Tetrafluoroethylene composite teeth sealing gasket and method for making same

A technology of sealing gasket and tetrafluoro gasket, which is applied in the direction of engine sealing, engine components, mechanical equipment, etc., can solve the problems of poor corrosion resistance, low operating pressure, hard surface of tooth-shaped gasket, etc., and achieves high surface requirements. condition, easy sealing properties, effect of reducing cold flow

Inactive Publication Date: 2007-03-07
ZHEJIANG UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The original PTFE gasket has cold flow phenomenon, and the working pressure is low, less than 5.0MPa. When the diameter of the gasket is large, it is less than 2.0MPa. The working temperature is usually below 150°C, while the toothed gasket has a hard surface and poor corrosion resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tetrafluoroethylene composite teeth sealing gasket and method for making same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0018] Reactor gasket Φ900xΦ950x3, operating pressure 5.0Mpa, temperature 40°C~-196°C, the original use of PTFE gaskets, when the pressure is 2MPa, there will be leakage, but after using metal winding gaskets, when the temperature is above -50°C , The seal is good, but when it is below -50 ° C, it will leak, and there is metal influence on the catalyst. After switching to high-pressure PTFE composite tooth-type sealing gasket, the seal is good, and it has no effect on the catalyst.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

This invention discloses a tetrafluoro complex sealed shim and its facture. In the shim is embedded with the mental tooth-shaped shim, the colophony around is suppressed and sintered under the high temperature from 370 deg. C to 430 deg. C. it makes use of the high pressure of the tooth-shaped shim, the causticity of tetrafluoro and the easily sealing of the surface to reduce the cold flow of tetrafluoro and the high requirements of the surface of the shim. This invention is suitable for high pressure and strong causticity; it seals well in the cycling temperature and pressure fluctuation. It is used in the temperature from minus 210 deg. C to 250 deg. C, the pressure from 4.0 MPa to 42.0 MPa, in the fields of medical chemistry, FI chemistry, deep cooling, and oil chemistry.

Description

technical field [0001] The invention relates to a tetrafluoro compound tooth-type sealing gasket and a manufacturing method thereof. Background technique [0002] The original PTFE gasket has cold flow phenomenon, and the working pressure is low, less than 5.0MPa. When the diameter of the gasket is large, it is less than 2.0MPa. The working temperature is usually below 150°C, and the toothed gasket has a hard surface and poor corrosion resistance. Contents of the invention [0003] The purpose of the present invention is to provide a tetrafluoro composite tooth-type sealing gasket and its manufacturing method, which can expand the application range of the tetrafluoro gasket, especially under high pressure and medium temperature conditions. [0004] The technical scheme that the present invention adopts is as follows: [0005] 1. PTFE composite tooth gasket: [0006] There are metal toothed pads embedded in the PTFE gasket. [0007] The two ends of the metal tooth pad ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16J15/12
Inventor 邵君平汪希萱
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com