...

Embodiment 3

[0057] Present embodiment is a kind of modifying agent, and the preparation method of described modifying agent comprises the following steps:

[0058] S1: Add the mixed acid into a three-necked flask equipped with a stirrer, a thermometer and a constant pressure dropping funnel, add 1,3,5-trifluorobenzene into the constant pressure dropping funnel, and stir at a temperature of 65°C Add 1,3,5-trifluorobenzene dropwise into the three-necked flask at a speed of 200r / min, and control the dropping rate at 1 drop / s. After the dropwise addition, raise the temperature to 72°C and continue stirring at a constant temperature for 3h After the reaction, the reaction product was washed 5 times successively with deionized water, sodium hydroxide solution, and deionized water, and suction filtered to obtain intermediate 1; the mixed acid was controlled to be 65% concentrated nitric acid and mass fraction The concentrated sulfuric acid that fraction is 98% is according to the mixture that vo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat-sensitive film-forming resin for a treatment-free CTP plate and a preparation method thereof, and relates to the field of materials. The epoxy resin is added into a four-necked flask, then a mixed solvent is added, and nitrogen protection is introduced, and the temperature is raised and stirred. Until the epoxy resin is completely dissolved, the reaction liquid a is obtained, the initiator is added to the mixed solvent, and the ultrasonic stirring is used to dissolve it completely, and the reaction liquid b is obtained, and the reaction liquid b is added to the constant pressure dropping funnel, and added dropwise In the reaction solution a, the intermediate product A is obtained, and then the modifier is added to the four-necked flask, heated and reacted at a constant temperature, and the reaction product is subjected to a rotary evaporation operation to obtain the heat-sensitive film-forming resin; by modifying The benzene ring and C-F bond in the agent are introduced into the epoxy resin molecular chain. The introduction of the benzene ring increases the rigidity of the molecular chain and weakens the thermal movement of the molecule. The introduced C-F bond has high bond energy and high stability. , thereby improving the heat resistance of epoxy resin.

Description

technical field [0001] The invention relates to the field of materials, in particular to a heat-sensitive film-forming resin for a treatment-free CTP plate and a preparation method thereof. Background technique [0002] With the development of key technologies such as information and manufacturing, pre-press plate-making is making every effort to popularize computer-to-plate (Computer To Plate, CTP). Computer-to-plate-making refers to the technology of inputting the original information into the computer for processing, and then directly outputting the information to the printing plate through computer control. The information on the electronic layout is transmitted to the printing plate, and the technology for printing the printing plate is obtained directly. Offset printing CTP plates mainly include photosensitive plates, heat-sensitive plates and inkjet plates according to the imaging mechanism, among which heat-sensitive plates occupy a dominant position in the market. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/10C08F212/34C07D265/16
CPCC08F283/10C07D265/16
Inventor 孙长义郭俊成李长华
Owner 安徽强邦新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap