Polishing boron sulfate rust remover

A technology of sulfate ester and rust removal liquid, applied in the field of rust removal, can solve the problems of increasing processing cost, affecting steel strength, hydrogen embrittlement, etc., achieving the effect of short rust removal time and preventing oxidation

CN109706459AActive Publication Date: 2019-05-03镇江纳润特高新科技发展有限公司 +1
0 Cites 2 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2019-05-03

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The application provides a polishing boron sulfate rust remover. The rust remover is prepared by mixing boron sulfate rust removers, alumina particles and / or zinc oxide particles and water, wherein the mass of the alumina particles accounts for 0.5%-1% of the total mass, and the mass of the water accounts for 1%-20% of the total mass. The efficient rust remover has a quick and simple rust removalfunction for severe rust, as well as inactivation and anti-oxidation functions; and not only can the rust removal effect is superior to the rust removal effect of strong acid or nitrogen and phosphorus rust removers, and the polishing boron sulfate rust remover is green and environmentally friendly, and has no toxic and side effects on human bodies.
Need to check novelty before this filing date? Find Prior Art

Description

Technical field

[0001] The invention relates to the technical field of rust removal, in particular to a polishing type boron sulfate rust removal liquid. Background technique

[0002] Ferrous metals, non-ferrous metals and other materials are prone to rust when placed outdoors or in the open air, which not only affects the appearance quality, but also affects the normal progress of painting and bonding processes. If they are not processed in time, the materials will be scrapped and lead to failure. Necessary economic losses.

[0003] The first generation of rust remover is a strong acid. The acid can chemically react with rust and metal oxides to form soluble salts, so as to achieve the purpose of rust removal. At the same time, the acid can react with the base metal to release hydrogen. Hydrogen can exert pressure on rust and insoluble oxide scale, which is conducive to their exfoliation and the reduction of high-valent iron, and accelerates the pickling process. However, the tra...

Examples

Embodiment 1

[0024] 1. First prepare the boron sulfate ester rust removal solution, the preparation steps are as follows:

[0025] (1) Put 55 parts of nonylphenol into the reaction kettle, heat to 105°C, then slowly add 2 parts of boric acid, and react for 135 minutes after the addition;

[0026] (2) After the reaction is completed, the temperature is lowered to 66°C, 3 parts of auxiliary glycerol are added, and the temperature is naturally lowered to room temperature;

[0027] (3) Slowly add 1.5 parts of S under vacuum 2 O 3 , Stir while adding, heat up to 55°C after adding, and react for 150 minutes;

[0028] (4) After the reaction is completed, the temperature is lowered to below 50°C, and 2.5 parts of auxiliary glycerin is added, reacted for 110 minutes, and then the temperature is naturally lowered to below 30°C to obtain.

[0029] 2. Mix the prepared borosulfate rust removal liquid with alumina particles with a particle size of 0.3 microns and water, and stir them evenly; the mass of alumina p...

Embodiment 2

[0032] 1. First prepare the boron sulfate ester rust removal solution, the preparation steps are as follows:

[0033] (1) Put 70 parts of nonylphenol polyoxyethylene ether NP-10 into the reactor, heat to 130°C, then slowly add 6 parts of boric acid, and react for 120 minutes after the addition;

[0034] (2) After the reaction is completed, the temperature is lowered to 75°C, 5 parts of sorbitol are added as an auxiliary agent, and the temperature is naturally lowered to room temperature;

[0035] (3) Slowly add 3 parts of SO under vacuum 3 , Stir while adding, heat up to 80°C after adding, react for 125 minutes;

[0036] (4) After the reaction is completed, the temperature is lowered to below 50°C, and 5 parts of epoxy soybean oil is added as an auxiliary agent, reacted for 130 minutes, and then the temperature is naturally lowered to below 30°C to obtain.

[0037] 2. Mix the prepared borosulfate rust removing liquid with alumina particles with a particle size of 1 micron and water, and...

Embodiment 3

[0040] 1. First prepare the boron sulfate ester rust removal solution, the preparation steps are as follows:

[0041] (1) Put 95 parts of nonylphenol polyoxyethylene ether NP-20 into the reactor, heat to 145°C, then slowly add 13 parts of boric acid, and react for 110 minutes after the addition;

[0042] (2) After the reaction is completed, the temperature is lowered to 95°C, 11 parts of the auxiliary propylene glycol are added, and the temperature is naturally lowered to room temperature;

[0043] (3) Slowly add 4.5 parts of S under vacuum 2 O 3 , Stir while adding, heat up to 95°C after adding, and react for 150 minutes;

[0044] (4) After the reaction is completed, the temperature is lowered to below 50°C, 9 parts of mannitol are added as an auxiliary agent, reacted for 180 minutes, and then the temperature is naturally lowered to below 30°C to obtain.

[0045] 2. Mix the prepared boron sulfate ester rust removal solution with zinc oxide particles with a particle size of 3 microns an...