Organic and inorganic complex finishing varnish

Abstract

The invention provides an organic and inorganic complex finishing varnish. An inorganic photocatalysis material is added into a complex organic liquid of silica sol and an elastic acrylic emulsion so as to form an organic and inorganic complex finishing varnish main-body material. The silica sol is added into the emulsion-formed film. Through compounding of the silica sol and the self-crosslinking emulsion, an organic and inorganic complex paint film is formed. The organic and inorganic complex paint film has hardness and density of silica sol and will not generate static charge. No pollutants will adhere to the paint film. Meanwhile, the elastic emulsion endows the paint film with flexibility, and the whole paint film is soft. Thus, the finishing varnish with good dispersity, high surface hardness and excellent anti-pollution performance is obtained.

Description

technical field

[0001] The invention relates to an organic-inorganic composite finish varnish, which is suitable for the field of decoration and protection of inner and outer walls of buildings. Background technique

[0002] In exterior wall architectural coatings, the proportion of water-based coatings is originally greater. The construction technology and coating formula of water-based coatings are also becoming more and more mature. Today's water-based paint can be divided into three parts: primer, middle coat and top coat. The top coat is also called the finish varnish, which is covered on the middle coating to achieve the effect of dustproof and anti-pollution.

[0003] In order to achieve the effect of dustproof and anti-pollution, the finish varnish needs to use special water-based resin emulsion. The water-based emulsion used for exterior walls is mainly divided into pure acrylic emulsion, styrene-acrylic emulsion and silicone-acrylic emulsion. The special water-b...

Examples

Embodiment 1

[0029] An organic and inorganic composite finish varnish, including organic emulsion, nanometer photocatalyst, water and additives, this composite finish varnish adopts the composite emulsion of acrylic elastic emulsion and silica sol colloid as the main component of varnish, wherein said acrylic elastic emulsion It is 996 emulsion; the consumption of described each composition is as follows: according to 1000 mass parts total paints, the consumption of described 996 emulsion is 275-320 mass parts, and the consumption of described silica sol colloid is 25-80 mass parts; The amount of the photocatalyst is 1-3 parts by mass, the amount of the additive is 47-70 parts by mass, and the balance is water.

Embodiment 2-5

[0031] Adopt the raw material shown in Table 1 and formula structure organic, inorganic composite finish varnish of the present invention.

[0032] Formulation of table 1 organic, inorganic composite finish varnish

[0033] raw material

[0034] Propylene Glycol

[0035] The wall coating obtained according to the construction process of the present invention has been tested by industry common standards, and the test results are shown in Table 2 below.

[0036] Table 2 The test performance of organic and inorganic composite finish varnish coatings

[0037] project

[0038] Coating resistance to temperature denaturation (3 cycles)

technical field

[0001] The invention relates to an organic-inorganic composite finish varnish, which is suitable for the field of decoration and protection of inner and outer walls of buildings. Background technique

[0002] In exterior wall architectural coatings, the proportion of water-based coatings is originally greater. The construction technology and coating formula of water-based coatings are also becoming more and more mature. Today's water-based paint can be divided into three parts: primer, middle coat and top coat. The top coat is also called the finish varnish, which is covered on the middle coating to achieve the effect of dustproof and anti-pollution.

[0003] In order to achieve the effect of dustproof and anti-pollution, the finish varnish needs to use special water-based resin emulsion. The water-based emulsion used for exterior walls is mainly divided into pure acrylic emulsion, styrene-acrylic emulsion and silicone-acrylic emulsion. The special water-b...

Examples

Embodiment 1

[0029] An organic and inorganic composite finish varnish, including organic emulsion, nanometer photocatalyst, water and additives, this composite finish varnish adopts the composite emulsion of acrylic elastic emulsion and silica sol colloid as the main component of varnish, wherein said acrylic elastic emulsion It is 996 emulsion; the consumption of described each composition is as follows: according to 1000 mass parts total paints, the consumption of described 996 emulsion is 275-320 mass parts, and the consumption of described silica sol colloid is 25-80 mass parts; The amount of the photocatalyst is 1-3 parts by mass, the amount of the additive is 47-70 parts by mass, and the balance is water.

Embodiment 2-5

[0031] Adopt the raw material shown in Table 1 and formula structure organic, inorganic composite finish varnish of the present invention.

[0032] Formulation of table 1 organic, inorganic composite finish varnish

[0033] raw material

[0034] Propylene Glycol

[0035] The wall coating obtained according to the construction process of the present invention has been tested by industry common standards, and the test results are shown in Table 2 below.

[0036] Table 2 The test performance of organic and inorganic composite finish varnish coatings

[0037] project

[0038] Coating resistance to temperature denaturation (3 cycles)