Production method of hexamethoxy methyl melamine resin

A technology of hexamethoxymethyl melamine and its production method, which is applied in the production field of hexamethoxymethyl melamine, can solve problems such as damage to the health of the operator, environmental pollution, etc., and achieve the effects of wide compatibility and good stability

Inactive Publication Date: 2011-06-15
ZHANGJIAGANG SHUNCHANG CHEM
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the production process of general cyanamide resin, most of them will emit harmful gas, cause environmental pollution, and damage the health of the operator.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of hexamethoxy methyl melamine resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] Such as figure 1 As shown, add melamine and excess paraformaldehyde into the reaction kettle, the molar ratio of paraformaldehyde to melamine should be greater than 10, under normal pressure, the temperature is controlled at 30-35 °C, and the moisture is controlled between 5-15%. During the period, the methylolation reaction is carried out by adding an appropriate amount of manganese dioxide catalyst to generate an intermediate product; after 3 to 4 hours, the methylolation reaction is basically completed, and then an excessive amount of methanol is added, wherein the mole of methanol and the original melamine The ratio should be greater than 8, and the temperature rises to 50-75°C. Also under the action of manganese dioxide catalyst, after about an hour, the etherification reaction is basically completed, and methanol-etherified melamine with a high degree of etherification is produced, namely: hexamethoxymethyl base melamine.

[0009] There is no three wastes generat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

This invention discloses a compound used for dope cross-linking agent: six methoxyl group methyl melamine. It solves puzzle of no way to synthesize high substituted degree methanol etherification melamine. First melamine and over dose formaldehyde under catalysis of manganese peroxide carry out methylolation reaction, gain intermediate product; secondly intermediate product and methanol under catalysis of manganese peroxide carry out etherification reaction, obtain six methoxyl group methyl melamine; this compound is a monomeric compound with six degree of functionality, has low molecular weight, high etherification degree, needle crystal shape. its melting point is 55 deg, possess wonderful stability, comprehensive intermiscibility; And its formaldehyde content is very low, has no injuryto flesh, and is a green product.

Description

technical field [0001] The invention relates to a production method of a compound used as a crosslinking agent, in particular to a production method of hexamethoxymethylmelamine. Background technique [0002] Cyanamide resin is a very important class of methanol etherified melamine formaldehyde resin, which developed rapidly during the 1960s. In the United States, this type of resin accounts for a large proportion of melamine resin. Since the mid-1980s in my country, melamine resin has entered a stage of comprehensive development. Among them, butanol-etherified melamine resin has been maturely applied in the coating industry, but methanol-etherified melamine-formaldehyde resin with a high degree of etherification is still in the development stage. Methanol etherified melamine formaldehyde resin with high etherification degree can be used in general industrial coatings such as automotive coatings, coil coatings, can coatings, home appliance coatings, wood coatings, cement and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07D251/00C08K5/3492
Inventor 陆建荣顾长春
Owner ZHANGJIAGANG SHUNCHANG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com