Silane cross-linked polyethylene insulation silver gray electric wire and cable and preparation method thereof

A polyethylene insulation, wire and cable technology, applied in the direction of insulated cables, insulated conductors, organic insulators, etc., can solve the problems of large gaps, achieve high insulation resistance, improve mechanical properties, and uniform glue production

Inactive Publication Date: 2016-12-07
浙江太湖远大新材料股份有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As we all know, in the industry, the temperature grade of 105°C and below can meet the requirements no matter whether XLPE, XLPVC or PVC is used. Above 150°C, the application of silicone rubber, fluoroplastics, polyimide and other varieties has also matured, but in the middle temperature grade (such as 125°C, 150°C) application development, there is a big gap with foreign countries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silane cross-linked polyethylene insulation silver gray electric wire and cable and preparation method thereof
  • Silane cross-linked polyethylene insulation silver gray electric wire and cable and preparation method thereof
  • Silane cross-linked polyethylene insulation silver gray electric wire and cable and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A silane crosslinked polyethylene insulating material silver-gray wire and cable, the silver-gray wire and cable includes an insulating material and a wire, and the insulating material is prepared from the following components by weight percentage:

[0045]

[0046]

[0047] and catalyst masterbatch;

[0048] Described catalyst masterbatch is made of following component:

[0049]

[0050] The two-step method for preparing the above-mentioned silane cross-linked polyethylene insulating material mainly consists of two parts, one is the preparation of the catalyst masterbatch, and the other is the preparation of the finished product.

[0051] 1. Catalyst masterbatch preparation:

[0052] Stir the above materials in a mixer, stirring at a low speed for 1 minute and then stirring at a high speed for 3 minutes, then release it and pour it into the hopper of the extruder (extruder temperature: 140-180°C), extrude through the twin-screw, and then pass through the cool...

Embodiment 2

[0062] A silane crosslinked polyethylene insulating material silver-gray wire and cable, the silver-gray wire and cable includes insulating materials and wires, and the insulating material is prepared from the following components by weight percentage:

[0063]

[0064] and catalyst masterbatch;

[0065] Described catalyst masterbatch is made of following component:

[0066]

[0067] The insulating material mentioned above was prepared by the two-step method of Example 1.

Embodiment 3

[0069] A silane crosslinked polyethylene insulating material silver-gray wire and cable, the silver-gray wire and cable includes insulating materials and wires, and the insulating material is prepared from the following components by weight percentage:

[0070]

[0071] and catalyst masterbatch;

[0072] Described catalyst masterbatch is made of following component:

[0073]

[0074]

[0075] The one-step method for preparing the above-mentioned silane cross-linked polyethylene insulating material mainly consists of two parts, one is the preparation of the catalyst masterbatch, and the other is the preparation of the finished product.

[0076] 1) Catalyst masterbatch preparation: Stir the above catalyst masterbatch materials in a mixer, first stir at a low speed for 1 minute, then stir at a high speed for 3 minutes, then pour them into the hopper of the extruder, the temperature of the extruder: 140-180°C, After the screw is extruded, it is cooled in a cooling water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of insulation wires and cables, in particular to a silane cross-linked polyethylene insulation silver gray electric wire and cable and a preparation method thereof. The silver gray electric wire and cable comprises an insulation material and a wire, wherein the insulation material is prepared from the following components: LLDPE-7042, LDPE, a silane coupling agent, a cross-linking agent DCP, an antioxidant 300 and a catalyst masterbatch, and the catalyst masterbatch is prepared from the following components: LLDPE-7042, LLDPE-8320, PP, an antioxidant 1010, an antioxidant DLTP, an antioxidant 1024, organic tin, a fluorine rubber masterbatch, a UV absorber and a silver gray masterbatch. The insulation material provide by the invention is mainly used for replacing the existing PVC material, and the insulation property is better than that of PVC; the PVC emits toxic and harmful gases when the electric wire is on fire due to aging and the like, while the silane insulation material is non-toxic and harmless.

Description

technical field [0001] The invention relates to the field of insulating material wires and cables, in particular to a silver-gray wire and cable made of a silane crosslinked polyethylene insulating material and a preparation method thereof. Background technique [0002] The types of polyolefins used in the cable industry mainly include PE, PP, EVA and EEA, etc. Among them, the relatively large amount and long application history are mainly PE, which include HDPE, MDPE, LDPE, LLDPE and cross-linked XLPE. Their application Needless to say. The current application and development trends of polyolefins in the industry mainly focus on the following aspects: [0003] (1) Serialization and perfection of halogen-free and low-smoke materials [0004] Halogen-free, low-smoke, flame-retardant cable materials have been developing rapidly in recent years, and thermoplastic materials that meet the requirements of the IEC92-359 standard have been more and more widely used. With the requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L23/12C08L27/12C08K5/14C08K5/134H01B3/44H01B7/28
CPCY02A30/14C08L23/06C08J3/226C08J2323/06C08J2423/08C08L2201/08C08L2203/202C08L2205/025C08L2205/035C08L2207/066H01B3/441H01B7/28C08L23/0815C08L23/12C08L27/12C08K5/14C08K5/1345
Inventor 赵勇李顺利俞丽琴蔡煜明李学贵
Owner 浙江太湖远大新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com